# US 5,699,733 A · Screen printing on film coated substrates

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 5,699,733 A
- Document ID: US5699733A
- Status: Granted
- Kind: A
- Application number: 08/719,349
- Filed: 1996-09-25
- Granted: 1997-12-23
- Earliest claimed: 1996-09-25
- Assignees: Industrial Technology Research Institute
- Inventors: De-An Chang; Jin-Yuh Lu
- Web page: https://patentgrep.com/patent/US5699733A

## CPC

- B41M 1/12: Stencil printing; Silk-screen printing
- B41M: PRINTING, DUPLICATING, MARKING, OR COPYING PROCESSES; COLOUR PRINTING, (correction of typographical errors B41J; processes for applying transfer pictures or the like B44C1/16; fluid media for correction of typographical errors by coating C09D10/00; printing textiles D06P)

## Abstract

An improved method of screen printing is described wherein a double sided tape (dry film) is applied between the substrate and the screened-on paste. Since the dry film ensures the adhesion of the paste, no minimum thickness of paste is needed to attain good adhesion. By applying a thin layer of paste multiple times any thickness over a wide range can be obtained. Once the desired thickness of paste has been applied, the dry film is removed by firing in an oxidizing atmosphere. The method is applicable to, among others, phosphors, resistive materials, and conductive materials.

## Claims

### Claim 1

A method for screen printing comprising the sequential steps of:
providing a substrate having a top surface;
laminating a dry film onto said top surface;
screen printing a first layer of a paste onto said dry film;
optionally screen printing additional layers of paste on said first paste layer; and
firing the substrate, the dry film, and any of the paste layers, thereby removing said dry film.

### Claim 2 (depends on 1)

The method of claim 1 wherein said paste is taken from the group consisting of phosphor paste, glass frit paste, barrier rib paste, insulating paste, conductive paste, and resistive paste.

### Claim 3 (depends on 1)

The method of claim 1 wherein the substrate is glass or aluminum oxide or a metal.

### Claim 4 (depends on 1)

The method of claim 1 wherein the minimum thickness of a single layer of the paste is about 4 microns.

### Claim 5 (depends on 1)

The method of claim 1 wherein the step of firing the substrate, the dry film, and any of the paste layers further comprises heating in air for between about 0.5 and 4 hours at a temperature between about 500.degree. and 1,300.degree. C.

### Claim 6 (depends on 1)

The method of claim 1 wherein the number of layers of paste is between 1 and 6.

### Claim 7 (depends on 1)

The method of claim 1 wherein the total thickness of the paste is between about 4 and 30 microns.

### Claim 8

A method for screen printing comprising the sequential steps of:
providing a substrate having a top surface;
laminating a dry film onto said top surface;
through a patterned screen, screen printing a first layer of a paste onto said dry film;
without changing the relative positions of the screen and the substrate, screen printing, through said patterned screen, additional paste layers; and
firing the substrate, the dry film, and the paste layers, thereby removing said dry film.

### Claim 9 (depends on 8)

The method of claim 8 wherein said paste comprises a phosphor.

### Claim 10 (depends on 9)

The method of claim 9 wherein the step of firing the substrate, the dry film, and the phosphor layers further comprises heating in air for between about 0.5 and 4 hours at a temperature between about 500.degree. and 600.degree. C.

### Claim 11 (depends on 8)

The method of claim 8 wherein said paste comprises a resistive material.

### Claim 12 (depends on 11)

The method of claim 11 wherein said resistive material taken from the group consisting of RuO.sub.2 --Ag, Pd--Ag, RuO.sub.2 --MnO, RuO.sub.2 --MnO--Al.sub.2 O.sub.3, and RuO.sub.2 --MnO--PbO.

### Claim 13 (depends on 11)

The method of claim 11 wherein the step of firing the substrate, the dry film, and the resistive material layers further comprises heating in air for between about 30 and 60 minutes at a temperature between about 500.degree. and 1,250.degree. C.

### Claim 14 (depends on 8)

The method of claim 8 wherein said paste comprises a conductive material.

### Claim 15 (depends on 14)

The method of claim 14 wherein said conductive material is taken from the group consisting of Pt, Ag, Pd, Ag--Pd, Ag--Pt, Ag--Zn, and Ag--Al.

### Claim 16 (depends on 14)

The method of claim 14 wherein the step of firing the substrate, the dry film, and the conductive material layers further comprises heating in air for between about 30 and 60 minutes at a temperature between about 500.degree. and 1,300.degree. C.