# US 5,702,991 A · Interpenetrating network compositions and structures > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,702,991 A - Document ID: US5702991A - Status: Granted - Kind: A - Application number: 08/661,338 - Filed: 1996-06-12 - Granted: 1997-12-30 - Earliest claimed: 1992-01-23 - Inventors: Richard L. Jacobs - Web page: https://patentgrep.com/patent/US5702991A ## CPC - C08J 3/243: {Two or more independent types of crosslinking for one or more polymers} - C08J 5/247: {using fibres of at least two types} - H05K 1/0353: {consisting of two or more materials, e.g. two or more polymers, polymer + filler, + reinforcement} - Y10T 442/2107: At least one coating or impregnation contains particulate material - Y10T 442/2123: At least one coating or impregnation contains particulate material - Y10T 442/2213: Coating or impregnation is specified as weather proof, water vapor resistant, or moisture resistant - Y10T 442/2631: Coating or impregnation provides heat or fire protection - Y10T 442/273: Coating or impregnation provides wear or abrasion resistance - Y10T 442/2738: Coating or impregnation intended to function as an adhesive to solid surfaces subsequently associated therewith - Y10T 442/2992: Coated or impregnated glass fiber fabric - Y10T 442/3472: Woven fabric including an additional woven fabric layer - C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29) - H05K: PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract Structure, composition and method in which a fiber reinforcement is impregnated with an interpenetrating network of a light cure resin and a thermosetting resin which are independently curable, enabling autobody component repair, electronic assembly bonding, etc. by selective cure first of one or the other resin, and the support against fluid flow of the uncured resin by the first cured resin. ## Claims ### Claim 1 Composition for interpenetrating network comprising a first reagent and a second reagent, said first reagent comprising a light curable resin of an ethylenically reactive vinyl-, or allyl-moiety containing monomer mixed with urethane polymer formers comprising diphenyl methane diisocyanate or dicyclohexane diisocyanate; said second reagent comprising a light curable resin of an ethylenically reactive vinyl-, or allyl-moiety containing monomer, oligomer or polymer and a polyol forming a urethane polymer with said diisocyanates; in combination with a filler for said composition in at least one of said first and second reagents, said composition and said filler being further combined with fiber reinforcement and a catalyst for the light cure of said light curable resin under conditions under which said light curable resins are not reactive and remain flowable and said urethane polymer forming diisocyanates are reactive with said polyol to form urethane polymer which is sufficiently cured to be nonflowable and to retain said light curable resins in place against flowing from said reinforcing fiber. ### Claim 2 (depends on 1) Combination according to claim 1, in which said filler is light transmitting sufficiently to permit curable of said light curable resins. ### Claim 3 (depends on 1) Combination according to claim 1, in which said light curable resins and said urethane polymer reaction product of said diisocyanates and polyol are each present in amounts from 5 to 95 parts by weight per 100 parts by weight of said composition. ### Claim 4 (depends on 3) Combination according to claim 3, in which said filler is particulate and is present in an amount from 5 to 500 parts by weight of filler per 100 parts by weight of said composition. ### Claim 5 (depends on 3) Combination according to claim 3, in which said reinforcing fiber is present in an amount from 10 to 500 parts by weight per 100 parts by weight of said composition. ### Claim 6 (depends on 5) Combination according to claim 5, which said filler is particulate and is present in an amount from 5 to 500 parts by weight of filler per 100 parts by weight of said composition. ### Claim 7 (depends on 3) Combination according to claim 3, in which said light curable resins and urethane polymer are each reinforced said reinforcing fiber, said combination being flexibly formable until said light curable resin is cured. ### Claim 8 (depends on 1) Combination according to claim 1, in which said fiber reinforcement comprises fibers of glass, carbon, metal, synthetic organic polymer, cellulosic or protein material. ### Claim 9 (depends on 8) Combination according to claim 8, in which said light curable resin comprises repeating units of allyl and/or allyl alcohol ester moieties. ### Claim 10 (depends on 1) Combination according to claim 1, in which each said light curable resin comprises repeating units of acrylic or acrylate, fumarate, maleate, unsaturated polyester resin, vinyl pyrollidone, vinyl pyridine, and/or butadiene moieties. ### Claim 11 (depends on 1) Combination according to claim 1, in which said filler comprises talc or silica. ### Claim 12 (depends on 1) Combination according to claim 1, in which said fiber reinforcement comprises fibers of glass, metal, synthetic organic polymer, cellulosic or protein material arranged in a web. ### Claim 13 (depends on 12) Combination according to claim 12, in which said fiber reinforcement comprises fiberglass web. ### Claim 14 (depends on 13) Combination according to claim 13, in which said filler comprises talc or silica. ### Claim 15 (depends on 14) Combination according to claim 14, in which said fiber reinforcement comprises a fiberglass web. ### Claim 16 (depends on 1) Combination according to claim 1, light cure catalyst comprises a titanocene. ### Claim 17 (depends on 1) Combination according to claim 1, in which said light cure catalyst comprises Bis(N5-2,4-cyclopentadien-1-yl), Bis(2,6-difluoro-3-(1H-pyrrol-1-yl)phenyl)titanium.