# US 5,700,516 A · Repulpable hot melt polymer/wax compositions for fibrous products > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,700,516 A - Document ID: US5700516A - Status: Granted - Kind: A - Application number: 08/733,534 - Filed: 1996-10-18 - Granted: 1997-12-23 - Earliest claimed: 1993-07-22 - Assignees: S. C. Johnson Commerical Markets, Inc. - Inventors: Paul E. Sandvick; Calvin J. Verbrugge - Web page: https://patentgrep.com/patent/US5700516A ## CPC - D21H 21/16: Sizing or water-repelling agents - C08L 91/06: Waxes - D21H 19/14: applied in a form other than the aqueous solution defined in group D21H19/12 - D21H 19/18: comprising waxes - D21H 19/20: comprising macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds - D21H: PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR - C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06) ## Abstract Hot melt wax compositions are described that render fibrous products such as paper, paperboard and corrugated paper containers water-resistant at room temperature, but enable such articles to be repulped and recycled when the coated articles are repulped in a heated nearly neutral to alkaline aqueous medium. The compositions comprise from about 20% to 97.5% by weight of a water-repellent wax that is a solid at 20.degree. C.; from about 2.5% to 50% by weight of an addition polymer of from about 50 to 95 mole percent of an ethylene-1,2-dicarboxylic acid or anhydride and from about 5 to 50 mole percent of at least one additional ethylenically unsaturated monomer selected from the group consisting of 1-alkenes having from about 4 to 60 carbon atoms wherein the polymer is dispersible in the water-repellent wax; optionally from about 1 to 90 mole percent of the carboxyl groups in the polymer may be further modified by reaction with a substituted or unsubstituted monoalcohol or monoamine; and optionally, from about 5% to 75% by weight of at least one fatty acid selected from the group consisting of fatty acids containing from about 12 to 48 carbon atoms. The compositions are solid at 20.degree. C., but start to become fluid between about 50.degree. C. to 95.degree. C. ## Claims ### Claim 1 A method of rendering fibrous articles water-resistant that comprises the steps of heating a hot melt polymer/wax composition that is dispersible in a heated nearly neutral to alkaline aqueous pH medium comprising A. from about 20% to 97.5% by weight based upon the total weight of the composition of a water-repellent wax that is a solid at 20.degree. C.; B. from about 2.5% to 50% by weight based upon the total weight of the composition of at least one addition polymer selected from the group consisting of (i) a polymer of from about 5 to 95 mole percent of at least one ethylenically unsaturated monocarboxylic acid monomer containing a free carboxyl group and from about 5 to 95 mole percent of at least one additional ethylenically unsaturated monomer, (ii) a polymer of from about 50 to 95 mole percent of at least one ethylenically-unsaturated dicarboxylic acid monomer selected from the group consisting of an ethylene-1,2-dicarboxylic acid containing two free carboxyl groups and an ethylene-1,2-dicarboxylic acid anhydride having two carboxyl groups in the form of an anhydride group, and from about 5 to 50 mole percent of at least one additional ethylenically unsaturated monomer, and (iii) a polymer of a total of from about 5 to 95 mole percent of (a) at least one of the ethylenically unsaturated monocarboxylic acid monomers and (b) at least one of the ethylenically-unsaturated dicarboxylic monomers and from about 5 to 95 mole percent of at least one additional ethylenically unsaturated monomer, wherein the additional ethylenically unsaturated monomer is selected from the group consisting of 1-alkenes having from about 4 to 60 carbon atoms; alkyl vinyl ethers having an ether alkyl group of from about 8 to 60 carbon atoms, and alkyl acrylates or alkyl methacrylates having an alkyl group of from about 8 to 60 carbon atoms, wherein the polymer is compatible with the water-repellent wax; and C. optionally, up to about 77.5% by weight based upon the total weight of the composition of at least one fatty acid selected from the group consisting of natural or synthetic fatty acids containing from about 12 to 48 carbon atoms, wherein the fatty acid is compatible with the polymer and wax, the total amount of wax, polymer and fatty acid comprising 100% of the total composition and the polymer is at least 2.5% by weight of the total composition, wherein the composition is a solid at 20.degree. C., but starts to become fluid between about 50.degree. C. and 95.degree. C., until it becomes fluid, applying to a fibrous article an amount of the fluid heated composition that is effective to render it water-resistant, and allowing the composition to cool to room temperature to form a coated fibrous article having a solid coating that is removable upon exposure of the coated fibrous article to a heated nearly neutral to alkaline pH medium. ### Claim 2 (depends on 1) The method of claim 1 wherein the fibrous article of paper is a sheet of paper. ### Claim 3 (depends on 1) The method of claim 1 wherein the fibrous article of paper is a paperboard article. ### Claim 4 (depends on 1) The method of claim 1 wherein the fibrous article is a corrugated paper article. ### Claim 5 A method of rendering fibrous articles water-resistant that comprises the steps of heating a hot melt polymer/wax composition that is dispersible in a heated nearly neutral to alkaline aqueous pH medium comprising A. from about 20% to 97.5% by weight based upon the total weight of the composition of a water-repellent wax that is a solid at 20.degree. C.; B. from about 2.5% to 50% by weight based upon the total weight of the composition of at least one addition polymer of from about 50 to 95 mole percent of at least one ethylenically-unsaturated dicarboxylic acid monomer selected from the group consisting of an ethylene-1,2-dicarboxylic acid containing two free carboxyl groups and an ethylene-1,2-dicarboxylic acid anhydride having two carboxyl groups in the form of an anhydride group, and from about 5 to 50 mole percent of at least one additional ethylenically unsaturated monomer selected from the group consisting of 1-alkenes having from about 4 to 60 carbon atoms, and C. optionally, up to about 77.5% by weight based upon the total weight of the composition of at least one fatty acid selected from the group consisting of natural or synthetic fatty acids containing from about 12 to 48 carbon atoms, wherein the fatty acid is compatible with the polymer and wax, the total amount of wax, polymer and fatty acid comprising 100% of the total composition and the polymer is at least 2.5% by weight of the total composition, wherein the composition is a solid at 20.degree. C., but starts to become fluid between about 50.degree. C. and 95.degree. C. until it becomes fluid, applying to a fibrous article an amount of the fluid heated composition that is effective to render it water-resistant, and allowing the composition to cool to room temperature to form a coated fibrous article having a solid coating that is removable upon exposure of the coated fibrous article to a heated nearly neutral to alkaline pH medium. ### Claim 6 (depends on 5) The method of claim 5 wherein the fibrous article is a sheet of paper. ### Claim 7 (depends on 5) The method of claim 5 wherein the fibrous article is a paperboard article. ### Claim 8 (depends on 5) The method of claim 5 wherein the fibrous article is a corrugated paper article. ### Claim 9 A method of rendering fibrous articles water-resistant that comprises the steps of heating a hot melt polymer/fatty acid composition that is dispersible in a heated nearly neutral to alkaline aqueous pH medium comprising A. from about 10% to 90% by weight based upon the total weight of the composition of paraffin wax; B. from about 5% to 30% by weight based upon the total weight of the composition of at least one addition polymer of from about 50 to 95 mole percent of maleic anhydride and from about 5 to 50 mole percent of at least one additional ethylenically unsaturated monomer selected from the group consisting of 1-alkenes having from about 10 to 28 carbon atoms, and C. from about 5% to 60% by weight based upon the total weight of the composition of stearic acid, the total amount of wax, polymer and stearic acid comprising 100% of the total composition and the polymer is at least 2.5% by weight of the total composition, wherein the composition is a solid at 20.degree. C. but starts to become fluid between about 50.degree. C. and 95.degree. C., until it becomes fluid, applying to a fibrous article an amount of the fluid heated composition that is effective to render it water-resistant, and allowing the composition to cool to room temperature to form a coated fibrous article having a solid coating that is removable upon exposure of the coated fibrous article to a heated nearly neutral to alkaline pH medium. ### Claim 10 (depends on 9) The method of claim 9 wherein the fibrous article is a sheet of paper. ### Claim 11 (depends on 9) The method of claim 9 wherein the fibrous article is a paperboard article. ### Claim 12 (depends on 9) The method of claim 9 wherein the fibrous article is a corrugated paper article. ### Claim 13 A method of rendering fibrous articles water-resistant that comprises the steps of heating a hot melt polymer/fatty acid composition that is dispersible in a heated nearly neutral to alkaline aqueous pH medium comprising A. from about 10% to 90% by weight based upon the total weight of the composition of paraffin wax; B. from about 5% to 30% by weight based upon the total weight of the composition of at least one addition polymer of from about 50 to 95 mole percent of maleic anhydride and from about 5 to 50 mole percent of at least one additional ethylenically unsaturated monomer selected from the group consisting of 1-alkenes having from about 10 to 28 carbon atoms, and C. from about 5% to 60% by weight based upon the total weight of the composition of stearic acid, the total amount of wax, polymer and stearic acid comprising 100% of the total composition and the polymer is at least 2.5% by weight of the total composition, wherein the composition is a solid at 20.degree. C., but starts to become fluid between about 50.degree. C. and 95.degree. C. and wherein from about 5 to about 30 mole percent of anhydride groups present in the polymer are reacted with taurine, until it becomes fluid, applying to a fibrous article an amount of the fluid heated composition that is effective to render it water-resistant, and allowing the composition to cool to room temperature to form a coated fibrous article having a solid coating that is removable upon exposure of the coated fibrous article to a heated nearly neutral to alkaline pH medium. ### Claim 14 (depends on 13) The method of claim 13 wherein the fibrous article is a sheet of paper. ### Claim 15 (depends on 13) The method of claim 13 wherein the fibrous article is a paperboard article. ### Claim 16 (depends on 13) The method of claim 13 wherein the fibrous article is a corrugated paper article. ### Claim 17 A method of rendering fibrous articles water-resistant that comprises the steps of heating a hot melt polymer/wax composition that is dispersible in a heated nearly neutral to alkaline aqueous pH medium comprising A. from about 20% to 97.5% by weight based upon the total weight of the composition of a water-repellent wax that is a solid at 20.degree. C.; B. from about 2.5% to 50% by weight based upon the total weight of the composition of at least one addition polymer selected from the group consisting of (i) a polymer of from about 5 to 95 mole percent of at least one ethylenically unsaturated monocarboxylic acid monomer containing a free carboxyl group and from about 5 to 95 mole percent of at least one additional ethylenically unsaturated monomer, (ii) a polymer of from about 50 to 95 mole percent of at least one ethylenically-unsaturated dicarboxylic acid monomer selected from the group consisting of an ethylene-1,2-dicarboxylic acid containing two free carboxyl groups and an ethylene-1,2-dicarboxylic acid anhydride having two carboxyl groups in the form of an anhydride group, and from about 5 to 50 mole percent of at least one additional ethylenically unsaturated monomer, and (iii) a polymer of a total of from about 5 to 95 mole percent of (a) at least one of the ethylenically unsaturated monocarboxylic acid monomers and (b) at least one of the ethylenically-unsaturated dicarboxylic monomers and from about 5 to 95 mole percent of at least one additional ethylenically unsaturated monomer, wherein the additional ethylenically unsaturated monomer is selected from the group consisting of 1-alkenes having from about 4 to 60 carbon atoms; alkyl vinyl ethers having an ether alkyl group of from about 8 to 60 carbon atoms, and alkyl acrylates or alkyl methacrylates having an alkyl group of from about 8 to 60 carbon atoms, wherein the polymer is compatible with the water-repellent wax; and C. optionally, up to about 77.5% by weight based upon the total weight of the composition of at least one fatty acid selected from the group consisting of natural or synthetic fatty acids containing from about 12 to 48 carbon atoms, wherein the fatty acid is compatible with the polymer and wax, the total amount of wax, polymer and fatty acid comprising 100% of the total composition and the polymer is at least 2.5% by weight of the total composition, wherein the composition is a solid at 20.degree. C., but starts to become fluid between about 50.degree. C. and 95.degree. C., until it becomes fluid, impregnating a fibrous article with an amount of the fluid heated composition that is effective to render it water-resistant, and allowing the composition to cool to room temperature to form an impregnated fibrous article having a binder of the composition that is removable upon exposure of the impregnated fibrous article to a heated nearly neutral to alkaline pH medium. ### Claim 18 (depends on 17) The method as claimed in claim 17 wherein the polymer is at least one addition polymer of from about 50 to 95 mole percent of at least one ethylenically-unsaturated dicarboxylic acid monomer selected from the group consisting of an ethylene-1,2-dicarboxylic acid containing two free carboxyl groups and an ethylene-1,2-dicarboxylic acid anydride having two carboxyl groups in the form of an anhydride group, and from about 5 to 50 mole percent of at least one additional ethylenically unsaturated monomer selected from the group consisting of 1-alkenes having from about 4 to 60 carbon atoms. ### Claim 19 (depends on 18) The method as claimed in claim 18 wherein the composition comprises from about 5% to 30% of the polymer, from about 5% to 60% of the fatty acid and the balance comprising the wax wherein the polymer is a polymer of maleic anhydride and at least one unsaturated monomer selected from the group consisting of 1-alkenes having from about 10 to 28 carbon atoms, the wax is paraffin wax, and the fatty acid is stearic acid. ### Claim 20 (depends on 17) The method as claimed in claim 17 wherein from about 1 mole percent to 90 mole percent of the total carboxyl groups contributed to the polymer by the monocarboxylic acid monomer or by the dicarboxylic acid monomer are reacted with compounds selected from the group consisting of substituted or unsubstituted alcohols having alkyl groups of from about 1 to 48 carbon atoms and primary or secondary substituted or unsubstituted amines having alkyl groups of from about 1 to 30 carbon atoms. ### Claim 21 (depends on 20) The method as claimed in claim 20 wherein from about 5 to about 30 mole percent of the anhydride groups are reacted with taurine. ### Claim 22 (depends on 17) The method as claimed in claim 17 wherein the composition includes a fatty acid. ### Claim 23 (depends on 22) The method as claimed in claim 22 wherein the fatty acid is selected from the group consisting of fatty acids having from about 16 to 22 carbon atoms. ### Claim 24 (depends on 17) The method as claimed in claim 17 wherein the composition comprises from about 5% to 30% of the polymer, from about 5% to 60% of the fatty acid and the balance comprising the wax. ### Claim 25 (depends on 24) The method as claimed in claim 24 wherein the weight ratio of polymer to fatty acid is from 25:75 to 75:25. ### Claim 26 (depends on 17) The method as claimed in claim 17 wherein the wax is selected from the group consisting of paraffin wax, microcrystalline wax and mixtures thereof. ### Claim 27 (depends on 1) The method as claimed in claim 1 wherein from about 1 mole percent to 90 mole percent of the total carboxyl groups contributed to the polymer by the monocarboxylic acid monomer or by the dicarboxylic acid monomer are reacted with compounds selected from the group consisting of substituted or unsubstituted alcohols having alkyl groups of from about 1 to 48 carbon atoms and primary or secondary substituted or unsubstituted amines having alkyl groups of from about 1 to 30 carbon atoms. ### Claim 28 (depends on 27) The method as claimed in claim 27 wherein from about 5 to about 30 mole percent of the anhydride groups are reacted with taurine. ### Claim 29 (depends on 1) The method as claimed in claim 1 wherein the composition includes a fatty acid. ### Claim 30 (depends on 29) The method as claimed in claim 29 wherein the fatty acid is selected from the group consisting of fatty acids having from about 16 to 22 carbon atoms. ### Claim 31 (depends on 1) The method as claimed in claim 1 wherein the composition comprises from about 5% to 30% of the polymer, from about 5% to 60% of the fatty acid and the balance comprising the wax. ### Claim 32 (depends on 31) The method as claimed in claim 31 wherein the weight ratio of polymer to fatty acid is from 25:75 to 75:25. ### Claim 33 (depends on 1) The method as claimed in claim 1 wherein the wax is selected from the group consisting of paraffin wax, microcrystalline wax and mixtures thereof. ### Claim 34 (depends on 5) The method as claimed in claim 5 wherein from about 1 mole percent to 90 mole percent of the total carboxyl groups contributed to the polymer by the dicarboxylic acid monomer are reacted with compounds selected from the group consisting of substituted or unsubstituted alcohols having alkyl groups of from about 1 to 48 carbon atoms and primary or secondary substituted or unsubstituted amines having alkyl groups of from about 1 to 30 carbon atoms. ### Claim 35 (depends on 34) The method as claimed in claim 34 wherein from about 5 to about 30 mole percent of the anhydride groups are reacted with taurine. ### Claim 36 (depends on 5) The method as claimed in claim 5 wherein the composition includes a fatty acid. ### Claim 37 (depends on 36) The method as claimed in claim 36 wherein the fatty acid is selected from the group consisting of fatty acids having from about 16 to 22 carbon atoms. ### Claim 38 (depends on 5) The method as claimed in claim 5 wherein the composition comprises from about 5% to 30% of the polymer, from about 5% to 60% of the fatty acid and the balance comprising the wax. ### Claim 39 (depends on 38) The method as claimed in claim 38 wherein the weight ratio of polymer to fatty acid is from 25:75 to 75:25. ### Claim 40 (depends on 5) The method as claimed in claim 5 wherein the wax is selected from the group consisting of paraffin wax, microcrystalline wax and mixtures thereof. ### Claim 41 (depends on 9) The method as claimed in claim 9 wherein from about 1 mole percent to 90 mole percent of the total carboxyl groups contributed to the polymer by the monocarboxylic acid monomer or by the dicarboxylic acid monomer are reacted with compounds selected from the group consisting of substituted or unsubstituted alcohols having alkyl groups of from about 1 to 48 carbon atoms and primary or secondary substituted or unsubstituted amines having alkyl groups of from about 1 to 30 carbon atoms. ### Claim 42 (depends on 41) The method as claimed in claim 41 wherein from about 5 to about 30 mole percent of the anydride groups are reacted with taurine. ### Claim 43 (depends on 9) The method as claimed in claim 9 wherein the weight ratio of polymer to fatty acid is from 25:75 to 75:25. ### Claim 44 (depends on 13) The method as claimed in claim 13 wherein the weight ratio of polymer to fatty acid is from 25:75 to 75:25.