Process for preparing a ceramic material for use in dental fillings and dental crowns
AssigneeBEGO Bremer Goldschlagerei Wilh. Herbst GmbH & Co.
InventorsWolfgang Wiedemann, Hans Georg Klinger
Life of this patent
Estimating the term…
Abstract
A bioactive ceramic material for dental fillings and crowns on the basis of calcium phosphate compounds contains crystallites of sparingly water-soluble calcium phosphate compounds in an amorphous, vitreous or polycrystalline matrix of readily water-soluble calcium phosphate compounds, the Ca/P-atomic ratio of the calcium phosphate compounds being altogether <1.65.
Claims20
A process for preparing a ceramic material for dental purposes, comprising the steps of:
- making calcium phosphate compounds from an aqueous solution of at least one calcium compound by adding at least one phosphate compound, and precipitating calcium phosphate compounds from the aqueous solution under such conditions that the Ca/P-atomic ratio is <1.65 wherein the solution is initially set to a pH value of 10 which reduces to a value of 7 during precipitation;
- drying the precipitate and then comminuting it to produce a product and
- then compressing the product into green compacts and sintering them at temperatures of 800.degree. to 1400.degree. C. so that crystallites of sparingly water-soluble calcium phosphate compounds are created in an amorphous or polycrystalline matrix of readily water-soluble calcium phosphate compounds.
A process for preparing a ceramic material for dental purposes comprising the steps of:
- making calcium phosphate compounds from an aqueous solution of at least one calcium compound by adding at least one phosphate compound, and precipitating calcium phosphate compounds from the aqueous solution under such conditions that the Ca/P-atomic ratio is <1.65;
- drying the precipitate and then comminuting it to produce a product;
- and
- then compressing the product into green compacts and sintering them at temperatures of 800.degree. to 1400.degree. C.;
- wherein the precipitating step takes place in an aqueous/organic medium,
- wherein the precipitating step comprises gradually adding a basic precipitating agent, and
- wherein solutions of the calcium compound and the phosphate compound are each initially set to a pH value of 10, so that, after the precipitation of the calcium phosphate compounds, the pH value of the solution containing the precipitated calcium phosphate compounds is 7, and so that crystallites of sparingly water-soluble calcium phosphate compounds are created in an amorphous or polycrystalline matrix of readily water-soluble calcium phosphate compounds.
A process for preparing a ceramic material for dental purposes, comprising the steps of:
- making calcium phosphate compounds from an aqueous solution of at least one calcium compound by adding at least one phosphate compound, and precipitating calcium phosphate compounds from the aqueous solution under such conditions that the Ca/P-atomic ratio is <1.65 wherein the solution is initially set to a pH value of 10 which reduces to a value of 7 during precipitation;
- drying the precipitate and then comminuting it to produce a product;
- and
- then compressing the product into green compacts and sintering them at temperatures of 800.degree. to 1400.degree. C. so that crystallites of sparingly water-soluble calcium phosphate compounds are created in a vitreous matrix of readily water-soluble calcium phosphate compounds.
Dependencies are inferred from the claim text.