Fiber of ethylene-vinyl alcohol copolymer and process for production thereof
AssigneeKuraray Co., Ltd.
InventorsKiyoshi Hirakawa, Izumi Tabuchi, Yusuke Ando, Shinji Yamaguchi
Life of this patent
Estimating the term…
Abstract
A fiber of ethylene-vinyl alcohol copolymer having a specific degree of crosslinking which is obtained by acetal decomposition regeneration reaction with a specific crosslinking agent. Because of its effective degree of crosslinking, this fiber has a greatly improved resistance to steam ironing and finds use for garments and living material.
Claims7
A fiber of crosslinked ethylene-vinyl alcohol copolymer containing 25-70 mol % ethylene, characterized in that the effective degree of cross-linking (K%) represented by equation (1) below satisfies equation (2) below,
- K(%)=1.2.times.{(27+m)/35}.times.(T.sub.mk -T.sub.mo) (1)
- where,
- m denotes the number of linear methylene groups and/or methine groups in the crosslinked moiety;
- T.sub.mk denotes the melting point (.degree.C.) of the fiber of ethylene-vinyl alcohol copolymer measured after crosslinking, and
- T.sub.mo denotes the melting point (.degree.C.) of the fiber of ethylene-vinyl alcohol copolymer measured before crosslinking,
- K(%).gtoreq.0.27X+4.9 (2)
- where,
- x denotes the ethylene content (in mol %).
A composite fiber of ethylene-vinyl alcohol copolymer containing 25-70 mol % ethylene and any other thermoplastic polymer, said ethylene-vinyl alcohol copolymer being characterized in that the effective degree of crosslinking (K %) represented by equation (1) below satisfies equation (2) below, with said copolymer forming part of the fiber surface,
- K(%)=1.2.times.{(27+m)/35}.times.(T.sub.mk -T.sub.mo) (1)
- where,
- m denotes the number of linear methylene groups and/or methine groups in the crosslinked moiety;
- T.sub.mk denotes the melting point (.degree.C.) of the fiber of ethylene-vinyl alcohol copolymer measured after crosslinking;
- and
- T.sub.mo denotes the melting point (.degree.C.) of the fiber of ethylene-vinyl alcohol copolymer measured before crosslinking,
- K(%).gtoreq.0.27X+4.9 (2)
- where,
- x denotes the ethylene content (in mol %).
A process for producing a fiber of ethylene-vinyl alcohol copolymer, said process comprising treating a fiber of ethylene-vinyl alcohol copolymer containing 25-70 mol % ethylene with a solution containing at least one species of the compound represented by formula (3) below in an acid condition of pH 1.0-5.0 at a temperature of 100.degree. C. to 140.degree. C. under pressure, ##STR2## where R.sub.1, R.sub.2, R.sub.3, and R.sub.4 each denotes an alkyl group, or R.sub.1 together with R.sub.2 and R.sub.3 together with R.sub.4 form rings for alkylene groups, R.sub.5 denotes hydrogen or an alkyl group, and n is a numeral in the range of 2 to 10, (R.sub.1, R.sub.2, R.sub.3, R.sub.4, and R.sub.5 may have substituent groups.)
A process for treating a composite fiber, said process comprising treating a composite fiber of ethylene-vinyl alcohol copolymer containing 25-70 mol % ethylene and any other thermoplastic polymer, said copolymer forming part of the fiber surface, with a solution containing at least one species of the compound represented by formula (3) below in an acid condition of pH 1.0-5.0 at a temperature of 100.degree. C. to 140.degree. C. under pressure, ##STR3## where R.sub.1, R.sub.2, R.sub.3, and R.sub.4 each denotes an alkyl group, or R.sub.1 together with R.sub.2 and R.sub.3 together with R.sub.4 form rings for alkylene groups, R.sub.5 denotes hydrogen or an alkyl group, and n is a numeral in the range of 2 to 10, (R.sub.1, R.sub.2, R.sub.3, R.sub.4, and R.sub.5 may have substituent groups.)
A process for dyeing a composite fiber of ethylene-vinyl alcohol copolymer containing 25-70 mol % ethylene and any other thermoplastic polymer, said copolymer forming part of the fiber surface, said process comprising dyeing said composite fiber simultaneously with treating it with a solution containing at least one species of the compound represented by formula (3) below in an acid condition of pH 1.0-5.0 at a temperature of 100.degree. C. to 140.degree. C. under pressure, ##STR4## where R.sub.1, R.sub.2, R.sub.3, and R.sub.4 each denotes an alkyl group, or R.sub.1 together with R.sub.2 and R.sub.3 together with R.sub.4 form rings for alkylene groups, R.sub.5 denotes hydrogen or an alkyl group, and n is a numeral in the range of 2 to 10, (R.sub.1, R.sub.2, R.sub.3, R.sub.4, and R.sub.5 may have substituent groups.)