Ready mixed setting-type joint compound, and method of making same
AssigneeNational Gypsum Company
InventorJashbhai M. Patel
Life of this patent
Estimating the term…
Abstract
A process for the production of a ready-mixed setting-type joint compound includes the use of calcium sulfate hemihydrate, water, and a set-retarding agent. The retarder includes a polymer composition including acrylic acid and acrylamide monomer units, for example a copolymer (or a mixture of copolymers) of acrylic acid and acrylamide or a blend of a homopolymer of acrylic acid and a homopolymer of acrylamide. The joint compound can be combined with an accelerator including a metallic salt. The joint compound of the invention can be formulated either as a lightweight joint compound or as a conventional weight joint compound. The joint compounds provide short setting times, reduced shrinkage, reduced preparation time, and beneficial application properties.
Claims21
A settable, ready-mixed joint compound composition suitable for use in concealing joints between edges of adjacent wallboard panels, said joint compound composition comprising:
- (a) calcium sulfate hemihydrate;
- (b) sufficient water to form a slurry with said calcium sulfate hemihydrate;
- and
- (c) a set-retarding agent comprising a polymer composition including acrylic acid and acrylamide monomer units, said set-retarding agent having a molecular weight in a range of between about 1700 and about 6700.
A settable, ready-mixed joint compound composition suitable for use in concealing joints between edges of adjacent wallboard panels, said joint compound composition comprising:
- (a) calcium sulfate hemihydrate;
- (b) sufficient water to form a slurry with said calcium sulfate hemihydrate;
- (c) a set-retarding agent comprising a copolymer of acrylic acid and acrylamide, said set-retarding agent being present in an amount of from about 0.6 to about 4.0 weight percent based on the weight of said calcium sulfate hemihydrate, said set-retarding agent having a molecular weight in a range of between about 1700 and about 6700;
- and
- (d) an agent for substantially accelerating the setting of said composition;
- and wherein:
- said composition has a setting time of about fifteen minutes or less and shrinks upon setting at a rate of about 10 volume percent or less.
A kit comprising:
- (a) a ready-mixed settable composition comprising (1) a calcium sulfate hemihydrate;
- (2) sufficient water to form a slurry with said calcium sulfate hemihydrate;
- and (3) a set-retarding agent comprising a copolymer of acrylic acid and acrylamide, said set-retarding agent having a molecular weight in a range of between about 1700 and about 6700;
- and
- (b) an agent for accelerating the setting of said composition (a), said accelerating agent comprising about 0.1 to about 5.0 weight percent based on the weight of said calcium sulfate hemihydrate.
A method of producing a joint compound composition suitable for concealing joints between edges of adjacent wallboard panels, said method comprising the steps of:
- (a) combining, to provide a ready-mixed settable cementitious composition, (1) calcium sulfate hemihydrate;
- (2) sufficient water to form a slurry with said calcium sulfate hemihydrate;
- and (3) a set-retarding agent comprising a polymer composition including acrylic acid and acrylamide monomer units, said set-retarding agent having a molecular weight in a range of between about 1700 and about 6700;
- and
- (b) combining an agent for accelerating the setting of said cementitious composition with the product of step (a);
- and wherein
- said set-retarding agent is present in an amount of from about 0.6 to about 4.0 weight percent based on the weight of the calcium sulfate hemihydrate.
A method of producing a settable, ready-mixed joint compound composition suitable for concealing joints between edges of adjacent wallboard panels, said method comprising the steps of:
- forming a slurry of (1) calcium sulfate hemihydrate;
- (2) water;
- and (3) a set-retarding agent comprising a copolymer of acrylic acid and acrylamide, to provide a ready-mixed, settable cementitious composition units, said set-retarding agent having a molecular weight in a range of between about 1700 and about 6700;
- wherein
- said set-retarding agent is present in an amount of from about 0.6 to about 4.0 weight percent based on the weight of the calcium sulfate hemihydrate.