Loading patent…
AssigneePall Corporation
InventorsPeter J. Degen, John Mischenko, III, Robert E. Kesting, Moira H. Bilich, Trevor A. Staff
Estimating the term…
The present invention provides for the first time ultrafiltration/diafiltration membranes that are capable of excluding 0.02 .mu.m diameter, monodisperse, latex particles and are capable of being dried without loss of such ultrafiltration properties. A rapid, reliable method for integrity testing membranes also has now been discovered. The test has particular applicability to ultrafiltration membranes, although it may also be used for testing microfiltration membranes as well. In accordance with the method, referred to as the K.sub.UF method, the membrane to be tested is first thoroughly wetted with a wetting liquid that is capable of fully wetting the membrane; a displacing liquid is placed in contact with one side of the wetted membrane and increasing pressure is then applied to said displacing liquid; and the flow rate through said membrane is measured as a function of the applied pressure; wherein the displacing liquid is substantially insoluble in the wetting liquid and the interfacial tension between the two liquids is about 10.0 dynes/cm or less. A plot of the flow rate of liquid, per unit area of the membrane, through the membrane as a function of applied pressure can be made and a straight line may be drawn through the steep part of the resulting curve, using regression analysis, which will intersect the horizontal axis at a given pressure value, which is then the K.sub.UF value.
An ultrafiltration polymeric membrane comprising a skin that is capable of excluding 0.04 .mu.m diameter, monodisperse, latex particles with a rejection coefficient greater than 0.998 after said membrane has been fully dried, and wherein said membrane has a K.sub.UF flow rate at 10 psi, using 1-butanol saturated with water as the wetting liquid and water saturated with 1-butanol as the displacing liquid at ambient temperature, below 50 cc/min per square foot of membrane area after being wet/dry cycled at least once.
A method for manufacturing an ultrafiltration membrane comprising (a) dissolving a polymeric resin in a carrier comprising both a solvent for the resin and a nonsolvent for the resin to form a solution, wherein the resin is present in an amount from 15 to 20 weight percent of the solution, and the amount of nonsolvent is from 26 to 34 weight percent of the solution, with the ratio of solvent to nonsolvent being from 1.5:1 to 2:1, such that the total amount of resin, solvent, and nonsolvent does not exceed 100%, (b) rapidly mixing the solution to reduce or eliminate the presence of gel particles, (c) filtering the solution to remove any gel particles that are present, (d) degassing the solution to remove any entrained gas, (e) casting or spinning the solution onto a support, and (f) contacting the resulting cast or spun solution with a setting bath that comprises both a solvent and a nonsolvent for the resin.
A method for manufacturing an ultrafiltration membrane comprising (a) dissolving a polymeric resin in a carrier comprising both a solvent for the resin and a nonsolvent for the resin, wherein the resin is present in an amount from 15 to 20 weight percent, and the amount of nonsolvent is from 26 to 34 weight percent of the solution, with the ratio of solvent to nonsolvent being from 1.5:1 to 2:1, (b) rapidly mixing the solution to reduce or eliminate the presence of gel particles, (c) degassing the solution to remove any entrained gas, (d) casting or spinning the solution onto a support, and (e) contacting the resulting cast or spun solution with a setting bath that comprises both a solvent and a nonsolvent for the resin.
Dependencies are inferred from the claim text.