US 5,789,489 AGranted
Fast-curing perfluoroelastomer composition
AssigneeE. I. Du Pont de Nemours and Company
InventorsMichael Cregg Coughlin, Charles David Monaco
Life of this patent
Estimating the term…
Abstract
Fast curing perfluoroelastomer compositions are provided which comprise a perfluoroelastomer having a plurality of nitrile groups and a plurality of carboxyl-containing groups, carboxylate-containing groups, carboxamide groups, or mixtures thereof; and an organotin curing agent.
Claims25
A curable perfluoroelastomer composition comprising
- (A) a perfluoroelastomer comprising copolymerized units of (1) a perfluoroolefin;
- (2) a perfluorovinyl ether selected from the group consisting of perfluoro(alkyl vinyl) ethers, perfluoro(alkoxy vinyl) ethers, and mixtures thereof;
- and (3) a cure site monomer having at least one nitrile group, selected from the group consisting of fluorinated olefins having at least one nitrile group, fluorinated vinyl ethers having at least one nitrile group, and mixtures thereof;
- wherein the perfluoroelastomer is characterized by i) having a plurality of carbonyl-containing endgroups selected from the group consisting of carboxyl endgroups, carboxylate endgroups, carboxamide endgroups, and mixtures thereof and ii) being substantially free of ionizable or ionized endgroups other than those having carbonyl-containing functional groups;
- and wherein the integrated absorbance ratio of the carbonyl-containing endgroups is greater than 0.1, the integrated absorbance ratio being determined by calculating the ratio of the integrated peak intensity within the range of 1620-1840 cm.sup.-1 to that within the range of 2220-2740 cm.sup.-1, as measured on a Fourier transform infrared spectrum of the perfluoroelastomer;
- and
- (B) about 0.1 to about 10 parts by weight per hundred parts by weight perfluoroelastomer of an organotin curing agent
- wherein the perfluoroelastomer composition is characterized by having a t.sub.s 2 of less than 4 minutes, when measured with a moving die rheometer at a moving die frequency of 1.66 Hertz, using an oscillation amplitude of .+-.0.5 degrees at 199.degree. C.
5 more elements
The composition of any one of the above claims wherein the amount of organotin curing agent is 1-4 parts by weight per hundred parts by weight perfluoroelastomer.
A curable perfluoroelastomer composition comprising
- (A) a perfluoroelastomer having a plurality of carbonyl-containing functional groups selected from the group consisting of carboxyl groups, carboxylate groups, and carboxamide groups, said perfluoroelastomer comprising copolymerized units of (1) a perfluoroolefin;
- (2) a perfluorovinyl ether selected from the group consisting of perfluoro(alkyl vinyl) ethers, perfluoro(alkoxy vinyl) ethers, and mixtures thereof;
- (3) a fluorinated comonomer selected from the group consisting of carboxyl-containing and carboxylate-containing comonomers, and (4) a cure site monomer having at least one nitrile group, selected from the group consisting of fluorinated olefins having nitrile groups, fluorinated vinyl ethers having at least one nitrile group and mixtures thereof wherein the integrated absorbance ratio of the carbonyl-containing functional groups is greater than 0.1, the absorbance ratio being determined by calculating the ratio of the integrated peak intensity within the range of 1620-1840 cm.sup.-1 to that within the range of 2220-2740 cm.sup.-1, as measured on a Fourier transform infrared spectrum of the perfluoroelastomer;
- and
- (B) about 0.1 to about 10 parts by weight per hundred parts by weight perfluoroelastomer of an organotin curing agent
- wherein the perfluoroelastomer composition is characterized by having a t.sub.s 2 of less than 4 minutes, when measured with a moving die rheometer at a moving die frequency of 1.66 Hertz, using an oscillation amplitude of .+-.0.5 degrees at 199.degree. C.
3 more elements