Polyesters production process
AssigneeE. I. Du Pont de Nemours and Company
InventorKamlesh Kumar Bhatia
Life of this patent
Estimating the term…
Abstract
An atmospheric pressure process for the continuous production of polyester is disclosed wherein a melt of bis(3-hydroxy propyl) terephthalate, or its low molecular oligomers, obtained by esterifying terephthalic acid or transesterifying dimethyl terephthalate with propylene glycol, is intimately contacted with an inert gas to facilitate polymerization and removal of the reaction by-products. The propylene glycol evolved and the inert gas are recycled.
Claims10
A process for preparing poly(1,4-butylene terephthalate) of at least a degree of polymerization of 50, by polymerizing bis(4-hydroxy butyl) terephthalate, or low molecular weight oligomers thereof, with the evolution of 1,4-butane diol and other volatile reaction by-products, the process conducted at atmospheric pressure or above, comprising intimately contacting the bis(4-hydroxy butyl) terephthalate or low molecular weight oligomers thereof in melt form with an inert gas flowing at a velocity of 0.2 to 3 ft/sec, such that the interfacial area between the melt and the gas phase is at least about 20 ft2/ft3 of the melt, and removing the volatile reaction by-products with the inert gas wherein the polymerization is completed in less than about 5 hours of contact time while the reactants are maintained in the melt form.
A process for the continuous production of high molecular weight poly(1,4-butylene terephthalate), having a DP of at least 50 from dimethyl terephthalate (DMT) and 1,4-butane diol (BD), the process conducted at about atmospheric pressure or above comprising:
- (a) transesterifying DMT with BD to produce bis(4-hydroxy butyl) terephthalate (BHBT) or its low molecular weight oligomers;
- (b) intimately contacting BHBT or its low molecular weight oligomers, in melt form, with an inert gas flowing in the process countercurrently to the flow of the reaction melt, at a velocity of 0.2 to 3 ft/sec, wherein the contact area is at least about 20 ft.sup.2 /ft.sup.3 of the melt, the 1,4-butane diol and other reaction by-products are continuously removed and wherein the product poly(1,4-butylene terephthalate) is removed continuously while an amount of reaction was equivalent to less than about 5 hours of the product throughput rate is maintained in the melt form;
- (c) recovering 1,4-butane diol, removed in step (b), from the inert gas, for recycle to step (a), and recycling the inert gas back to the system.
Dependencies are inferred from the claim text.