Method for placing indicia on substrates having an enamel band thereon
AssigneeLibbey-Owens-Ford Co.
InventorAnthony C. Ho
Life of this patent
Estimating the term…
Abstract
Indicia is affixed to an enamel band on a substrate. An ink suitable for use in known ink jet printers containing inorganic pigments and no frits is applied in a predetermined, easily changeable, pattern to the surface of an enamel band found on a substrate such as plastic or glass. Subsequently the substrate having the enamel band and ink thereon may be heated to a temperature sufficient to cause the frits in the enamel band to adhere to the inorganic pigment in the ink to form permanent opaque indicia on the enamel band in the form of a separate and distinct layer.
Claims17
A process for affixing indicia to a substrate comprising the steps of:
- a) providing a substrate having an enamel band applied to at least one surface thereof;
- b) applying to the enamel band in a pattern by a non-contact ink jet printing process an ink composition including an inorganic pigment, whereby indicia substantially conforming to the pattern supplied from a non-contact ink jet printer is affixed to the substrate.
A process for affixing indicia and patterns to a polycarbonate glazing for automotive use, including the steps of:
- a) providing a polycarbonate glazing;
- b) utilizing an ink jet printer to apply to the surface of the polycarbonate glazing in a predetermined pattern an ink jet composition comprising:
- i) from about 0.5% to about 80% by weight of pigments,
- ii) from about 20% to about 95% by weight of a vehicle, and
- iii) from 0% to about 30% by weight of resin.
A process for permanently affixing indicia to a soda-lime-silica glass windshield for automotive use, comprising the steps of:
- a) providing a glazing including a surface having a frit containing black enamel band provided thereon;
- b) utilizing an ink jet printer to apply to the black enamel band in a predetermined pattern an ink jet composition comprising:
- i) from about 3% to about 7% by weight of 1-Methoxy-2-Propanol,
- ii) from about 5% to about 10% by weight of Titanium Dioxide,
- iii) from about 20% to about 35% by weight of Methanol,
- iv) from about 20% to about 35% by weight of 2-Butanone, and
- v) from about 1% to about 3% by weight of N-Methyl-2-Pyrrolidone,
- vi) from 0% to 30% acrylic resin, and
- c) firing said windshield having the enamel band and the ink thereon to a temperature and for a time sufficient to cause the pigments in the ink to adhere to the frit in the enamel band;
- and
- d) bending said windshield to a predetermined shape.
A process for permanently affixing indicia to a glass sheet of the type having a frit containing enamel band applied to a surface thereof, said method including the steps of:
- a) utilizing a non-contact ink jet printer to apply to said enamel band an ink composition including from about 5% by weight to about 10% by weight of titanium dioxide pigment at a temperature from about 70.degree. F. to about 200.degree. F.;
- and
- b) heating the glass article having the ink thereon to a temperature and for a time sufficient to cause the titanium dioxide pigment to adhere to the frit present in said enamel band.
A process for permanently affixing indicia to a glass sheet, including the steps of:
- a) providing a glass sheet, including a surface having a frit containing enamel band applied thereto;
- b) utilizing a non-contact ink jet printer to apply to the surface in a predetermined pattern by contacting therewith droplets generated by said non-contact ink jet printer an ink composition comprising:
- i) from about 3% to about 7% by weight of 1-Methoxy-2-Propanol,
- ii) from about 5% to about 10% by weight of Titanium Dioxide,
- iii) from about 20% to about 35% by weight of Methanol,
- iv) from about 20% to about 35% by weight of 2-Butanone, and
- v) from about 1% to about 3% by weight of N-Methyl-2-Pyrrolidone,
- vi) from 0% to 30% of acrylic resin, and
- c) heating the glass article having the enamel band and the ink thereon to a temperature and for a time sufficient to cause the pigment in the ink to adhere to the frit in the enamel band.
A method for permanently affixing indicia to soda-lime-silica glass glazings for automotive or architectural use, including the steps of:
- a) providing a glazing including a surface having a frit containing black enamel band provided thereon;
- b) utilizing an ink jet printer to apply to the black enamel band in a predetermined pattern an ink jet composition comprising:
- i) from about 3% to about 7% weight of 1-Methoxy-2-Propanol,
- ii) from about 5% to about 10% by weight of Titanium Dioxide,
- iii) from about 20% to about 35% by weight of Methanol,
- iv) from about 20% to about 35% by weight of 2-Butanone, and
- v) from about 1% to about 3% weight of N-Methyl-2-Pyrrolidone,
- vi) from 0% to 30% acrylic resin, and
- c) firing the glazing having the enamel band and the ink thereon to a temperature and for a time sufficient to cause the pigments in the ink to adhere to the frit in the enamel band.
Dependencies are inferred from the claim text.