# US 5,705,970 A · Rare-earth containing iron-base resin bonded magnets > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,705,970 A - Document ID: US5705970A - Status: Granted - Kind: A - Application number: 08/386,761 - Filed: 1995-02-10 - Granted: 1998-01-06 - Earliest claimed: 1993-10-15 - Assignees: Kabushiki Kaisha Sankyo Seiki Seisakusho - Inventors: Shigeru Nishida; Takafumi Kuwazawa; Tetsuo Hoshina - Web page: https://patentgrep.com/patent/US5705970A ## CPC - H02K 1/02: characterised by the magnetic material - H01F 1/0558: {bonded together} - H02K 15/03: having permanent magnets - H02K 37/14: with magnets rotating within the armatures - H02K: DYNAMO-ELECTRIC MACHINES (dynamo-electric relays H01H53/00; conversion of DC or AC input power into surge output power {H03K3/53}) - H01F: MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES ## Abstract A motor having rotor has a good balance of inertia and a magnetic characteristic that match the specifications of the motor with which those rotors are to be used. A rare-earth containing iron-base resin-bonded magnet is molded from an iron-base magnetic powder containing a rare earth metal such as neodymium and praseodymium in powder, a thermoplastic or thermosetting resin and additive. A density and magnetic characteristic is proportionally changed by adjusting a mixing ratio of a filler powder. Specifically, when a mixing ratio of filler powder containing tungsten having a density 19.1 g/cm.sup.3 is in 13 vol % is injected, or a mixing ratio of alloy powder containing tungsten an nickel, or tungsten and chromium having a density 10.5 g/cm.sup.3 is compression-mold, its magnetic flux assume the same value as those of compression-molded Sm--Co magnets. ## Claims ### Claim 1 A method for manufacturing a rare-earth containing iron-base resin-bonded magnet, comprising the step of: preparing a first mix of an iron-base magnetic powder that contains a rare earth metal selected from the group consisting of neodymium and praseodymium with a filler powder; preparing a second mix of a resin including one of thermoplastic resin and thermosetting resin and an additive; and forming a predetermined shape by molding said first and second mixes, wherein the filler powder contains at least one element selected from the group consisting of tungsten, nickel, cobalt, copper, iron, chromium, silicon, carbon manganese, molybdenum, titanium, zinc, lead, tin, and aluminum. ### Claim 2 (depends on 1) A method for manufacturing a rare-earth containing iron-base resin-bonded magnet according to claim 1 wherein the rare-earth containing iron base resin-bonded magnet is formed by injection molding. ### Claim 3 (depends on 1) A method for manufacturing a rare-earth containing iron-base resin-bonded magnet according to claim 1 wherein the rare-earth containing iron-base resin-bonded magnet is formed by compression molding. ### Claim 4 (depends on 1) A method for manufacturing a rare-earth containing iron-base resin-bonded magnet according to claim 1 wherein the rare-earth containing iron-base resin-bonded magnet is formed by extrusion molding. ### Claim 5 A rare-earth containing iron-base resin-bonded magnet consisting essentially of: an iron-base magnetic powder that contains a rare earth metal selected from the group consisting of neodymium and praseodymium; a filler powder; a resin including one of thermoplastic resin and thermosetting resin; and an additive, wherein the filler powder contains at least one element selected from the group consisting of tungsten, nickel, cobalt, copper, iron, chromium, silicon, carbon manganese, molybdenum, titanium, zinc, lead, tin, and aluminum. ### Claim 6 (depends on 5) A rare-earth containing iron-base resin-bonded magnet as claimed in claim 5, wherein the magnet has inertia and magnetic characteristics are determined by the relative amounts of the iron-based magnetic powder and said filler powder. ### Claim 7 A method for manufacturing a rare-earth containing iron-base resin-bonded magnet, comprising the steps of: mixing an iron-base magnetic powder that contains a rare earth metal selected from the group consisting of neodymium and praseodymium with one of thermoplastic resin and thermosetting resin, and an additive; mixing a filler powder with a resin including one of thermoplastic resin and thermosetting resin and an additive; and forming a predetermine shape by molding, wherein the filler powder contains at least one element selected from the group consisting of tungsten, nickel, cobalt, copper, iron, chromium, silicon, carbon manganese, molybdenum, titanium, zinc, lead, tin, and aluminum. ### Claim 8 (depends on 7) A method for manufacturing a rare-earth containing iron-base resin-bonded magnet according to claim 7 wherein the rare-earth containing iron-base resin-bonded magnet is formed by injection molding. ### Claim 9 (depends on 7) A method for manufacturing a rare-earth containing iron-base resin-bonded magnet according to claim 7 wherein the rare-earth conbtaining iron-base resin-bonded magnet is formed by compression molding. ### Claim 10 (depends on 7) A method for manufacturing a rare-earth containing iron-base resin-bonded magnet according to claim 7 wherein the rare-earth containing iron-base resin-bonded magnet is formed by extrusion molding. ### Claim 11 A rare earth-iron resin-bonded magnet comprising: magnetic powder of the iron family containing rare earths; tungsten alloy filler powder having a specific gravity greater than that of the magnetic powder of the ion family; thermosetting resin; and an additive, wherein the rare earth-iron resin-bonded magnet is formed by compression-molding the mixture. ### Claim 12 (depends on 11) A rare earth-iron resin-bonded magnet as claimed in claim 11, wherein the resin constitutes within 1.about.3 wt %, the filler constitutes within 20.about.50 w % and magnetic powder constitutes a remaing part in a weight ratio and, wherein the filler has a means grain size of not less than 30 .mu.m. ### Claim 13 (depends on 11, 12) A rare earth-iron resin-bonded magnet as claimed in one of the claims 11 and 12, wherein the filler is an alloy of W and at least one element selected from among Ni, Co and Fe and W and is within 25.about.45 w % in a weight ratio. ### Claim 14 (depends on 11, 12, 13) A rare earth-iron resin-bonded magnet as claimed in any one of the claims 11 to 13, wherein the filler is an alloy of W and Ni, and constitutes 36 wt %, and the filler constitutes 36 wt % in a weight ratio, and wherein a rust preventive resin coating is applied to at least one of the inner and outer periphery of the magnet. ### Claim 15 (depends on 11, 12, 13, 14) A rare earth-iron resin-bonded magnet as claimed in any one of the claims 11 to 14, wherein the filler is an alloy of W and Ni, and constitutes 45 wt %, and the filler constitutes 31 wt % in a weight ratio, and wherein a rust preventive resin coating is applied to at least one of the inner and outer periphery of the magnet. ### Claim 16 A bonded magnet comprising: a synthetic resin binder; a magnetic powder containing rare earth metal, iron and boron; and a mixture of Ni-W alloy mixed powder with at least one element selected from among Cr, Mo, Zn and Al. ### Claim 17 (depends on 16) A bonded magnet as claimed in claim 16, wherein the Ni-W alloy powder contains within 64.about.70 wt % Ni, W within 36.about.30 wt % W, and at least one element Cr, Mn, Zn and Al whose loadings range from 1 to 10 wt %. ### Claim 18 A corrosion resistant bonded magnet comprising: a synthetic resin binder; a magnetic powder containing rare earth metal, iron and boron; and a mixture of Ni-W alloy mixed powder with an additive consisting one element selected from the group consisting of Cr, Mn, Zn, and Al, whereby an electrode potential difference between the magnetic powder and the mixture of Ni-W with the additive is reduced.