US 5,803,947 AGranted

Method of producing metallic magnesium, magnesium oxide or a refractory material

AssigneeMineral Development International A/S

InventorsJohn Engell, Jens S.o slashed.nderberg Frederiksen, Karsten Agersted Nielsen

Life of this patent

Estimating the term…

Loading patent…

Abstract

Metallic magnesium and pure magnesium oxide are produced by carbothermal reduction of starting materials such as magnesium oxide containing minor amounts of oxides of Fe, Si, Ca and Al, and/or magnesium silicate minerals, such as olivine, at subatmospheric pressure. Metallic magnesium is evaporated from a reduction zone and pure metallic magnesium and pure magnesium oxide are precipitated in a second condensation zone. Si is partly evaporated as SiO which is precipitated in a first condensation zone upstream the second condensation zone, partly converted to SiC and an alloy of Si and Fe in the reaction mixture. The starting materials may also be processed by a method wherein their magnesium component is converted to magnesium oxide in the reaction mixture, while the remaining components are converted to SiC and an alloy of Si and Fe. Au and valuable siderophilic elements may be recovered by leaching the alloy of Si and Fe.

Claims28

Dependent claims

A method of producing metallic magnesium by carbothermal reduction of a starting material selected from the group consisting of magnesium oxide containing minor amounts of oxides of Fe, Si, Ca and Al;

natural and industrially produced magnesium silicate minerals;
and mixtures thereof which comprises:
mixing the starting material with carbon to form a reaction mixture, the carbon being present in an amount of at least 1 mole C/mole SiO.sub.2 plus at least 1 mole C/mole FeO plus at least 3 mole C/mole Fe.sub.2 O.sub.3 plus at least 1 mole C/mole MgO;
heating the reaction mixture in a reduction zone to a temperature T.sub.r of from 1400.degree. to 1700.degree. C. and at a pressure p.sub.r of from 0.01-1.75 kPa;
reducing iron oxide components of the starting material to iron in the reduction zone;
reducing a silica component of the starting material to SiO, which is partly converted to SiC and an alloy of Si and Fe, "Si.sub.z Fe", in the reduction zone, partly evaporated from the reduction zone and converted to SiC, Si, and/or Mg.sub.2 SiO.sub.4 by reaction with carbon in a separate first condensation zone at a pressure p.sub.1 of from 0.01-1.1 kPa and at a temperature T.sub.1 higher than:
##EQU5## and lower than T.sub.min +100.degree. C. and in any case lower than T.sub.r ;
reducing a magnesium oxide component of the starting material to gaseous metallic magnesium in the reduction zone;
evaporating said gaseous metallic magnesium from the reduction zone and condensating said gaseous metallic magnesium in a separate second condensation zone arranged downstream from the first condensation zone at a pressure p.sub.2 of from 0.01-1.1 kPa and at a temperature T.sub.2 less than 638.degree. C.;
and
withdrawing CO formed by the reduction processes from the second condensation zone and maintaining the pressure p.sub.2 at a preselected value with a pump;
whereby the temperature gradient between the first condensation zone and the second condensation zone is kept as steep as possible;
and
whereby p.sub.2 .ltoreq.p.sub.1 .ltoreq.p.sub.r.

11 more elements

A method of producing pure magnesium oxide by carbothermal reduction of a starting material selected from the group consisting of magnesium oxide containing minor amounts of oxides of Fe, Si, Ca and Al;

natural and industrially produced magnesium silicate minerals;
and mixtures thereof, which comprises:
mixing the starting material with carbon to form a reaction mixture, the carbon being present in an amount of at least 1 mole C/mole SiO.sub.2 plus at least 1 mole C/mole FeO plus at least 3 mole C/mole Fe.sub.2 O.sub.3 plus at least 1 mole C/mole MgO;
heating the reaction mixture in a reduction zone to a temperature T.sub.r of from 1400.degree. to 1700.degree. C. and at a pressure p.sub.r of from
0.01 to 10.sup.(-16381.multidot.(T.sbsp.r.sup.+273).spsp.-1.sup.+10.03) kpa ;
reducing iron oxide components of the starting material to iron in the reduction mixture;
reducing a silica component of the starting material to SiO, which is partly converted to SiC and an alloy of Si and Fe, "Si.sub.z Fe", in the reduction zone, partly evaporated from the reduction zone and converted to SiC, Si, and/or Mg.sub.2 SiO.sub.4 by reaction with carbon in a separate first condensation zone at a pressure p.sub.1, where p.sub.1 .ltoreq.p.sub.r, and at a temperature T.sub.1 higher than:
##EQU6## and lower than T.sub.min +100.degree. C. and in any case lower than T.sub.r ;
reducing a magnesium oxide component of the starting material at least partially to gaseous metallic magnesium in the reduction zone;
and
evaporating said gaseous metallic magnesium from the reduction zone and reacting said gaseous metallic magnesium with CO formed in the reduction zone with a separately added oxygen containing gas selected from molecular oxygen, air, CO.sub.2, CO, H.sub.2 O or mixtures thereof, to magnesium oxide and precipitating said magnesium oxide in a separate oxidation and condensation zone located downstream of the first condensation zone at a pressure p.sub.2, where p.sub.2 .ltoreq.p.sub.1, and at a temperature T.sub.2 of from 638.degree. C. to T.sub.1 ;
withdrawing the magnesium oxide from the oxidation and condensation zone and, if necessary, removing carbon from the withdrawn product by oxidation;
and
withdrawing gases formed by the reduction and oxidation processes from the oxidation and condensation zone and maintaining the pressure p.sub.2 at a preselected value with a pump;
whereby p.sub.2 .ltoreq.p.sub.1 .ltoreq.p.sub.r.

12 more elements

A method of processing a starting material selected from the group consisting of magnesium oxide containing minor amounts of oxides of Fe, Si, Ca and Al;

natural and industrially produced magnesium silicate minerals;
and mixtures thereof, which comprises:
mixing the starting material with carbon to form a reaction mixture, the carbon being present in an amount of at least 1 mole C/mole SiO.sub.2 plus at least 1 mole C/mole FeO plus at least 3 mole C/mole Fe.sub.2 O.sub.3 plus at least 1 mole C/mole MgO;
heating the reaction mixture in a reaction zone to a temperature T.sub.r of from 1400.degree. to 1800.degree. C. and at a pressure p.sub.r of from
10.sup.(-16381.multidot.(T.sbsp.r.sup.+273).spsp.-1.sup.+10.03) to
10.sup.(-17043.multidot.(T.sbsp.r.sup.+273).spsp.-1.sup.+10.75) kPa,
whereby
iron oxide components of the starting material are reduced to iron in the reaction zone,
a silica component of the starting material is at least partially converted to SiC and an alloy of Si and Fe, Si.sub.z Fe", in the reaction zone, and
a magnesium oxide component of the starting material is at least partially converted to magnesium oxide;
withdrawing an essentially fully converted mixture as end product from the reaction zone;
withdrawing CO formed by the reduction processes from the reaction zone and maintaining the pressure p.sub.r in the reaction zone at a preselected value with a pump.

9 more elements