# US 5,707,436 A · Process for the production of purple pigments > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,707,436 A - Document ID: US5707436A - Status: Granted - Kind: A - Application number: 08/412,972 - Filed: 1995-03-29 - Granted: 1998-01-13 - Earliest claimed: 1994-03-30 - Assignees: Cerdec Aktiengesellschaft Keramische Farben - Inventors: Klaus-Dieter Fritsche; Bernd Dorbath; Norbert Giesecke; Kerstin Ruhnau - Web page: https://patentgrep.com/patent/US5707436A ## CPC - C03C 8/14: Glass frit mixtures having non-frit additions, e.g. opacifiers, colorants, mill-additions - C03C 1/04: Opacifiers, e.g. fluorides or phosphates; Pigments - C09C 1/0078: {Pigments consisting of flaky, non-metallic substrates, characterised by a surface-region containing free metal} - C09C 1/28: Compounds of silicon {(C09C1/0009, C09C1/0015, C09C1/0078 take precedence)} - C09C 3/066: {Treatment or coating resulting in a free metal containing surface-region (C09C1/0078 takes precedence)} - C01P 2002/02: Amorphous compounds - C01P 2004/84: one phase coated with the other - Y10T 428/2993: Silicic or refractory material containing [e.g., tungsten oxide, glass, cement, etc.] - C03C: CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS - C09C: TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES (treatment of materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone C04B14/00, C04B18/00, C04B20/00); PREPARATION OF CARBON BLACK {; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS} - C01P: INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract Prior art production of purple pigments based on colloidal gold on stovable/sinterable/fireable support material involves the reduction of a gold compound in the presence of a chemical reducing agent. Purple pigments may be produced more simply according to the invention by intimately mixing and/or grinding the support material and the gold compound in dry form or by bringing an aqueous solution or suspension of a gold compound and a support material into contact and then thermally treating the mixture at a temperature above the decomposition temperature of the gold compound and below the sintering temperature of the support material, wherein the gold compound is converted into colloidal gold. ## Claims ### Claim 1 A process for the production of a purple pigment based on a fireable support material selected from the group consisting of a glass flux, other oxide or silicate material and mixtures thereof coated with colloidal gold, comprising bringing a finely powdered support material into intimate contact with at least one gold compound, wherein the weight ratio of support materials to gold in the gold compounds is between 10:1 and 2000:1, characterized in that (i.sub.1) the support material and the gold compound or compounds are intimately mixed and/or ground in dry form or (i.sub.2) the support material is brought into contact with an aqueous solution or suspension of the gold compound or compounds in the absence of a reducing agent and without adding a precipitation agent for converting the water-soluble gold compound or compounds to water-insoluble compounds and (ii) the resultant mixture is thermally treated at a temperature above the decomposition temperature of the gold compound or compounds and below the sintering temperature of the support material until the gold compound or compounds are converted into colloidal gold. ### Claim 2 (depends on 1) A process according to claim 1 wherein a glass flux is used as the support material. ### Claim 3 (depends on 2) A process according to claim 2 wherein the glass flux is a glass frit having an average particle diameter in the range of from 0.5 .mu.m to 50 .mu.m. ### Claim 4 (depends on 1) A process according to claim 1, wherein at least one gold compound selected from the group consisting of Li, Na and K dicyanoaurate (I), gold cyanide, tetrahalogenoauric acid, Li, Na and K disulphitoaurate(I), gold sulphide, gold(I) thiolates, gold(I) amine complexes and gold oxide are used. ### Claim 5 (depends on 4) A process according to claim 4, wherein HAuCl.sub.4 or a hydrate thereof is used. ### Claim 6 (depends on 1) A process according to claim 1, wherein the support material and the gold compound or compounds are brought into contact in a quantity such that the weight ratio of support material to gold is between 10:1 and 200:1. ### Claim 7 (depends on 1) A process according to claim 1, wherein the thermal treatment is performed in the range of between 150.degree. C. and less than 300.degree. C. ### Claim 8 (depends on 1) A process according to claim 1, wherein a water-soluble gold compound is dissolved in water the solution is brought into contact with the support material and the product, from which excess solution solution has been removed, is thermally treated. ### Claim 9 (depends on 1) A process according to claim 1, wherein, for the purpose of hue modification, the support material is additionally brought into contact with an effective quantity of at least one compound of Ag, Cu, Co, Ni, Sn, Ru, Rh, Pd, Os, Ir or Pt in solid or dissolved form before, during or after said support material is brought into contact with said at least one gold compound, before and/or after thermal treatment, whereby the compounds acting to modify hue are deposited on the surface of the support material. ### Claim 10 (depends on 1) A process according to claim 1 wherein a support material consisting of at least one glass frit and, optionally, up to 10 wt. % of hue-modifying oxides selected from the group consisting of TiO.sub.2, CeO.sub.2, SnO.sub.2 and SiO.sub.2, at least one solid gold compound and, optionally, an additional hue-modifying compound from the series of compounds of Ag, Cu, Co, Ni, Rh, Ru, Pd, Os, Ir and Pt, are ground together when dry and the mixture is thermally treated at a temperature in the range from 150.degree. C. to a temperature below the softening point of the glass frit.