# US 5,703,002 A · Photocatalyst particles containing ferromagnetic metal particles and method for synthesis thereof > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,703,002 A - Document ID: US5703002A - Status: Granted - Kind: A - Application number: 08/703,550 - Filed: 1996-08-27 - Granted: 1997-12-30 - Earliest claimed: 1995-08-30 - Assignees: Agency of Industrial Science & Technology, Ministry of International Trade & Industry - Inventors: Atsuya Towata; Mutsuo Sando - Web page: https://patentgrep.com/patent/US5703002A ## CPC - B01J 35/39: Photocatalytic properties - B01J 35/70: characterised by their crystalline properties, e.g. semi-crystalline (catalysts comprising carbon B01J21/18; molecular sieves B01J29/00) - B01J 2235/00: Indexing scheme associated with group B01J35/00, related to the analysis techniques used to determine the catalysts form or properties - B01J 2235/15: X-ray diffraction - B01J: CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS ## Abstract Photocatalyst particles consist essentially of a matrix consisting of the crystal phase of a semiconducting metal oxide as a photocatalyst and ferromagnetic metal particles dispersed in the matrix, having an average particle diameter of 15 nm at most and a specific surface area of 100 m.sup.2 /g at least, and permitting recovery by a magnetic force. A method for the production of the photocatalyst particles consists essentially of dispersing water in a hydrophobic organic solvent containing a surfactant thereby forming a microemulsion, adding to the microemulsion a raw material for the formation of the crystal phase of a semiconducting metal oxide as a photocatalyst and a raw material for the formation of ferromagnetic metal particles, causing the raw materials contained in the mixture resulting from the preceding step to undergo hydrolysis and inducing precipitation of the hydroxide and oxide thereof in the resultant mixture, separating the precipitates from the resultant mixture, and heat-treating the separated precipitates under a reducing condition. ## Claims ### Claim 1 Photocatalyst particles consisting essentially of a matrix consisting of a crystal phase of a semiconducting metal oxide and ferromagnetic metal particles dispersed in said matrix, wherein said photocatalytic particles have an average particle size of 15 nm at most and a specific surface area of at least 100 m.sup.2 /g. ### Claim 2 (depends on 1) The photocatalyst particles according to claim 1, wherein said semiconducting metal oxide is at least one member selected from the group consisting of titania and zinc oxide. ### Claim 3 (depends on 1) The photocatalyst particles according to claim 1, wherein said ferromagnetic metal particles are formed of at least one member selected from the group consisting of nickel, cobalt, and iron. ### Claim 4 (depends on 1) The photocatalyst particles according to claim 1, wherein said ferromagnetic metal particles comprise 2 to 20% by weight of said photocatalyst particles. ### Claim 5 (depends on 1) A method for the production of photocatalyst particles according to claim 1, which consists essentially of dispersing water in a hydrophobic organic solvent containing a surfactant thereby forming a microemulsion, adding to said microemulsion a raw material for the formation of the crystal phase of a semiconducting metal oxide as a photocatalyst and a raw material for the formation of ferromagnetic metal particles, causing said raw materials contained in the mixture resulting from the preceding step to undergo hydrolysis and inducing precipitation of the hydroxide and oxide thereof in said resultant mixture, separating said precipitates from said resultant mixture, and heat-treating the separated precipitates under a reducing condition. ### Claim 6 (depends on 5) The method according to claim 5, wherein said hydrophobic organic solvent is at least one member selected from the group consisting of hexane, toluene, benzene, and xylene. ### Claim 7 (depends on 5) The method according to claim 5, wherein said surfactant is at least one member selected from the group consisting of anionic surfactant, cationic surfactant, nonionic surfactant, and amphoteric surfactant. ### Claim 8 (depends on 7) The method according to claim 7, wherein said surfactant is a nonionic surfactant and has an HLB in the range of 3.5 to 6. ### Claim 9 (depends on 7) The method according to claim 7, wherein the content of said surfactant in said hydrophobic organic solvent is in the range of 1.0.times.10.sup.-5 to 1.0.times.10.sup.-3 mol/L. ### Claim 10 (depends on 5) The method according to claim 5, wherein the amount of water dispersed in said microemulsion is in the range of 9 to 11 g/liter of said microemulsion. ### Claim 11 (depends on 5) The method according to claim 5, wherein the raw material for the formation of said semiconducting metal oxide is the metal alkoxide or metal halogenide of at least one member selected from the group consisting of titania and zinc oxide. ### Claim 12 (depends on 5) The method according to claim 5, wherein the raw material for the formation of said ferromagnetic metal particles is a metal alkoxide or halogenide of at least one member selected from the group consisting of nickel, cobalt, and iron. ### Claim 13 (depends on 5) The method according to claim 5, wherein said heat treatment under a reducing condition is carried out at a temperature in the range of 250.degree. to 400.degree. C. ### Claim 14 (depends on 5) The method according to claim 5, wherein the sum of the amounts of the raw material for the semiconducting metal oxide crystals and the raw material for the ferromagnetic metal-containing particles to be added to the microemulsion is such that said ferromagnetic metal particles account for 2 to 20% by weight, based on the amount of said photocatalyst particles.