Self-aligned polycide process that utilizes a planarized layer of material to expose polysilicon structures to a subsequently deposited metal layer that is reacted to form the metal silicide

A method for forming a layer of metal silicide over a structure formed as part of a semiconductor device, the method comprising the steps of:

• forming a layer of insulation material over the semiconductor device so that the structure is covered with the layer of insulation material;
• removing the layer of insulation material until the layer of insulation material is substantially planar, and the thickness of the layer of insulation material over the structure is within a thickness range;
• etching the planarized layer of insulation material until portions of the structure are exposed;
• depositing a layer of metal over the layer of insulation material and the exposed structure;
• reacting the layer of metal with the structure to form a layer of metal silicide over the structure and a layer of unreacted metal over the layer of insulation material;
• and
• removing the layer of unreacted metal from the layer of insulation material.

A method for forming a layer of metal silicide over a structure formed as part of a semiconductor device, the method comprising the steps of:

• forming a layer of insulation material over the semiconductor device such that the structure is covered with the layer of insulation material;
• removing the layer of insulation material until the layer of insulation material is substantially planar, and a surface of the structure is exposed;
• and
• selectively chemical vapor depositing a layer of metal over the structure.

A method for forming polycide on a semiconductor device formed in a substrate of a first conductivity type, the device including:

• a plurality of active device regions;
• a field oxide region formed in the substrate that isolates the plurality of active device regions,
• a plurality of spaced-apart doped regions formed in the substrate so that a pair of doped regions is formed in each active device region, the doped regions defining a plurality of substrate channel regions such that each pair of doped regions in an active device region defines a corresponding substrate channel region therebetween,
• a plurality of gate oxide regions formed over the plurality of substrate channel regions such that each gate oxide region is formed over a corresponding substrate channel region,
• a plurality of gates formed over the plurality of gate oxide regions such that each gate is formed over a corresponding gate oxide region, each of the gates having sidewalls,
• an interconnect line formed over the field oxide region, the interconnect line having sidewalls, and
• a plurality of spacers formed over the sidewalls of the gates, and the sidewalls of the interconnect line,
• the method comprising the steps of:
• depositing a layer of insulation material having a thickness over the field oxide region, the substrate, the gates, the interconnect line, and the spacers;
• removing the layer of insulation material until the layer of insulation material is substantially planar, and a surface of the gates is exposed;
• etching the layer of insulation material until surfaces of both the gates and the interconnect line are exposed;
• depositing a layer of metal over the layer of insulation material, the gates, the spacers, and the interconnect line;
• reacting the layer of metal with the gates and interconnect line to form a layer of metal silicide over the gates and interconnect line, and a layer of unreacted metal over the layer of insulation material and the spacers;
• and
• removing the layer of unreacted metal from the layer of insulation material and the spacers, thereby leaving the layer of metal silicide over the gates and the interconnect line.

A method for forming polycide on a semiconductor device formed in a substrate of a first conductivity type, the device including:

• a plurality of active device regions;
• a field oxide region formed in the substrate that isolates the plurality of active device regions,
• a plurality of spaced-apart doped regions formed in the substrate so that a pair of doped regions is formed in each active device region, the doped regions defining a plurality of substrate channel regions such that each pair of doped regions in an active device region defines a corresponding substrate channel region therebetween,
• a plurality of gate oxide regions formed over the plurality of substrate channel regions such that each gate oxide region is formed over a corresponding substrate channel region,
• a plurality of gates formed over the plurality of gate oxide regions such that each gate is formed over a corresponding gate oxide region,
• an interconnect line formed over the field oxide region, the interconnect line having sidewalls, and
• a plurality of spacers formed over the sidewalls of the gates, and the sidewalls of the interconnect line,
• the method comprising the steps of:
• depositing a layer of insulation material having a thickness over the field oxide region, the substrate, the gates, the interconnect line, and the spacers;
• removing the layer of insulation material, a portion of the gates, and a portion of the spacers formed over the sidewalls of the gates until the layer of insulation material is substantially planar, and the top surfaces of the gates and the interconnect line are exposed;
• depositing a layer of metal over the layer of insulation material, the spacers, the gates, and the interconnect line;
• reacting the layer of metal with the gates and the interconnect line to form a layer of metal silicide over the gates and interconnect line, and a layer of unreacted metal over the layer of insulation material and the spacers;
• and
• removing the layer of unreacted metal, thereby leaving the layer of metal silicide over the gates and the interconnect line.

A method for forming polycide on a semiconductor device formed in a substrate of a first conductivity type, the device including:

• a plurality of active device regions;
• a field oxide region formed in the substrate that isolates the plurality of active device regions,
• a plurality of spaced-apart doped regions formed in the substrate so that a pair of doped regions is formed in each active device region, the doped regions defining a plurality of substrate channel regions such that each pair of doped regions in an active device region defines a corresponding substrate channel region therebetween,
• a plurality of gate oxide regions formed over the plurality of substrate channel regions such that each gate oxide region is formed over a corresponding substrate channel region,
• a plurality of gates formed over the plurality of gate oxide regions such that each gate is formed over a corresponding gate oxide region, each of the gates having sidewalls,
• an interconnect line formed over the field oxide region, the interconnect line having sidewalls, and
• a plurality of spacers formed over the sidewalls of the gates, and the sidewalls of the interconnect line,
• the method comprising the steps of:
• depositing a layer of insulation material having a thickness over the field oxide region, the substrate, the gates, the interconnect line, and the spacers;
• removing the layer of insulation material until the layer of insulation material is substantially planar, and the thickness of the layer of insulation material over the gates is within a thickness range;
• etching the layer of insulation material until surfaces of both the gates and the interconnect line are exposed;
• depositing a layer of metal over the layer of insulation material, the gates, the spacers, and the interconnect line;
• reacting the layer of metal with the gates and interconnect line to form a layer of metal silicide over the gates and interconnect line, and a layer of unreacted metal over the layer of insulation material and the spacers;
• and
• removing the layer of unreacted metal, thereby leaving the layer of metal silicide over the gates and the interconnect line.

A method for forming polycide on a semiconductor device formed in a substrate of a first conductivity type, the device including:

• spaced-apart doped regions formed in the substrate, the doped regions defining a substrate channel region therebetween,
• a gate oxide region formed over the substrate channel region,
• a gate formed over the gate oxide region, the gate having sidewalls, and
• a spacer formed over the sidewalls of the gate,
• the method comprising the steps of:
• depositing a layer of insulation material having a thickness over the substrate, the gate, and the spacer;
• removing the layer of insulation material until the layer of insulation material is substantially planar, and the thickness of the layer of insulation material over the gate is within a thickness range;
• etching the layer of insulation material until a surface of the gate is exposed;
• depositing a layer of metal over the layer of insulation material and the gate;
• reacting the layer of metal with the gate to form a layer of metal silicide over the gate, and a layer of unreacted metal over the layer of insulation material;
• and
• removing the layer of unreacted metal from the layer of insulation material, thereby leaving the layer of metal silicide over the gate.