Method of welding polyurethane thin film
AssigneePolygenex International, Inc.
InventorTilak M. Shah
Life of this patent
Estimating the term…
Abstract
A method of welding at least two layers of a thin thermoplastic polyurethane elastomer (10A,B) to form a weld seam (12) to produce polyurethane barrier products such as, but not limited to, gloves (20), condoms (30), inflatable catheter balloon cuffs (48A,B), ostomy pouches (50), organ bags (60), and instrument covers (70) through a process of pre-heating a sealing die platen, the at least two layers of the polyurethane (10A,B) softened while under pressure from the preheated die platen, followed by welding the at least two layers of polyurethane (10A,B) film by transmission of a radio-frequency energy to the film (10A,B) to produce a weld seam (12) and then allowing the weld seam (12) to cool, the resultant product having seam integrity.
Claims5
A method of welding at least two layers of a thermoplastic polyurethane elastomer film, comprising the steps of:
- (a) pre-heating a welding platen to a temperature above a Vicat softening temperature and below a thermoplastic elastomer film deformation temperature of said thermoplastic polyurethane elastomer film, said thermoplastic polyurethane elastomer film having a thickness in a range from about 0.5 to about 5.0 mils (0.0127 to 0.127 mm);
- (b) placing at least two layers of said polyurethane film on the preheated platen, said platen heating said thermoplastic polyurethane elastomer film to a temperature above the Vicat softening temperature of said thermoplastic polyurethane elastomer film and below a melting temperature of said thermoplastic polyurethane elastomer film;
- (c) compressing the layers of film in surface apposition to form an interface therebetween by applying pressure from a die and from said welding platen to said thermoplastic polyurethane elastomer film;
- (d) transmitting radio-frequency energy to the layers of film while said thermoplastic polyurethane elastomer film is under said pressure, welding the film layers at said interface therebetween forming a weld;
- and
- (e) cooling said weld of the at least two layers of film, wherein said weld is free of holidays, pins holes, charring, burning, and wrinkles.
Dependencies are inferred from the claim text.