# US 5,700,596 A · Nickel hydroxide active material powder and nickel positive electrode and alkali storage battery using them > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,700,596 A - Document ID: US5700596A - Status: Granted - Kind: A - Application number: 07/795,845 - Filed: 1991-11-21 - Granted: 1997-12-23 - Earliest claimed: 1991-07-08 - Assignees: Matsushita Electric Industrial Co., Ltd. - Inventors: Munehisa Ikoma; Norikatsu Akutsu; Masashi Enokido; Fumihiko Yoshii; Hideo Kaiya; Shingo Tsuda - Web page: https://patentgrep.com/patent/US5700596A ## CPC - H01M 4/52: of nickel, cobalt or iron - H01M 4/32: Nickel oxide or hydroxide electrodes - H01M 10/345: {Gastight metal hydride accumulators} - Y02E 60/10: Energy storage using batteries - H01M: PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY - Y02E: REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION ## Abstract The tap density of nickel hydroxide powders is improved, the expansion of a positive electrode is inhibited and the energy density of the positive electrode and the cycle life characteristics are improved by specifying the shape of the nickel hydroxide powders and besides, adding to the nickel hydroxide powders at least one of Cd, Ca, Zn, Mg, Fe, Co and Mn. The nickel hydroxide active material powders contain 1-7 wt % of at least one of Cd, Ca, Zn, Mg, Fe, Co and Mn and comprise a mixture of spherical or nearly spherical particles and non-spherical particles. ## Claims ### Claim 1 A nickel hydroxide active material powder for use in making nickel positive electrodes, which is a mixture of spherical or nearly spherical particles having a particle size of about 10-30 .mu.m and non-spherical particles having a particle size of less than about 10 .mu.m which comprises a nickel hydroxide powder containing 1-7 wt % of at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese before production of positive electrodes and is an aggregate of innumerable primary particles of 0.1 .mu.m or less. ### Claim 2 (depends on 1) A nickel hydroxide active material powder according to claim 1, which is an aggregate of innumerable primary particles of 0.1 .mu.m or less. ### Claim 3 (depends on 1) A nickel hydroxide active material powder according to claim 1, wherein at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese is present as a solid solution inside the crystal of the nickel hydroxide active material powder. ### Claim 4 (depends on 1) A nickel hydroxide active material powder according to claim 1, which contains 3-7 wt % of zinc and 0.1-1 wt % of cobalt. ### Claim 5 (depends on 1) A nickel hydroxide active material powder according to claim 1, which has an average particle size of 7-20 .mu.m and a tap density of at least 1.9 g/cm.sup.3. ### Claim 6 (depends on 1) A nickel hydroxide active material powder according to claim 1, which has a BET specific surface area of 10-20 m.sup.2 /g measured by adsorption of nitrogen gas. ### Claim 7 (depends on 1) A nickel hydroxide active material powder according to claim 1, which has a void volume of 0.015-0.04 cm.sup.3 /g measured by adsorption of nitrogen gas. ### Claim 8 (depends on 1) A nickel hydroxide active material powder according to claim 1, which has a void volume having a pore radius of 30 .ANG. or more of at least 20% based on total void volume which is calculated from adsorption isotherm of adsorption side of nitrogen gas. ### Claim 9 (depends on 1) A nickel hydroxide active material powder according to claim 1, which is continuously obtained from sodium hydroxide and a mixed aqueous solution of nickel sulfate and a sulfate or nitrate of at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese by adjusting reaction pH to 11.3.+-.0.2 and reaction temperature to 30.degree.-40.degree. C. and by controlling the residence time and the stirring condition in a reaction tank. ### Claim 10 A nickel hydroxide active material for nickel positive electrodes which comprises a nickel hydroxide powder containing 1-7 wt % of at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese, is an aggregate of innumerable primary particles of 0.1 .mu.m or less, and has a void volume having a pore radius of 30 .ANG. or more of 20-70% based on total void volume. ### Claim 11 (depends on 10) A nickel hydroxide active material according to claim 10, wherein the nickel hydroxide active material powder is a mixture of spherical or nearly spherical particles and non-spherical particles. ### Claim 12 (depends on 10) A nickel hydroxide active material according to claim 10, wherein the nickel hydroxide active material powder has a BET specific surface area of 10-20 m.sup.2 /g measured by adsorption of nitrogen gas. ### Claim 13 (depends on 10) A nickel hydroxide active material according to claim 10, wherein the nickel hydroxide active material powder has an average particle size of 7-20 .mu.m and a tap density of at least 1.9 g/cm.sup.3. ### Claim 14 (depends on 10) A nickel hydroxide active material according to claim 10, wherein the nickel hydroxide active material powder has a void volume of 0.015-0.04 cm.sup.3 /g. ### Claim 15 (depends on 10) A nickel hydroxide active material according to claim 10, which is a powder obtained from an aqueous sodium hydroxide solution and a mixed aqueous solution of nickel sulfate, zinc sulfate and cobalt sulfate by adjusting the pH to 11.3.+-.0.2 in production of nickel hydroxide. ### Claim 16 A nickel positive electrode which comprises a three-dimensional porous body or a flat sheet which supports a nickel hydroxide active material mainly composed of nickel powder and which imparts electric conductivity wherein the nickel hydroxide active material comprises a mixture of spherical or nearly spherical particles having a particle size of about 10-30 .mu.m and non-spherical particles having a particle size of less than about 10 .mu.m which comprises a nickel hydroxide powder containing 1-7 wt % of at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese and a powder of at least one member selected from the group consisting of cobalt, cobalt oxide, zinc oxide, zinc, cadmium and cadmium oxide and is an aggregate of innumerable primary particles of 0.1 .mu.m or less. ### Claim 17 (depends on 16) A nickel positive electrode according to claim 16, wherein weight ratio of nickel hydroxide:cobalt:cobalt hydroxide:zinc oxide and/or cadmium oxide:cadmium and/or zinc is 100:4-18:0-10:0-10:0-10. ### Claim 18 (depends on 16) A nickel positive electrode according to claim 16, wherein the three-dimensional porous body is a sponge-like nickel porous body or a punching metal. ### Claim 19 (depends on 16) A nickel positive electrode according to claim 16, wherein the flat sheet is a nickel foil or a nickel-plated iron foil. ### Claim 20 (depends on 18) A nickel positive electrode according to claim 18, wherein the sponge-like nickel porous body has a density of 200-700 g/m.sup.2. ### Claim 21 (depends on 16) A nickel positive electrode according to claim 16, wherein the nickel hydroxide powder is an aggregate of innumerable primary particles of 0.1 .mu.m or less. ### Claim 22 (depends on 16) A nickel positive electrode according to claim 16, wherein at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese is present as a solid solution inside the crystal of the nickel hydroxide active material powder. ### Claim 23 (depends on 16) A nickel positive electrode according to claim 16, wherein the nickel hydroxide active material powder contains 3-7 wt % of zinc and 0.1-1 wt % of cobalt. ### Claim 24 (depends on 16) A nickel positive electrode according to claim 16, wherein the nickel hydroxide active material powder has an average particle size of 7-20 .mu.m and a tap density of at least 1.9 g/cm.sup.3. ### Claim 25 (depends on 16) A nickel positive electrode according to claim 16, wherein the nickel hydroxide powder has a BET specific surface area of 10-20 m.sup.2 /g measured by adsorption of nitrogen gas. ### Claim 26 (depends on 16) A nickel positive electrode according to claim 16, wherein the nickel hydroxide powder has a void volume of 0.015-0.04 cm.sup.3 /g measured by adsorption of nitrogen gas. ### Claim 27 (depends on 16) A nickel positive electrode according to claim 16, wherein the nickel hydroxide powder has a void volume having a pore radius of 30 .ANG. or more of at least 20% based on total void volume which is calculated from adsorption isotherm of adsorption side of nitrogen gas. ### Claim 28 (depends on 16) A nickel positive electrode according to claim 16, wherein he nickel hydroxide powder is obtained from sodium hydroxide and a mixed aqueous solution of nickel sulfate and a sulfate or a nitrate of at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese by controlling the reaction pH and reaction temperature. ### Claim 29 (depends on 16) A nickel positive electrode according to claim 16, wherein the reaction pH is 11.3.+-.0.2 and the reaction temperature is 30.degree.-40.degree. C. ### Claim 30 (depends on 16) A nickel positive electrode according to claim 16, which contains a powder having water repellency. ### Claim 31 An alkali storage battery comprising a nickel positive electrode mainly composed of nickel oxide, a negative electrode mainly composed of a hydrogen absorbing alloy capable of carrying out electrochemical hydrogen absorbing and desorbing reaction or a negative electrode mainly composed of cadmium oxide, an alkali electrolyte, a separator, a case containing these electricity generating elements and a sealing plate provided with a safety vent wherein before initial charging and discharging, said nickel positive electrode is mainly composed of a three dimensional porous body or a flat sheet which imparts electrical conductivity and supports nickel hydroxide powders comprising a mixture of spherical or nearly spherical particles having a particle size of about 10-30 .mu.m and non-spherical particles having a particle size of less than about 10 .mu.m which comprises nickel hydroxide powders containing 1-7 wt % of at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese and additionally containing a powder of at least one member selected from the group consisting of cobalt, cobalt oxide, zinc oxide, zinc, cadmium, and cadmium oxide and is an aggregate of innumerable primary particles of 0.1 .mu.m or less, the specific gravity of the alkali electrolyte is 1.23-1.4, and the amount of the electrolyte per 1 Ah of battery capacity is 1.0-2.0 cm.sup.3 /Ah. ### Claim 32 (depends on 31) An alkali storage battery according to claim 31, wherein weight ratio of nickel hydroxide:cobalt:cobalt hydroxide:zinc oxide and/or cadmium oxide:cadmium and/or zinc is 100:4-18:0-10:0-10:0-10. ### Claim 33 (depends on 31) An alkali storage battery according to claim 31, wherein the three-dimensional porous body is a sponge-like nickel porous body or a punching metal. ### Claim 34 (depends on 31) An alkali storage battery according to claim 31, wherein the flat sheet is a nickel foil or a nickel-plated iron foil. ### Claim 35 (depends on 31) An alkali-storage battery according to claim 31, wherein the sponge-like nickel porous body has a density of 200-700 g/m.sup.2. ### Claim 36 (depends on 31) An alkali storage battery according to claim 31, wherein the nickel positive electrode contains powders having water repellency. ### Claim 37 (depends on 31) An alkali storage battery according to claim 31, wherein the nickel hydroxide powder is an aggregate of innumerable primary particles of 0.1 .mu.m or less. ### Claim 38 (depends on 31) An alkali storage battery according to claim 31, wherein at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese is present as a solid solution inside the crystal of the nickel hydroxide active material powder. ### Claim 39 (depends on 31) An alkali storage battery according to claim 31, wherein the nickel hydroxide active material powder contains 3-7 wt % of zinc and 0.1-1 wt % of cobalt. ### Claim 40 (depends on 31) An alkali storage battery according to claim 31, wherein the nickel hydroxide active material powder has an average particle size of 7-20 .mu.m and a tap density of at least 1.9 g/cm.sup.3. ### Claim 41 (depends on 31) An alkali storage battery according to claim 31, wherein the nickel hydroxide powder has a BET specific surface area of 10-20 m.sup.2 /g measured by adsorption of nitrogen gas. ### Claim 42 (depends on 31) An alkali storage battery according to claim 31, wherein the nickel hydroxide powder has a void volume of pores of 0.015-0.04 cm.sup.3 /g measured by adsorption of nitrogen gas. ### Claim 43 (depends on 31) An alkali storage battery according to claim 31, wherein the nickel hydroxide powder has a void volume having a pore radius of 30 .ANG. or more of at least 20% based on total void volume which is calculated from adsorption isotherm of adsorption side of nitrogen gas. ### Claim 44 (depends on 31) An alkali storage battery according to claim 31, wherein the nickel hydroxide active material is obtained from sodium hydroxide and a mixed aqueous solution of nickel sulfate and a sulfate or a nitrate of at least one metal selected from the group consisting of cadmium, calcium, zinc, magnesium, iron, cobalt and manganese by controlling reaction pH and reaction temperature. ### Claim 45 (depends on 44) An alkali storage battery according to claim 44, wherein the reaction pH is 11.3.+-.0.2 and the reaction temperature is 30-40.degree. C. ### Claim 46 (depends on 31) An alkali storage battery according to claim 31, wherein the electrolyte comprises at least one compound selected from the group consisting of potassium hydroxide and sodium hydroxide and lithium hydroxide. ### Claim 47 (depends on 46) An alkali storage battery according to claim 46, wherein the electrolyte contains lithium hydroxide (LiOH) in an amount of at least 10 g/l. ### Claim 48 (depends on 31) An alkali storage battery according to claim 31, wherein zincate ion is present in the alkali electrolyte. ### Claim 49 (depends on 31) An alkali storage battery according to claim 31, wherein the separator is a nonwoven fabric subjected to sulfonation treatment. ### Claim 50 (depends on 31) An alkali storage battery according to claim 31, wherein actuating pressure of the safety vent provided at the sealing plate is 5-30 kg/cm.sup.3.