US 5,741,349 A · Refractory lining system for high wear area of high temperature reaction vessel

Abstract

A refractory-lined high temperature reaction vessel comprises a refractory ring lining constructed of refractory brick, a cooler, and a heat transfer medium disposed between the refractory ring lining and the cooler. The refractory brick comprises magnesia (MgO) and graphite. The heat transfer medium contacts the refractory brick and a cooling surface of the cooler, and is composed of a material that accommodates relative movement between the refractory brick and the cooler. The brick is manufactured such that the graphite has an orientation providing a high thermal conductivity in the lengthwise direction through the brick that is higher than the thermal conductivity in directions perpendicular to the lengthwise direction. The graphite preferably is flake graphite, in the range of about 10 to 20 wt %, and has a size distribution selected to provide maximum brick density. The reaction vessel may be used for performing a reaction process including the steps of forming a layer of slag on a melt in the vessel, the slag having a softening point temperature range, and forming a protective frozen layer of slag on the interior-facing surface of the refractory lining in at least a portion of a zone where the surface contacts the layer of slag, the protective frozen layer being maintained at or about the softening point of the slag.

Claims20

Dependent claims

A smelting method for use in a vessel including a refractory lining having a surface that faces the interior of the vessel, and a hollow cooler disposed exterior to the refractory lining, the cooler including a cooler hot face surface in thermal contact with the refractory lining, and a coolant heat transfer surface in contact with a moving coolant having a thermal conductivity, the method comprising the steps of:

forming a layer of slag on a melt in the vessel, the slag in said layer of slag having a softening point temperature range;
and
forming a protective frozen layer of slag on the interior facing surface of the refractory lining in at least a portion of a zone where the interior facing surface contacts the layer of slag, and maintaining the protective frozen layer of slag in or about the softening point temperature range of the slag.

A smelting method for use in a vessel including a refractory lining having a surface that faces the interior of the vessel and a hollow cooler disposed exterior to the refractory lining, the cooler including a cooler hot face surface in thermal contact with the refractory lining and a coolant heat transfer surface in contact with a moving coolant having a thermal conductivity, the vessel being a smelter having a postcombustion zone, the cooler having a thickness of about 20 mm, a cooler hot face surface having a minimum specific heat capacity of about 320 kcal/m/h/.degree.C. (at 0.degree. C.), a maximum ratio of cooler panel hot face to coolant contact surface of about 1.3, and a minimum coolant flow velocity of about 2.4 m/s, the method comprising the steps of:

forming a substantially horizontal layer of slag on a melt in the vessel, the slag in said layer having a softening point temperature range;
forming a protective frozen layer of slag on the interior facing surface of the refractory lining in at least a portion of a zone where the interior facing surface contacts the substantially horizontal layer of slag, and maintaining the temperature of the protective frozen layer of slag in or about the softening point temperature range of the slag, said frozen slag layer forming and maintaing step including:
controlling the temperature of the slag adjacent the refractory lining at least in the postcombustion zone of the vessel;
maintaining a slag thickness in the range of about 0.12 to about 0.25 inch, maintaining the process temperature in a range of about 1500.degree. C. to about 1800.degree. C., and maintaining the thermal conductivity in a range of about 12.5 to about 25 BTU-in/ft.sup.2 -.degree.F.-hr;
circulating a coolant through the cooler at a rate sufficient to extract heat through the refractory lining, from the layer of slag to the cooler, so that a thin frozen layer of slag is formed and maintained on the interior facing surface of the refractory lining;
selecting a ratio of effective cooler hot surface area to coolant heat transfer surface area to maximize extraction of heat in the coolant circulating step;
and
selecting a flow rate of coolant through the cooler sufficient to maintain the coolant at a temperature below the boiling point of the coolant and to substantially suppress nucleate boiling of the coolant;
maintaining the operating pressure in the vessel in a range of about 10 to 50 psi;
injecting O.sub.2 in the postcombustion zone in the vessel;
and
including magnesia (MgO) in the layer of slag in an amount sufficient to promote formation of a slag coating.

9 more elements

Dependencies are inferred from the claim text.

Refractory lining system for high wear area of high temperature reaction vessel

Life of this patent

Refractory lining system for high wear area of high temperature reaction vessel

Life of this patent

Abstract

Claims20