Semiconductor device produced by a single furnace cycle diffusion and oxidation process
AssigneesSony Corporation, Sony Electronics Inc.
InventorJon A. Gwin
Life of this patent
Estimating the term…
Abstract
A semiconductor deposition and oxidation process using a single furnace cycle. The temperature and gas mixture is stabilized inside the furnace prior to introduction of a dopant at a relatively low temperature. The temperature of the chamber is then ramped-up and the dopant is diffused into the wafer in an inert ambient. The temperature is then ramped-up again and oxygen is introduced to produce an oxide layer. The wafers are then removed from the furnace and any residue of the dopant within the chamber is effectively neutralized by introducing a high flow of oxygen.
Claims9
A semiconductor device produced by a process for processing semiconductor devices during a single cycle of a furnace, comprising the ordered steps of:
- starting a single furnace cycle by loading a semiconductor device into a heating chamber of a furnace and heating said chamber to a chamber temperature lower than that which would produce diffusion of a dopant in said semiconductor device;
- maintaining said chamber temperature while forming a layer of dopant glass on a surface of said semiconductor device;
- increasing said chamber temperature to a diffusion temperature adequate to drive said dopant into said semiconductor device in an inert environment;
- maintaining said diffusion temperature and inert environment for a period of time to drive said dopant into said semiconductor device:
- elevating said chamber temperature to an oxidizing temperature and generating an oxidizing environment for a period of time to achieve oxidation of said semiconductor device;
- and
- removing said semiconductor device from said heating chamber of said furnace to complete said single furnace cycle.
A semiconductor device produced by a process for processing semiconductor devices during a single cycle of a furnace, comprising the ordered steps of:
- establishing a target silicon resistance for said semiconductor devices;
- starting a single furnace cycle by loading a semiconductor device into a heating chamber of a furnace;
- heating said chamber to a chamber temperature lower than that which would produce diffusion of a dopant in said semiconductor device to a degree which would produce a silicon resistance which is less than said target resistance;
- maintaining said chamber temperature while forming a layer of dopant glass on a surface of said semiconductor device;
- increasing said chamber temperature to a diffusion temperature adequate to drive said dopant into said semiconductor device in an inert environment;
- maintaining said diffusion temperature and inert environment for a period of time to drive said dopant into said semiconductor device to produce said target resistance;
- elevating said chamber temperature to an oxidizing temperature and generating an oxidizing environment for a period of time to achieve oxidation of said semiconductor device;
- and
- removing said semiconductor device from said heating chamber of said furnace to complete said single furnace cycle.
A semiconductor device produced by a process for processing semiconductor devices during a single cycle of a furnace, comprising the ordered steps of:
- starting a single furnace cycle by heating a heating chamber of a furnace to 850.degree. C.;
- loading a semiconductor device into said heating chamber;
- stabilizing said heating chamber temperature in a gas mixture of 2050 sccm of N.sub.2 and 3500 sccm of O.sub.2 ;
- maintaining said chamber temperature and gas mixture while forming a layer of dopant glass on a surface of said semiconductor device by introducing POCL.sub.3 vapor for 75 minutes, wherein said POCL.sub.3 vapor is generated by passing N.sub.2 gas through a bubbler containing liquid POCL.sub.3 with said liquid POCL.sub.3 held at a temperature below ambient temperature;
- increasing said chamber temperature to a diffusion temperature of 900.degree. to 1100.degree. C. to drive said dopant into said semiconductor device in a nitrogen environment produced by a flow of 6000 sccm of N.sub.2 ;
- maintaining said diffusion temperature and nitrogen environment for a period of 50 minutes to drive said dopant into said semiconductor device;
- generating an oxygen and hydrogen environment by establishing a flow of 5000 sccm of H.sub.2 and 3000 sccm of O.sub.2 within said heating chamber;
- oxidizing said semiconductor device by maintaining said diffusion temperature and hydrogen and oxygen environment for a period of time to achieve oxidation of said wafers;
- reducing said chamber temperature to 800.degree. C.;
- removing said wafers from said heating chamber;
- and
- introducing an oxygen flow of 10000 sccm of O.sub.2 at a chamber temperature of 800.degree. C. into said chamber for at least 45 minutes to react with any remaining dopant inside said chamber;
- removing said semiconductor device from said heating chamber of said furnace to complete said single furnace cycle.
Dependencies are inferred from the claim text.