Loading patent…
AssigneeGeneral Electric Company
InventorHenry Peter Offer
Estimating the term…
A process for providing a significant improvement in the detrimental tensile residual stress condition on the root side of welds, especially on the inside wall of piping welds. The method uses a high welding torch travel speed (>10 inches/min), especially on the last one or two cap passes. The process relies on the limited thermal heat sink capability of the pipe wall and nearly completed weld joint itself to generate a significant through-wall temperature gradient, and therefore a sufficient through-wall stress gradient during the welding. This stress gradient results in metal plasticity and permanent strains, and therefore a reduction in the magnitude of the final residual stress or, preferably as conditions allow, a reversal in the direction of the stresses from tensile to compressive. The method can be used as a welding process or as a heat treatment. In the case of heat treatment, the far surface of the weld joint is heated without fusion of the material making up the far surface.
A method for heat treating first and second metal components joined in a depthwise direction by a weld joint formed, at least in part, by a root pass at a near surface and a plurality of passes built successively on top of said root pass in a direction from said near surface to a far surface, comprising the step of heating said far surface of said weld joint during a pass by discharging an arc of electric current from a tip of an electrode traveling along said far surface at a torch travel speed such that a temperature distribution is created across the material between said near and far surfaces, whereby the stress state at said near surface undergoes a reversal from tension to compression substantially without heat sinking external to said near surface.
A method for heat treating first and second metal components joined in a depthwise direction by a weld joint formed, at least in part, by a root pass at a near surface and a plurality of passes built successively on top of said root pass in a direction from said near surface to a far surface, comprising the step of heating said far surface of said weld joint during a cap pass by discharging an arc of electric current from a tip of an electrode traveling along said far surface at a torch travel speed such that a temperature distribution is created across the material between said near and far surfaces substantially without heat sinking external to said near surface and said electrode travels at a speed greater than 10 inches per minute during said cap pass.
A weld joint for joining first and second metal components in a depthwise direction, comprising a root pass at a near surface and a plurality of passes built successively on top of said root pass in a direction from said near surface to a far surface, said weld joint having a residual stress state produced by a process comprising the step of heating said far surface of said weld joint during a pass by discharging an arc of electric current from a tip of an electrode traveling along said far surface at a torch travel speed such that a temperature distribution is created across the material between said near and far surfaces, whereby the stress state at said near surface undergoes a transition from relatively high tension to relatively low tension or compression substantially without heat sinking external to said near surface.
A method for heat treating first and second metal components joined in a depthwise direction by a weld joint formed, at least in part, by a root pass at a near surface and a plurality of passes built successively on top of said root pass in a direction from said near surface to a far surface, wherein prior to said heat treating said weld joint has residual tensile stresses at said near surface which are substantially equal to or greater than a predetermined tensile stress, comprising the step of heating said far surface of said weld joint during a cap pass by discharging an arc of electric current from a tip of an electrode traveling along said far surface at a torch travel speed such that a temperature distribution is created across the material between said near and far surfaces, whereby a stress less than said predetermined tensile stress is formed at said near surface substantially without heat sinking external to said near surface.
Dependencies are inferred from the claim text.