# US 5,707,598 A · Porous material composed of layered silica and metal oxide and a process for manufacturing the same > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,707,598 A - Document ID: US5707598A - Status: Granted - Kind: A - Application number: 08/192,962 - Filed: 1994-02-07 - Granted: 1998-01-13 - Earliest claimed: 1992-01-13 - Assignees: Kabushiki Kaisha Toyota Chuo Kenkyusho - Inventors: Shinji Inagaki; Yoshiaki Fukushima; Akane Okada; Chuzo Kato; Kazuyuki Kuroda - Web page: https://patentgrep.com/patent/US5707598A ## CPC - B01J 20/10: comprising silica or silicate - B01J 21/08: Silica - B01J 23/04: Alkali metals - B01J 29/049: {Pillared clays} - B01J 35/57: Honeycombs - Y10T 428/24149: Honeycomb-like - Y10T 428/249969: Of silicon-containing material [e.g., glass, etc.] - Y10T 428/24997: Of metal-containing material - B01J: CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract A porous material composed of many SiO.sub.4 tetrahedra sheets having interlayer bridges of SiO.sub.2. It has pores having a diameter of 10 .ANG. or above, and possesses the properties of a solid acid formed by the isomorphous substitution of metal atoms for Si of SiO.sub.4 frameworks. It is made by a process including introducing an organic substance into interlayer space of crystals of layered silicates to expand the spacing between crystal layers, as well as forming bridges of SiO.sub.2 therebetween, bringing the intercalated compounds into contact with a metal salt to link metal atoms to the SiO.sub.4 frameworks, and firing the products. The material can withstand a temperature of 800.degree. C., has a pore diameter larger than that of zeolites, etc., and is useful in making an adsorbent or catalyst for molecules having a high molecular weight, such as a catalyst for the catalytic cracking of petroleum. ## Claims ### Claim 1 A process for manufacturing a porous material which consists essentially of: (a) introducing an organic substance having a molecular size of at least 10 .ANG. by ion exchange into an interlayer space of crystals of layered silicates, and forming interlayer bridges of essentially SiO.sub.2 in said interlayer space between adjacent layers of said layered silicates by condensation of surface silanols of said adjacent layers, said adjacent layers having bent portions partially bonded to each other by said interlayer bridges of SiO.sub.2 thereby forming a honeycomb cross-section, wherein said organic substance is cetyltrimethylammonium, undecyltrimethylammonium or nonyltrimethylammonium, said layered silicates having bent portions partially bonded to each other by said interlayer bridges of SiO.sub.2, thereby forming a non-pillared honeycomb cross-section; (b) bringing said crystals into contact with a metal cation; and (c) firing said crystals at a temperature sufficient for removal of said organic substance; the steps being carried out in the order of either (a) then (b) then (c); (b) then (a) then (c); (a) and (b) together, then (c); or (a) then (c) then (b) and then (c) again, the steps (a), (b) and (c) performed under conditions so that said porous material formed has a multiplicity of pores with a diameter of at least 10 .ANG., and said pores having a substantially uniform diameter, and said porous material formed possessing properties of a solid acid from said contact with said metal cations. ### Claim 2 (depends on 1) The process of claim 1, wherein said ion exchange is carried out by exchanging cations of said organic substance for sodium ions existing between said layers. ### Claim 3 (depends on 2) The process of claim 2, wherein said cations are of a single organic substance. ### Claim 4 (depends on 2) The process of claim 2, wherein said cations are of a plurality of different organic substances having different molecular sizes or weights. ### Claim 5 (depends on 1) The process of claim 1, wherein said step (a) is carried out at a temperature of about 65.degree. C. and for a period of about a week. ### Claim 6 (depends on 1) The process of claim 1, wherein said step (b) is carried out by dipping said crystals in a solution of said metal cation. ### Claim 7 (depends on 1) The process of claim 1, wherein said step (c) is carried out at a temperature of 500.degree. C. to 800.degree. C. and for a period of several hours. ### Claim 8 (depends on 1) The process of in claim 1, wherein said step (c) is carried out in any single gas or combination of gases including as a component at least either oxygen, or ozone, or oxygen and ozone together for promoting said removal of said organic substances. ### Claim 9 A process for manufacturing a porous material which comprises: (a) introducing at least one organic substance having a molecular size of at least 10 .ANG. by ion exchange into an interlayer space of crystals of layered silicates, and forming interlayer bridges of SiO.sub.2 by condensation of surfaces silanols; (b) mixing a powder of said crystals with a powder of a salt of a metal; and (c) firing said crystals at a temperature sufficient for removal of said organic substance; the steps being carried out in the order of either (a) then (b) then (c); (b) then (a) then (c); (a) and (b) together, then (c); or (a) then (c) then (b) and then (c) again, thereby forming a porous structure having a honeycomb cross-section. ### Claim 10 (depends on 9) The method of claim 9, wherein the crystals are fired at a temperature of about 500.degree. C. to 800.degree. C.