Process for refining high-impurity copper to anode copper
AssigneeThe Trustees of Columbia University in the City of New York
InventorsNickolas J. Themelis, Baozhong Zhao
Life of this patent
Estimating the term…
Abstract
A process for refining high-impurity blister copper to anode quality copper is disclosed. In an oxidation step of a blister copper refining stage, soda ash fluxing removes antimony and arsenic while also removing sulfur and iron. In a deoxidation step of the blister copper refining stage, sulfur hexafluoride is injected at a controlled oxygen concentration to remove bismuth while reducing the oxygen content. Slag is continuously or periodically skimmed from the surface of the molten blister copper to prevent re-entry of impurities. The process may be carried out in batch operation or, in a preferred embodiment, in continuous flow-through operation.
Claims16
A process for refining molten blister copper into anode copper comprising:
- a. a first step of simultaneously injecting into molten blister copper a first oxygen-containing gas in an amount to provide at least 5 Nm.sup.3 of oxygen and at least 10 kg of soda ash for each ton of molten blister copper being refined, the injecting taking place while the molten blister copper is maintained at a temperature between 1150.degree. C. and 1300.degree. C., and skimming slag from a top surface of the molten blister copper during the injecting of the first oxygen-containing gas and the soda ash, at a rate sufficient to remove impurities from the molten blister copper, thereby producing partially refined molten copper;
- and
- b. a second step of simultaneously injecting into the partially refined molten copper a hydrocarbon, a second oxygen-containing gas in an amount sufficient to maintain an oxygen concentration of between 500 to 2000 ppm in the partially refined molten copper, and at least 0.05 kg of sulfur hexafluoride for each kg of bismuth in the molten blister copper being refined, the injecting taking place while the partially refined molten copper is maintained at a temperature between 1150.degree. C. and 1300.degree. C.
A process for refining molten blister copper into anode copper comprising:
- a. a first step of simultaneously injecting into molten blister copper:
- i. a first oxygen-containing gas in an amount to provide at least 0.7 Nm.sup.3 of oxygen for each kg of sulfur contained in the molten blister copper being refined,
- ii. at least 0.7 kg of soda ash for each kg of arsenic contained in the molten blister copper being refined, and
- iii. at least 0.4 kg of soda ash for each kg of antimony contained in the molten blister copper being refined, the injecting taking place while the molten blister copper is maintained at a temperature between 1150.degree. C. and 1300.degree. C.;
- and concurrently skimming slag from a top surface of the molten blister at a rate sufficient to remove impurities from the molten blister copper, thereby producing partially refined molten copper;
- and
- b. a second step of simultaneously injecting into the partially refined molten copper:
- i. a hydrocarbon,
- ii. a second oxygen-containing gas in an amount sufficient to maintain an oxygen concentration of between 500 to 2000 ppm in the partially refined molten copper, and
- iii. at least 0.35 kg of sulfur hexafluoride for each kg of bismuth contained in the molten blister copper being refined,
- the injecting taking place while the partially refined molten copper is maintained at a temperature between 1150.degree. C. and 1300.degree. C.
Dependencies are inferred from the claim text.