Shrinkage-compensating concrete
OwnerEdward K. Riceinventor
Life of this patent
Estimating the term…
Abstract
A shrinkage compensating cement exceeding the ASTM standard specification limiting 28 day expansion to 115% of the 7 day expansion. 28 day expansions of 120-200% are contemplated. The expansion takes place over an extended period of time, to better offset the shrinkage occurring as the concrete dries. The development of tensile stresses in the concrete is reduced and also is delayed, allowing more time for the tensile strength of the concrete to increase as the concrete dries. Shrinkage cracking is consequently significantly reduced.
Claims28
A shrinkage-compensating concrete having a seven day expansion and a 28 day expansion, comprising Portland cement, and an expansive component wherein the concrete has a 28 day expansion greater than 1150% of the seven day expansion, as measured by ASTM C878 wet cure method for 28 days.
A shrinkage-compensating cement having a seven day expansion and a 28 day expansion, comprising Portland cement, and an expansive component wherein the cement has a 28 day expansion greater than 115% of the 7 day expansion as measured by ASTM C806 and wherein the expansive component is ground to about 6300 cm.sup.2 /gm.
A shrinkage-compensating concrete having a seven day expansion and a 28 day expansion comprising Portland cement, and an expansive component wherein the concrete has a seven day expansion less than 0.04%, as measured by ASTM C878 wet cure method for 28 days.
A shrinkage-compensating concrete having a seven day expansion and a 28 day expansion and including an expansive component and Portland cement, comprising:
- an expansive cement having a 28 day expansion greater than 115% of the seven day expansion as measured by ASTM C806, the expansive component comprising 30 to 60% clinker and 40 to 70% gypsum, and the expansive cement comprised of 5% to 35% expansive component and 65 to 95% Portland cement, aggregate, and water.
A method of forming an expansive cement with a 7 day expansion of less than 0.04% and a 28 day expansion of more than 115% of the 7 day expansion by intergrinding an expansive clinker with gypsum and Portland clinker in a ball mill and wherein the expansive clinker, gypsum, and Portland cement have a fineness of 4500 cm.sup.2 /gm.
A method of forming an expansive concrete wherein the concrete is formed by a batching and mixing procedure when the concrete is wet, comprising the steps of wet blending an expansive cement component with ordinary Portland cement during the batching and mixing of the wet concrete wherein the batching and mixing of the wet concrete is comprised of:
- charging the mixer with about 80% of mixing water, adding coarse aggregate, and then adding Portland cement and expansive cement component and then,
- adding fine aggregate and additional water.
A method of forming an expansive concrete wherein the concrete is formed by a batching and mixing procedure when the concrete is wet, comprising the steps of wet blending a ground expansive clinker with ground gypsum and ordinary Portland cement during the batching and mixing of the wet concrete wherein the ground expansive clinker, ground gypsum and Portland cement form an expansive cement having a 7-day expansion of from about 0.40% to 0.10% as measured by ASTM C806, and a 28-day expansion exceeding 115% of the 7-day expansion as measured by ASTM C806.
A method of making an expansive cement comprising the steps of:
- grinding a mixture of about 0-20% rock gypsum and 80-100% expansive cement clinker in a ball mill to form a first ground mixture;
- and
- dry blending or grinding a second mixture including about 40-50% of the first ground mixture and 50-60% dry ground gypsum.
A method for using an expansive cement in a mortar having a 7 day and a 28 day expansion, comprising the steps of:
- pouring the mortar containing the expansive cement so that it fills a preset dimension;
- allowing the expansive cement to hydrate and gain tensile strength over time wherein the hydration of the expansive cement results in expansion of the mortar.
- from its original preset dimension over time, to compensate for shrinkage resulting from drying with the expansion of the mortar at 28 days exceeding 115% of the expansion of the mortar at 7 days as measured by ASTM C806.
A method for using an expansive cement in a concrete having a 7 day expansion and a 28 day expansion, comprising the steps:
- pouring the concrete containing the expansive cement so that it fills a preset dimension;
- allowing the expansive cement to hydrate,
- and gain tensile strength over time wherein the hydration of the expansive cement results in an expansion of the concrete from its original preset dimension over time, to compensate for shrinkage resulting from drying, with the expansion of the concrete at 28 days exceeding 115% of the expansion of the concrete at 7 days as measured by ASTM C878 wet cure method for 28 days.
A shrinkage-compensating concrete having a seven-day expansion and a 28 day expansion comprising Portland cement, and an expansive component wherein the concrete has
- an expansive component having a seven day expansion less than 0.04% and a 28 day expansion about 120 to 200% of the seven day expansion as measured by ASTM C878 wet cure method for 28 days, the expansive component comprising 30 to 60% clinker and the balance being gypsum, and the shrinkage-compensating concrete comprised of about 4% to 35% expansive component and the balance being Portland cement.
A shrinkage-compensating cement having a seven day expansion and a 28 day expansion, comprising Portland cement, and an expansive component wherein the cement has a 28 day expansion of 160% of the seven day expansion as measured by ASTM C806.
A shrinkage-compensating cement having a seven day expansion and a 28 day expansion comprising Portland cement, and an expansive component wherein the cement has a 28 day expansion of 183% of the 7 day expansion.
A shrinkage-compensating cement having a seven day expansion and a 28 day expansion comprising Portland cement and an expansive component wherein the cement has a 7 day expansion of about 0.02-0.04% and a 28 day expansion of about 120-200% of the 7 day expansion as measured by ASTM C806 and wherein the expansive component is ground to about 4500 cm.sup.2 /gm.
A shrinkage-compensating cement having a seven day expansion and a 28 day expansion comprising Portland cement, and an expansive component wherein the cement has a seven day expansion less than 0.04%, as measured by ASTM C806.
A method of wet blending expansive concrete and for using the expansive concrete in a construction, with the expansive concrete including an expansive component, Portland cement, and other components, comprising the steps of:
- separately shipping the expansive component to a mixing site apart from the other concrete components;
- and
- adjusting the ratio of expansive component to Portland cement, to adjust the amount of expansion of the expansive concrete, to compensate for anticipated shrinkage of the expansive concrete, after the expansive concrete is placed in a construction.
A method of forming an expansive concrete including gypsum and clinker, by a batching and mixing procedure when the concrete is wet comprising the steps of:
- dry blending gypsum and clinker to form an expansive component;
- and
- wet blending the expansive component with ordinary Portland cement during the batching and mixing of the concrete.
Dependencies are inferred from the claim text.