Aluminous press plate and process for producing same
AssigneeFormica Corporation
InventorsAlan Thomas Brooker, Pascale Marie Elisabeth Cordiez
Life of this patent
Estimating the term…
Abstract
A press plate for decorative laminate production has an aluminum alloy core plate exhibiting a 0.2% compressive yield stress of not less than about 180 MPa at 140.degree. C., an aluminum cladding layer integrally bonded to opposing surfaces of the core plate, and a layer of aluminum oxide formed on the aluminous cladding which is substantially free of grain line effects.
Claims17
An aluminous press plate for producing decorative laminates from decorative laminate materials, in a press apparatus, said plate comprising:
- (a) a substantially flat core plate having opposed planar pressing surfaces of substantial area, the core plate being composed of an aluminum alloy having a 0.2% compressive yield stress of not less than about 180 MPa at 140.degree. C.;
- (b) a thin cladding layer of aluminum of not less than about 99% purity integrally bonded to the opposed planar surfaces of the core plate;
- and
- (c) a continuous film of aluminum oxide on the aluminum cladding, the Al.sub.2 O.sub.3 film being substantially free of grain line effects and substantially defining a surface finish of the decorative laminate.
An aluminous press plate as defined in any one of the preceding claims in which the film of Al.sub.2 O.sub.3 has a thickness selected from the range of about 10 to 50 microns.
A press apparatus for producing decorative laminate sheets comprising:
- (a) means for supporting resinous mixtures and substrate materials as a substantially planar layer;
- (b) an aluminous press plate having
- (i) a core of an aluminum alloy having a 0.2% compressive yield stress of not less than about 180 MPa at 140.degree. C.,
- (ii) a thin cladding layer of aluminum of not less than about 99% purity integrally bonded to the opposed planar surfaces of the core, and
- (iii) a continuous film of Al.sub.2 O.sub.3 having a thickness of up to about 50 microns on the aluminum cladding, the Al.sub.2 O.sub.3 film being substantially free to grain line effects;
- and
- (c) means to urge the Al.sub.2 O.sub.3 film against the resinous mixture and substrate material to form a generally planar laminate sheet.
A process for producing an aluminous press plate for producing decorative laminate sheets, the steps comprising:
- (a) providing a aluminous core plate having opposed planar pressing surfaces of substantial area, which core plate is composed of an aluminum alloy having a 0.2% compressive yield stress of not less than about 180 MPa at 140.degree. C.;
- (b) diffusion bonding a thin cladding layer of aluminum of not less than about 99% purity to the planar surfaces of the core;
- and
- (c) oxidizing the thin cladding layer to form a film of Al.sub.2 O.sub.3.