Tire having good diverse properties

A pneumatic tire comprising a pair of parallel annular beads, at least one radial carcass ply wrapped around said beads, a tread radially above a crown portion of said carcass ply, and sidewalls disposed between said tread and said beads, wherein said tread comprises a tread base including tread base rubber and a tread cap including tread cap rubber wherein said tread base rubber has a 300% modulus of 16 to 19 MPa, a tensile strength at break of 17.5 to 22.5 MPa, elongation at break of 270 to 435%, RT (room temperature) rebound of 57 to 64, a tan delta at 10% strain of 0.075 to 0.11, G' at 1% strain of 1770 to 2070 KPa, a G' at 50% strain of 790 to 1010 KPa, and an E' of 0.1 to 0.13.times.10.sup.9 dynes/cm.sup.2, and said tread cap rubber has a 300% modulus of 8 to 11 MPa, a tensile strength at break of 15 to 20 MPa, an elongation at break of 420 to 530%, RT Rebound of 45 to 54, a tan delta at 10% strain of 0.090 to 0.12, G' at 1% strain of 990 to 1350 KPa, a G' at 50% strain of 540 to 700 KPa, E' of 0.06 to 0.08.times.10.sup.9 dynes/cm.sup.2, and wherein lateral grooves in a shoulder of the tire have an angle of about 80 degrees with respect to the center line of the tread and all said lateral grooves vary in width less than 10%, and a circumferential scribe line having a depth of 8% to 16% of the maximum tread depth and a width of 2% to 5% of a shoulder block width divides a shoulder block into an inner portion and an outer portion wherein the inner portion comprises 10% to 40% of the width of the shoulder block as measured from an adjacent circumferential groove to the shoulder of the tire, and walls of circumferential grooves in said tread have an angle of 7 degrees with respect to a line perpendicular to the tread surface, and wherein said carcass is shaped in a mold to have a footprint factor of less than 1.3 at standard inflation and load, and wherein said tread at a center rib has a depth of 0.32 inch.

A tire tread comprising a tread base including tread base rubber and a tread cap including tread cap rubber wherein said tread base rubber has a 300% modulus of 16 to 19 MPa, a tensile strength at break of 17.5 to 22.5 MPa, elongation at break of 270 to 435%, RT (room temperature) rebound of 57 to 64, a tan delta at 10% strain of 0.075 to 0.11, G' at 1% strain of 1770 to 2070 KPa, a G' at 50% strain of 790 to 1010 KPa, and an E' of 0.1 to 0.13.times.10.sup.9 dynes/cm.sup.2, and said tread cap rubber has a 300% modulus of 8 to 11 MPa, a tensile strength at break of 15 to 20 MPa, an elongation at break of 420 to 530%, RT Rebound of 45 to 54, a tan delta at 10% strain of 0.090 to 0.12, G' at 1% strain of 990 to 1350 KPa, a G' at 50% strain of 540 to 700 KPa, E' of 0.06 to 0.08.times.10.sup.9 dynes/cm.sup.2, and wherein the tread depth in a shoulder of the tread is about 84% to 100% of the maximum tread depth and wherein lateral grooves in a shoulder of the tire have an angle of 75 to 90 degrees with respect to the center line (CL) of the tread and all said lateral grooves vary from each other in width less than 25%, and a circumferential scribe line having a depth of 8% to 16% of the maximum tread depth and a width of 2% to 5% of a shoulder block width divides a shoulder block into two portions wherein an inner portion has a width comprising 10% to 40% of the width of the shoulder block as measured from an adjacent circumferential groove to the shoulder of the tread, and walls of circumferential grooves in said tread have an angle of 5 to 20 degrees with respect to a line perpendicular to the tread surface.