Polyimide coated heavy metal fluoride glass fiber and method of manufacture
AssigneeGallileo Electro-Optics Corporation
InventorsLubos Vacha, Peter J. Melling
Life of this patent
Estimating the term…
Abstract
A method of making a polyimide coated heavy metal fluorinated fiber includes the steps of drawing an optical fiber through a low-temperature curing polyimide solution to form a polyimide coating which cures in a range of about 200.degree. and 390.degree. C. A low curing temperature enables a low temperature profile to be used for curing the coating. The low-temperature curing conditions provide a maximum fiber exposure temperature above the glass transition temperature of the fiber but minimize crystallization of the fiber during curing. The method is also applicable to chalcogenide fibers which carry optical signals in the infrared region.
Claims5
A method of making a coated fiber comprising the steps of:
- drawing a fiber through a curable coating solution to form a coated fiber, said fiber having a glass transition temperature and said curable coating solution having a curing temperature which is higher than said glass transition temperature;
- drawing said coated fiber through a curing oven to form a cured coated fiber, said oven having a temperature profile which exposes said coated fiber to a temperature above the glass transition temperature and sufficient to cure said curable coating solution, said step of drawing through said oven occurring at a rate sufficient to cure said curable coating solution and to minimize crystallization of said fiber and optical losses caused by crystallization.
A method of making a coated fiber comprising the steps of:
- drawing a fiber through a curable coating solution to form a coated fiber, said fiber having a glass transition temperature and said curable solution having a curing temperature which is higher than said glass transition temperature;
- drawing said coated fiber through a curing oven to form a cured coated fiber;
- operating said oven to produce a temperature profile therein which exposes said coated fiber to a temperature above the glass transition temperature and sufficient to cure said curable coating solution, said step of drawing through said oven occurring at a rate sufficient to cure said curable coating solution and to minimize crystallization of said fiber and optical losses caused by crystallization.
A method of making a coated fiber comprising the steps of:
- drawing a fiber through a curable coating solution to form a coated fiber, said fiber having a glass transition temperature and said curable coating solution having a curing temperature which is higher than said glass transition temperature;
- operating a curing oven at a temperature profile sufficient to produce therein a temperature above the glass transition temperature and sufficient to cure said curable coating solution;
- drawing said coated fiber through the curing oven to expose the fiber to the temperature profile within the curing oven at a rate sufficient to cure said curable coating solution to form a cured coated fiber and to minimize crystallization of said fiber and optical losses caused by crystallization.
Dependencies are inferred from the claim text.