Reactor blend polypropylene, process for the preparation thereof and process for preparing metallocene ligands

Abstract

Fractionable, reactor blend polypropylenes, directly obtainable from the polymerization reaction of propylene, having: (a) content of isotactic pentads (mmmm) comprised between 25 and 85%; (b) ratio M.sub.w,/M.sub.n <5; containing from 10 to 70% by weight of a fraction soluble in boiling diethyl ether, said fraction having a content of isotactic pentads (mmmm) comprised between 5 and 25%, and from 30 to 90% by weight of a boiling n-heptane-insoluble fraction, soluble in xylene at 135.degree. C., said fraction having a content of isotactic pentads (mmmm) comprised between 50 and 99%, are disclosed. These polymers are suitable as thermoplastic-elastomeric materials. A process for the preparation of these polymers and a process for the preparation of 2-aryl-substituted indenyl metallocene ligands is also disclosed.

Dependencies are inferred from the claim text.