Method of producing fine metal spheres of uniform size

A method of producing soft fine metal spheres for semiconductor packaging from a material selected from gold and copper, said method comprising the steps of:

• a) feeding a fine wire made from one of gold and copper by a predetermined length out of the outlet end of a guide having a fine internal bore,said wire having a diameter not more than 100 .mu.m;
• b) cutting said wire into wire chips having an equal mass relative to each other and a chip length/chip diameter ratio between 5 and 100 by actuating a cutting device arranged in close proximity of said outlet end;
• c) arranging the wire chips so that the wire chips are spaced apart a minimum distance sufficient to prevent the chips from merging when melted;
• d) heating the resulting spaced-apart wire chips up to but not exceeding 100.degree. C. above the melting point thereof, thereby forming said wire chips into molten spheres;
• and
• e) cooling the resulting molten spheres, thereby forming solid spheres.

A method of producing soft fine metal spheres for semiconductor packaging from a material selected from gold and copper, said method comprising the steps of:

• a) disposing both a first guide having a minute internal bore of a first diameter, and a second guide having a fine internal bore of a diameter greater than that of said first guide so that said internal bores of said first and second guides are aligned with each other;
• b) inserting a fine wire made from one of gold and copper and having a diameter of not more than 100 .mu.m through said bores of said first and second guides until the end of the fine wire is received by a predetermined length in said bore of said second guide;
• c) causing a relative radial movement between said first guide and said second guide, thereby shearing the fine wire into a wire chip having a chip length/chip diameter ratio between 5 and 100;
• d) repeating steps (b) and (c), thereby forming a plurality of wire chips having an equal mass relative to each other;
• e) arranging the wire chips so that the wire chips are spaced apart a minimum distance sufficient to prevent the chips from merging when melted;
• f) heating the resulting spaced-apart wire chips up to but not exceeding 100.degree. C. above the melting point thereof, thereby forming said wire chips into molten spheres;
• and
• g) cooling the resulting molten spheres, thereby forming solid spheres.

A method of producing soft fine metal spheres for semiconductor packaging from a material selected from gold and copper, said method comprising the steps of:

• a) holding the end of a fine wire made from one of gold and copper and of not more than 100 .mu.m in diameter by a holding device;
• b) moving the holding device, thereby extracting said fine wire from a guide by a predetermined length;
• c) cutting said fine wire into a wire chip having a chip length/chip diameter ratio between 5 and 100 by utilizing a cutting device disposed in close proximity of said holding device;
• d) repeating steps (b) and (c), thereby forming a plurality of wire chips having an equal mass relative to each other;
• e) arranging the wire chips so that the wire chips are spaced apart a minimum distance sufficient to prevent the chips from merging when melted;
• f) heating the resulting spaced-apart wire chips up to but not exceeding 100.degree. C. above the melting point thereof, thereby forming said wire chips into molten spheres;
• and
• g) cooling the resulting molten spheres, thereby forming solid spheres.

A method of producing soft fine metal spheres for semiconductor from a material selected from gold and copper, said method comprising the steps of:

• a) extracting a fine wire made from one of gold and copper and of not more than 100 .mu.m in diameter by a predetermined length out of a guide by means of feed rolls arranged on the outlet side of said guide;
• b) cutting said fine wire into a wire chip having a chip length/chip diameter ratio between 5 and 100 by utilizing a cutting device disposed in close proximity to said feed rolls;
• c) repeating steps (a) and (b), thereby forming a plurality of wire chips having an equal mass relative to each other;
• d) arranging the wire chips to that the wire chips are spaced apart a minimum distance sufficient to prevent the chips from merging when melted;
• e) heating the resulting spaced-apart wire chips up to but not exceeding 100.degree. C. above the melting point thereof, thereby forming said wire chips into molten spheres;
• and
• f) cooling the resulting spheres, thereby forming solid spheres.

A method of producing soft fine metal spheres for semiconductor packaging from a material selected from gold and copper, said method comprising the steps of:

• a) arranging a cutting device having a first roll provided with a plurality of cutting edges disposed at a predetermined circumferential pitch, a second roll in contact with said first roll, and a guide portion for guiding a fine wire between said first and second rolls;
• b) driving at least one of said first roll and said second roll, thereby clamping and tracking a fine wire made from one of gold and copper and not more than 100 .mu.m in diameter into a nip between said first and second rolls and thereby cutting said fine wire into wire chips having an equal mass relative to each other and a chip length/chip diameter ratio between 5 and 100 by utilizing said cutting edges;
• c) arranging the wire chips so that the wire chips are spaced apart a minimum distance sufficient to prevent the chips from merging when melted;
• d) heating the resulting spaced-apart wire chips up to but not exceeding 100.degree. C. above the melting point thereof, thereby forming said wire chips into molten spheres;
• and
• e) cooling the resulting molten spheres, thereby forming solid spheres.

A method of producing soft fine metal spheres for semiconductor packaging from a material selected from gold and copper, said method comprising the steps of:

• a) preparing wire chips from one of gold and copper, each chip having a diameter not more than 100 .mu.m, an equal mass relative to each other, and a chip length/chip diameter ratio between 5 and 100;
• b) arranging the wire chips spaced apart a minimum distance sufficient to prevent the chips from merging when melted;
• c) conveying said wire chips through a heating means, thereby heating said wire chips to a temperature up to but not exceeding 100.degree. C. above the melting point thereof, and thereby forming said chips into molten spheres;
• and
• d) cooling the resulting molten spheres to solidify said spheres, thereby forming solid spheres.

A method of producing soft fine metal spheres for semiconductor packaging from a material selected from gold and copper, said method comprising the steps of:

• a) providing a heat resistant base plate having a top surface defining a plurality of recesses,
• b) stretching a fine wire made from one of gold and copper and of not more than 100 .mu.m in diameter across said recesses such that the ratio of the diameter relative to the amount the wire spans each groove is between 5 and 100, and
• c) heating the stretched fine wire to a temperature up to but not exceeding 100.degree. C. above its melting point, thereby melting said fine wire and separate said fine wire into uniform portions while simultaneously forming the resulting separated portions of wire into molten spheres;
• d) cooling the resulting molten spheres, thereby forming solid spheres.