# US 5,707,918 A · Hydrocarbon isomerization catalyst blend > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,707,918 A - Document ID: US5707918A - Status: Granted - Kind: A - Application number: 08/521,146 - Filed: 1995-08-29 - Granted: 1998-01-13 - Earliest claimed: 1995-08-29 - Assignees: Phillips Petroleum Company - Inventors: An-hsiang Wu; Charles A. Drake; Ralph J. Melton - Web page: https://patentgrep.com/patent/US5707918A ## CPC - B01J 35/19: {Catalysts containing parts with different compositions} - B01J 27/13: Platinum group metals - B01J: CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS ## Abstract A Group VIII metal- and chloride-containing composition is prepared by a method which comprises mixing (A) a solid material containing at least one Group VIII metal (Pt and/or Pd and/or Ni) and alumina as the support and (B) an alumina-supported aluminum- and chlorine-containing compound which has been prepared by mixing an alumina material with AlCl.sub.3 and/or at least one organoaluminum chloride (such as ethylaluminum dichloride), heating the mixture at a temperature of about 600.degree.-750.degree. C. and then with an HCl-containing gas at a temperature of about 100.degree.-750.degree. C. The thus-obtained composition comprising components (A) and (B) is employed as a catalyst in the isomerization of C.sub.4 -C.sub.8 alkanes and/or cycloalkanes (e.g., n-butane). ## Claims ### Claim 1 A method of preparing a solid Group VIII metal- and chlorine-containing composition which comprises blending: (A) a first solid material comprising (i) at least one Group VIII metal selected from the group consisting of platinum, palladium and nickel and (ii) alumina as the support, wherein halogens are substantially absent from said first solid material; and (B) a second solid material comprising at least one aluminum- and chlorine-containing compound and alumina as the support, wherein Group VIII metals are substantially absent from said second solid material and wherein said second solid material has been prepared by a method comprising (a) mixing a first alumina material with at least one aluminum- and chlorine-containing compound selected from the group consisting of aluminum chloride and organoaluminum chlorides; (c) heating the material obtained in step (a) in a substantially inert gas atmosphere at a temperature of about 600.degree.-750.degree. C. for a time period of at least about 10 minutes; and (c) treating the material obtained in step (b) with a hydrogen chloride-containing gas at a temperature of about 100.degree.-750.degree. C. for a time period of at least about 10 minutes. ### Claim 2 (depends on 1) A method in accordance with claim 1, wherein the weight ratio of said first solid material (A) to said second solid material (B) in said composition is about 1:40 to about 10:1. ### Claim 3 (depends on 2) A method in accordance of claim 2, wherein said at least one aluminum- and chlorine-containing compound used in step (a) is aluminum chloride. ### Claim 4 (depends on 2) A method in accordance with claim 2, wherein said at least one aluminum- and chlorine-containing compound used in step (a) is selected from the group consisting of methylaluminum dichloride, methylaluminum sesquichloride, dimethylaluminum chloride, ethylaluminum dichloride, ethylaluminum sesquichloride, diethylaluminum chloride, propylaluminum dichloride, dipropylaluminum chloride, butylaluminum dichloride, dibutylaluminum chloride and mixtures thereof. ### Claim 5 (depends on 2) A method in accordance with claim 2, wherein the weight ratio of said at least one aluminum- and chlorine-containing compound to said first alumina material in step (a) is about 0.05:1 to about 1:1, wherein time period of step (b) is about 0.5-20 hours, and the time period of step (c) is about 0.2-20 hours. ### Claim 6 (depends on 5) A method in accordance with claim 5 wherein step (c) is carried out at a temperature of about 250.degree.-650.degree. C. for a time period of about 0.5-3 hours. ### Claim 7 (depends on 2) A method in accordance with claim 2, wherein said first solid material (A) has been prepared by a method comprising (1) impregnating a second alumina material with at least one compound of at least one Group VIII metal selected from the group consisting of platinum, palladium and nickel; (2) calcining the impregnated alumina material obtained in step (1) at a temperature of about 300.degree.-650.degree. C. for a time period of at least about 10 minutes; and (3) treating the calcined material obtained in step (2) with a reducing gas at a temperature of about 200.degree.-550.degree. C. for a time period of at least about 10 minutes. ### Claim 8 (depends on 7) A method in accordance with claim 7, wherein said second alumina material is impregnated in step (1) with at least one dissolved platinum compound. ### Claim 9 (depends on 8) A method in accordance with claim 8, wherein said second alumina material is also impregnated with at least one dissolved titanium compound. ### Claim 10 (depends on 7) A method in accordance with claim 7, wherein said second alumina material is impregnated in step (1) with least one palladium compound. ### Claim 11 (depends on 7) A method in accordance with claim 7, wherein said second alumina material is impregnated in step (1) with at least one nickel compound. ### Claim 12 (depends on 7) A method in accordance with claim 7, wherein the time period of step (2) is about 0.5-20 hours, the time period of step (3) is about 0.5-200.degree. C., and said reducing gas used in step (3) comprises free hydrogen. ### Claim 13 A method in accordance with step 7, wherein said second alumina material used in step (1) contains about 0.5-1.0 weight-% Ti. ### Claim 14 (depends on 1) A method in accordance with claim 1, wherein said first alumina material used in step (a) contains about 0.05-1.0 weight-% Ti. ### Claim 15 (depends on 1) A method in accordance with claim 1, wherein said composition comprising said first solid material (A) and said second material (B) contains about 0.01-50 weight-% of said at least one Group VIII metal and about 1-8 weight-% Cl. ### Claim 16 (depends on 15) A method in accordance with claim 15, wherein said composition contains about 1-45 weight-% nickel. ### Claim 17 (depends on 15) A method in accordance with claim 15, wherein said composition contains about 0.1-10 weight-% of at least one Group VIII metal selected from the group consisting of platinum and palladium. ### Claim 18 (depends on 17) A method in accordance with claim 17, wherein said composition further comprises about 0.05-1.0 weight-% titanium. ### Claim 19 (depends on 1) A composition prepared by the method of claim 1. ### Claim 20 (depends on 2) A composition prepared by the method of claim 2. ### Claim 21 (depends on 3) A composition prepared by the method of claim 3. ### Claim 22 (depends on 4) A composition prepared by the method of claim 4. ### Claim 23 (depends on 7) A composition prepared by the method of claim 7. ### Claim 24 (depends on 15) A composition prepared by the method of claim 15. ### Claim 25 (depends on 16) A composition prepared by the method of claim 16. ### Claim 26 (depends on 17) A composition prepared by the method of claim 17. ### Claim 27 (depends on 18) A composition prepared by the method of claim 18. ### Claim 28 (depends on 1) A process for isomerizing at least one saturated feed hydrocarbon containing 4-8 carbon atoms per molecule selected from the group consisting of alkanes and cycloalkanes to at least one product isomer which comprises contacting said at least one saturated feed hydrocarbon and hydrogen gas at a temperature of at least 200.degree. C. with the catalyst composition prepared by the method of claim 1.