# US 5,707,478 A · Method for producing thermoplastic resin sheet or film > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,707,478 A - Document ID: US5707478A - Status: Granted - Kind: A - Application number: 08/523,758 - Filed: 1995-09-05 - Granted: 1998-01-13 - Earliest claimed: 1993-02-25 - Assignees: Idemitsu Petrochemical Co., Ltd. - Inventors: Atsushi Fujii; Akira Funaki; Tohru Yukumoto - Web page: https://patentgrep.com/patent/US5707478A ## CPC - B29C 59/046: {for layered or coated substantially flat surfaces} - B29C 48/08: flexible, e.g. films - B32B 37/1036: {Pressing between one press band and a cylinder} - B29C 48/00: Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor (extrusion blow-moulding B29C49/04) - B29C: SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING (making preforms B29B11/00; making laminated products by combining previously unconnected layers which become one product whose layers will remain together B32B37/00 - B32B41/00) - B32B: LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM ## Abstract A method is provided for producing a thermoplastic resin sheet or film by hot-melting and then cooling a thermoplastic resin to form a sheet or film. The thermoplastic resin sheet or film is moved so that it is pressed against the outer surface of an external heated roll and against a heated, endless metal belt. The endless metal belt is disposed at one end around a moving, internal heating roll and at an opposite end thereof around a moving, internal cooling roll. The internal heating roll heats the endless metal belt to a temperature higher than the softening point of the thermoplastic resin and higher than the temperature of the external heating roll to thermally adhere the thermoplastic resin sheet or film to the external heated roll or the heated, endless metal belt. The thermoplastic resin sheet or film is then moved along on the external heated roll or belt into a high temperature zone. The thermoplastic resin sheet or film is then released from the contact with the external heated roll and released from contact with the endless metal belt in a low temperature zone. The thermoplastic resin sheet or film is then peeled from the endless metal belt. Methods are also provided for producing a laminate of two or more thermoplastic resin sheets or films. The above methods provide non-stretched thermoplastic resin sheets, films or laminates with high-quality surfaces, which are suitable for wrapping foods and medicines. ## Claims ### Claim 1 A method for producing a thermoplastic resin sheet or film comprising: (a) hot-melting and then cooling a thermoplastic resin to provide a thermoplastic resin sheet or film, (b) providing an external heated roll, the external heated roll being heated to a temperature higher than a softening point of the thermoplastic resin sheet or film and providing a moving, heated, endless metal belt, the moving, heated, endless metal belt being disposed at one end around a moving, internal heating roll and at an opposite end thereof around a moving, internal cooling roll, the internal heating roll heating the moving, heated, endless metal belt to a temperature higher than the softening point of the thermoplastic resin and higher than the temperature of the external heating roll to provide a high temperature zone, the external heating roll being in contact with the moving, heated, endless metal belt, (c) moving the resin sheet or film from step (a) so that the resin sheet or film presses against an outer surface of the external heated roll or presses against an outer surface of the moving, heated, endless metal belt to thermally adhere the thermoplastic resin sheet or film to the external heated roll or to the moving, heated, endless metal belt, (d) moving the resin sheet or film along with the external heated roll or the moving, heated, endless metal belt into said high temperature zone so that the resin sheet or film is pressed between the outer surface of the external heated roll and the outer surface of the moving, heated, endless metal belt in said high temperature zone, (e) releasing the thermoplastic resin sheet or film from contact with the external heated roll in said high temperature zone, (f) releasing the thermoplastic resin sheet or film from contact with the moving, heated, endless metal belt in a low temperature zone adjacent to the internal cooling roll and (g) peeling the thermoplastic resin sheet or film from the moving, heated, endless metal belt. ### Claim 2 (depends on 1) The method as claimed in claim 1, in which the thermoplastic resin sheet or film is pressed under a pressure of 1 kg/cm.sup.2 or higher. ### Claim 3 (depends on 1) The method as claimed in claim 1, in which the external hot roll and the moving heated, endless metal belt are maintained at a temperature such that the thermoplastic resin sheet or film is at a temperature of 120.degree. C. to 350.degree. C. ### Claim 4 (depends on 1) The method as claimed in claim 1, in which the moving, heated, endless metal belt moves at a speed of 10 to 40 m/minute. ### Claim 5 (depends on 1) The method as claimed in claim 1, in which the external heated roll is at a temperature of 130.degree. C. and the moving, heated, endless metal belt is at a temperature of 145.degree. C. ### Claim 6 (depends on 1) The method as claimed in claim 1, in which the external heated roll is at a temperature of 140.degree. C. and the moving, heated, endless metal belt is at a temperature of 150.degree. C. ### Claim 7 (depends on 1) The method as claimed in claim 1, wherein there is a temperature difference of at least 1.degree. C. in the high temperature zone between the moving, heated, endless metal belt and the external heated roll. ### Claim 8 A method for producing a laminate sheet or film made of two separate thermoplastic resin sheets or films comprising: (a) hot-melting and then cooling a first thermoplastic resin and a second thermoplastic resin to respectively form a first thermoplastic resin sheet or film and a second thermoplastic resin sheet or film, (b) providing a moving, external heated roll, the moving, external heated roll being heated to a temperature higher than a softening point of the first thermoplastic resin sheet or film, (c) providing a moving, heated, endless metal belt, the moving, heated endless metal belt being disposed at one end around a moving internal heated roll and at an opposite end thereof around a moving internal cooling roll, the internal heated roll heating the moving, heated endless metal belt to a temperature higher than the softening point of the first and second thermoplastic resins and higher than the temperature of the moving, external heated roll to provide a high temperature zone, (d) moving said first thermoplastic resin sheet or film from step (a) to said high temperature zone so that said first thermoplastic resin sheet or film is pressed by and adhered to an outer surface of the moving, external heated roll, (e) moving said second thermoplastic resin sheet or film from step (a) to be pressed by and adhered to an outer surface of the moving, heated, endless metal belt, (f) moving each of said first thermoplastic resin sheet or film and said second thermoplastic resin sheet or film respectively along with the external heated roll and the moving, heated, endless metal belt, (g) moving said first thermoplastic resin sheet or film and said second thermoplastic resin sheet or film between the outer surface of the moving, external heated roll and the outer surface of the moving, heated, endless metal belt, to press together said first thermoplastic resin sheet or film and said second thermoplastic resin sheet or film and to form a laminate, (h) releasing the laminate from contact with the moving, external heated roll in said high temperature zone, (i) releasing the laminate from contact with the moving, heated, endless metal belt in a low temperature zone adjacent to the internal cooling roll, and (j) removing the laminate from the moving, heated, endless metal belt. ### Claim 9 (depends on 8) The method as claimed in claim 8, in which the first and second thermoplastic resin sheets or films are pressed under a pressure of 1 kg/cm.sup.2 or higher. ### Claim 10 (depends on 9) The method as claimed in claim 9, in which the thermoplastic resin is selected from the group consisting of polyethylene, polypropylene, polyethylene terephthalate, polystyrene, polycarbonate, polyvinyl chloride and polymethyl methacrylate. ### Claim 11 (depends on 10) The method as claimed in claim 10, in which the thermoplastic resin sheet or film has a thickness of 0.1 to 2 mm. ### Claim 12 (depends on 10) The method as claimed in claim 10, in which the thermoplastic resin sheet or film has a thickness of 0.2 to 1.0 mm. ### Claim 13 (depends on 12) The method as claimed in claim 12, in which the thermoplastic resin sheet or film is pressed under a pressure of 3 to 600 kg/m.sup.2. ### Claim 14 (depends on 9) The method as claimed in claim 9, in which the external heated roll and the moving, heated, endless metal belt are each independently maintained at a temperature such that the first and second thermoplastic resin sheets or films are at a temperature of 120.degree. C. to 350.degree. C.; and the moving, heated, endless metal belt moves at a speed of 10 to 40 m/minute. ### Claim 15 (depends on 9) The method as claimed in claim 9, in which each of the first and second thermoplastic resins are selected from the group consisting of polyethylene, polypropylene, polyethylene terephthalate, polystyrene, polycarbonate, polyvinyl chloride and polymethyl methacrylate; and the first and second thermoplastic resin sheets or films each having a thickness of 0.1 to 2 mm. ### Claim 16 (depends on 8) The method as claimed in claim 8, wherein there is a temperature difference of at least 1.degree. C. in the high temperature zone between the moving, heated, endless metal belt and the external heated roll. ### Claim 17 A method for producing a laminate sheet or film made of at least first, second and third separate thermoplastic resin sheets or films comprising: (a) hot-melting and then cooling each of first, second and third separate thermoplastic resins to respectively form first, second and third separate thermoplastic resin sheets or films, (b) providing a moving, external heated roll, the moving, external heated roll being heated to a temperature higher than a softening point of the first thermoplastic resin sheet or film, and providing a moving, endless metal belt which is disposed at one end around a moving, internal heating roll and at an opposite end thereof around a moving, internal cooling roll, the internal heating roll heating the moving, endless metal belt to a temperature higher than the softening point of the thermoplastic resins and higher than the temperature of the moving, external heated roll to provide a high temperature zone, (c) moving said first thermoplastic resin sheet or film from step (a) to said high temperature zone so that said first thermoplastic resin sheet or film is pressed by and adhered to an outer surface of the moving external heated roll, (d) moving said second thermoplastic resin sheet or film from step (a) so that said second thermoplastic resin sheet or film is pressed by and adhered to the outer surface of the moving, heated, endless metal belt, (e) moving each of said first thermoplastic resin sheet or film and said second thermoplastic resin sheet or film respectively along with the moving, external heated roll and the moving, heated, endless metal belt, (f) inserting said third thermoplastic resin sheet or film between said first thermoplastic resin sheet or film and said second thermoplastic resin sheet or film, (g) optionally inserting at least one further thermoplastic resin sheet or film between said first thermoplastic resin sheet or film and said second thermoplastic resin sheet or film, (h) pressing together all of said thermoplastic resin sheets or films between the outer surface of the moving, external heated roll and the outer surface of the moving, heated, endless metal belt to form a laminate, (i) releasing the laminate from contact with the moving, external heated roll in said high temperature zone, (j) releasing the laminate from contact with the moving, heated, endless metal belt in a low temperature zone adjacent to the internal cooling roll, and (k) removing the laminate from the moving, heated, endless metal belt. ### Claim 18 (depends on 17) The method as claimed in claim 17, in which all the thermoplastic resin sheets or films are pressed under a pressure of 1 kg/cm.sup.2 or higher. ### Claim 19 (depends on 18) The method as claimed in claim 18, in which the thermoplastic resins are selected from the group consisting of polyethylene, polypropylene, polyethylene terephthalate, polystyrene, polycarbonate, polyvinyl chloride and polymethyl methacrylate; and the thermoplastic resin sheets or films each have a thickness of 0.1 to 2 mm. ### Claim 20 (depends on 18) The method as claimed in claim 18, in which the external heated roll and the moving, heated, endless metal belt are each independently maintained at a temperature such that the thermoplastic resin sheets or films are at a temperature of 120.degree. C. to 350.degree. C.; and the moving, heated, endless metal belt moves at a speed of 10 to 40 m/minute. ### Claim 21 (depends on 17) The method as claimed in claim 17, wherein there is a temperature difference of at least 1.degree. C. in the high temperature zone between the moving, heated, endless metal belt and the external heated roll.