Method for making metal oxide textiles for spectral emitters
AssigneeThe Quantum Group, Inc.
InventorEva M. Wong
Life of this patent
Estimating the term…
Abstract
Several new and useful compositions of rare earth oxides and mixtures of rare earth oxides are made into strong flexible fibrous textiles and strands. By varying the mixtures of rare earth metal oxides that make up the textiles and strands, the emission spectra can be matched to the absorption spectra of a variety of semiconductor photovoltaic cells. Furthermore, the addition of between 1-10 mol % of thorium oxide to the rare earth metal oxide fibers inhibits microcrystalline grain growth at high temperatures.
Claims19
A method of making a metal oxide textile comprising:
- imbibing a polymeric organic textile template with an aqueous metal nitrate solution;
- exposing the metal nitrate imbibed textile to gaseous ammonia to produce a metal hydroxide imbibed textile;
- and
- heating the metal hydroxide imbibed textile under conditions sufficiently controlled to produce a metal oxide textile having tensile strength greater than 75 kPa.
A method of making a metal oxide textile comprising:
- imbibing a polymeric organic textile template with an aqueous metal nitrate solution;
- exposing the metal nitrate imbibed textile to gaseous ammonia to produce a metal hydroxide imbibed textile;
- and
- heating the metal hydroxide imbibed textile from room temperature to about 400.degree. C. at a rate between 0.25.degree. C./min and 0.5.degree. C./min to produce a metal oxide textile having tensile strength greater than 75 kPa.
A method of making a metal oxide textile comprising:
- imbibing a polymeric organic textile template with an aqueous metal nitrate solution;
- exposing the metal nitrate imbibed textile to gaseous ammonia to produce a metal hydroxide imbibed textile;
- and
- heating the metal hydroxide imbibed textile from about 400.degree. C. to about 450.degree. C. at a rate of about 50.degree. C./hr and holding at about 450.degree. C. for at least about one hour to produce a metal oxide textile having tensile strength greater than 75 kPa.
A method of making a metal oxide textile comprising:
- imbibing a polymeric organic textile template with an aqueous metal nitrate solution;
- exposing the metal nitrate imbibed textile to gaseous ammonia to produce a metal hydroxide imbibed textile;
- and
- heating the metal hydroxide imbibed textile from room temperature to a first temperature of about 400.degree. C. at a rate between 0.25.degree. C./min and 0.5.degree. C./min, then heating to a second temperature of about 450.degree. C. over one hour and holding the textile at the second temperature for about 12 hours, followed by raising the temperature a third time to between 600.degree. to 1400.degree. C. at a rate between 15.degree. C./min. and 25.degree. C./min., holding the textile at the third temperature from 1 to 24 hours and then cooling to room temperature over 8 to 12 hours to produce a metal oxide textile having tensile strength greater than 75 kPa.
A method of making a metal oxide textile comprising:
- imbibing a polymeric organic textile template with an aqueous metal nitrate solution;
- exposing the metal nitrate imbibed textile to gaseous ammonia to produce a metal hydroxide imbibed textile;
- and
- heating the metal hydroxide imbibed textile in two stages, the first heating stage comprising heating the textile to a temperature of about 400.degree. C. at a rate between 0.25.degree. C./min and 0.5.degree. C./min, then heating to a second temperature of about 450.degree. C. over one hour and holding the textile at the second temperature for about 12 hours, followed by cooling to room temperature;
- and,
- the second heating stage comprising heating the textile from room temperature to about 600.degree. C. at a rate between 15.degree. C./min and 25.degree. C./min, holding at that temperature for about 30 minutes and then raising the temperature to between 600.degree. and 1400.degree. C. at a rate between 15.degree. C./min and 25.degree. C./min, holding the textile at that temperature between 1 and 24 hours and then cooling to room temperature over 8 to 12 hours to produce a metal oxide textile having tensile strength greater than 75 kPa.
Dependencies are inferred from the claim text.