Graft polymer and thermoplastic resin composition
AssigneeMitsubishi Rayon Co., Ltd.
InventorsAkihiro Toritani, Koichi Shishido, Masahiro Osuka, Akira Nakata
Life of this patent
Estimating the term…
Abstract
A method for particles agglomeration and enlargement of a diene type polymer rubber latex, which comprises subjecting a diene type polymer rubber latex produced by emulsion polymerization, to particles agglomeration and enlargement to obtain a particles-enlarged diene type polymer rubber latex (A), wherein the particles enlargement is allowed to take place by agglomeration based mainly on Brownian coagulation; a graft copolymer (B) of a particles-enlarged diene type polymer rubber latex (A) obtained by the above method; and a thermoplastic resin composition comprising said graft copolymer (B).
Claims1
A thermoplastic resin composition comprising:
- 70-99% by weight of a vinyl chloride monomer-containing thermoplastic resin (C) and
- 1-30% by weight of a graft copolymer (B) obtained by graft-polymerizing, in at least one stage, at least one monomer selected from the group consisting of an aromatic vinyl monomer, a (meth)acrylic acid ester monomer, an unsaturated nitrile monomer and a monomer copolymerizable therewith, onto a particles-enlarged diene monomer containing polymer rubber latex (A) having a number-average particle diameter of 0.15-0.5 .mu.m, obtained by subjecting a diene monomer-containing polymer rubber latex produced by emulsion polymerization, to particles agglomeration and enlargement based mainly on Brownish coagulation,
- wherein said particles-enlarged diene monomer-containing polymer rubber latex (A) is contained in an amount of 55-85% by weight in terms of solid content based on said graft copolymer (B).