Method of making a sintered article

Abstract

A method of making a sintered article is disclosed, the method comprising the steps of mixing a prealloyed ferrous powder having a composition in the following ranges in weight %: carbon 0.7-2.7/chromium 3-6/cobalt 5-10/vanadium 0.5-3/molybdenum 6-11/silicon 0.3-2/ others total 2 max/balance iron and optionally up to 3 wt % tungsten, with an addition of carbon powder of at least 0.1 wt %, compacting said powder mixture by uniaxial pressing to form a green compact of near net shape, sintering said green compact in a continuous gas atmosphere sintering furnace at a temperature in the range from 1130.degree. C. to 1250.degree. C. such that the final density of said sintered material is greater than 95% of the theoretical density as a result of the sintering operation alone.