# US 5,708,045 A · Very low density molded polyurethane foams via isocyanate-terminated prepolymers

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 5,708,045 A
- Document ID: US5708045A
- Status: Granted
- Kind: A
- Application number: 08/826,358
- Filed: 1997-03-26
- Granted: 1998-01-13
- Earliest claimed: 1995-10-18
- Assignees: Arco Chemical Technology, L.P.
- Inventors: Andrew M. Thompson; James L. Lambach
- Web page: https://patentgrep.com/patent/US5708045A

## CPC

- C08G 18/10: Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step
- C08G 18/48: Polyethers
- C08G 18/4837: {and other oxyalkylene units}
- C08G 2110/0008: flexible
- C08G 2110/005: < 50kg/m3
- C08G 2110/0083: prepared using water as the sole blowing agent
- C08G: MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS

## Abstract

Very soft, very low density, all water-blown polyurethane foams are prepared by reacting an isocyanate-terminated prepolymer with from 30% to 150% stoichiometric excess of water. The foams have molded densities less than or equal to 1.5 lb/ft.sup.3 and softness, as measured by 25% ILD of less than or equal to 15 lbs., yet retain excellent resiliency, tear strength and elongation. The foams are suitable for use in cushioning applications such as those traditionally employing polyester fiberfill.

## Claims

### Claim 1

An all water-blown, isocyanate-terminated prepolymer-derived, polyurethane molded foam having a molded density less than or equal to 1.5 lb/ft.sup.3 and a softness, as measured by 25% ILD, of less than or equal to 15 lbs, said molded foam prepared by a process comprising:
a) providing an isocyanate-terminated prepolymer prepared by reacting an excess of one or more di- or polyisocyanates with a polyoxyalkylene polyether polyol component having a nominal, average functionality of between 2 and 8, a hydroxyl number of between about 12 and 56, and an oxyethylene content of between 0 and 30 weight percent, said polyoxyalkylene polyether component comprised of one or more polyoxyalkylene polyether polyols, such that said isocyanate-terminated prepolymer has a free NCO group content of between 12 and 22 weight percent;
b) mixing with said isocyanate-terminated prepolymer, water as a reactive blowing agent, in an amount of 30 mol percent to 150 mol percent in stoichiometric excess, based on the free NCO group content of said isocyanate-terminated prepolymer, to form a foamable polyurethane reactive mixture;
c) introducing said foamable polyurethane reactive mixture into a mold; and
d) recovering a foamed polyurethane product.

### Claim 2 (depends on 1)

The molded foam of claim 1 wherein said polyoxyalkylene polyether polyol component has an average nominal functionality of from 2 to about 3; said isocyanate-terminated prepolymer has a free NCO group content of from 14 to about 20 weight percent; and wherein water is employed in an amount from 30 mol percent to 80 mol percent in excess of the stoichiometric amount based on the NCO group content of said isocyanate-terminated prepolymer.

### Claim 3 (depends on 2)

The molded foam of claim 2 wherein at least one of said polyoxyalkylene polyols in said polyoxyalkylene polyether polyol component has an oxyethylene content of from 5 to 30 weight percent.

### Claim 4 (depends on 1)

The molded foam of claim 1 wherein said di- or polyisocyanate is selected from the group consisting of TDIs, MDIs, and mixtures thereof.

### Claim 5 (depends on 1)

The process of claim 1 further comprising one or more polymerization catalysts in an amount of from 0.1 to about 5.0 weight percent based on foam weight.

### Claim 6 (depends on 1)

The molded foam of claim 1 wherein said polyoxyalkylene polyol component comprises a polyoxyalkylene diol having an equivalent weight of from 1000 Da to 5000 Da and an oxyethylene content of 0% to 30% by weight.

### Claim 7 (depends on 6)

The molded foam of claim 6 wherein said polyoxyalkylene polyol component further comprises a polyoxyalkylene triol having an equivalent weight of from 1000 Da to 5000 Da and an oxyethylene content of 0% to 30% by weight.

### Claim 8 (depends on 6)

The molded foam of claim 6 wherein said di- or polyisocyanate comprises TDIs, or a mixture of TDIs and MDIs.

### Claim 9 (depends on 1)

The molded foam of claim 1 wherein said molded density is about 1.3 lbs/ft.sup.3 or less.

### Claim 10 (depends on 1)

The molded foam of claim 1 wherein said molded density is about 1.0 lb/ft.sup.3 or less.

### Claim 11 (depends on 1)

The molded foam of claim 1 wherein said polyoxyalkylene polyether polyol component contains a polymer-modified polyoxyalkylene polyether polyol.

### Claim 12 (depends on 1)

The molded foam of claim 1 wherein said isocyanate-terminated prepolymer is a reaction product of a mixture of TDIs and MDIs; said polyoxyalkylene polyol component comprises a polyoxyalkylene diol having an equivalent weight of from 1500 Da to 3000 Da and an oxyethylene content of from 8% to about 20% by weight; said isocyanate-terminated prepolymer has an NCO group content of from 14 to about 20 weight percent by weight; and water is employed in an amount of from about 35 mol percent to 65 mol percent in stoichiometric excess based on the NCO group content of said isocyanate-terminated prepolymer.