A process for forming a multilayer wiring in a fabricated wafer, said multilayer wiring comprising a plurality of wirings stacked via silicon and oxygen-containing insulating layers each provided between one and another of said wirings, one of said wirings being electrically connected to another wiring through via-holes, the surfaces of the wiring exposed at the via-holes being covered by an oxide film, which comprises the steps of:

• (a) introducing into a pretreatment chamber said fabricated wafer having the wirings, one of which is substantially covered thereon by the oxygen-containing insulating layer having said via-holes;
• (b) introducing a rare gas into said pretreatment chamber and then forming a plasma in said chamber by electric discharge to physically remove a substantial amount of said oxide film from the exposed surfaces due to the collision of plasma particles against the surfaces, said surface of said oxygen-containing insulating layer having a reduced oxygen/silicon ratio after the pretreatment of step (b);
• (c) introducing an etching gas into said chamber, then forming a plasma in said pretreatment chamber by electric discharge and introducing said fabricated wafer from step (b) into said plasma to increase the oxygen content of the surface of said oxygen-containing insulating layer, and restore the reduced oxygen/silicon ratio of the surface of the oxygen-containing insulating layer to that ratio found before the pretreatment of step (b);
• (d) ceasing the introduction of both the rare gas and etching gas in said pretreatment chamber and then evacuating said pretreatment chamber;
• (e) subjecting the exposed surfaces of the wiring to a treatment for corrosion prevention by exposing the fabricated wafer to a plasma of one or more of oxygen gas, fluorine gas, and a fluorine compound-containing gas, and transferring said fabricated wafer to an evacuated deposition chamber;
• (f) introducing a deposition material gas into said deposition chamber containing the corrosion-prevention treated wafer placed therein, and selectively depositing said material only on said exposed surfaces of the wiring in said via-holes to fill said via-holes with the deposited material;
• and,
• (g) preparing another wiring on said oxygen-containing insulating layer.

A process for forming a multilayer wiring in a fabricated wafer, said multilayer wiring comprising a plurality of wirings stacked via silicon and oxygen-containing insulating layers each provided between one and another of said wirings, one of said wirings being electrically connected to another wiring through via-holes, the surfaces of the wiring exposed at the via-holes being covered by an oxide film, which comprises the steps of:

• (a) introducing into a pretreatment chamber said fabricated wafer having the wirings, one of which is substantially covered thereon by the oxygen-containing insulating layer having said via-holes;
• (b) introducing a rare gas into said pretreatment chamber, then forming a plasma in said chamber by electric discharge to physically remove a substantial amount of said oxide film from the exposed surfaces due to the collision of plasma particles against the surfaces, and ceasing the introduction of the rare gas in the pretreatment chamber, said surface of said oxygen-containing insulating layer having a reduced oxygen/silicon ratio after the pretreatment of step (b);
• (c) introducing an etching gas into said chamber, then forming a plasma in said pretreatment chamber by electric discharge and introducing said fabricated wafer from step (b) into said plasma to increase the oxygen content of the surface of said oxygen-containing insulating layer and restore the reduced oxygen/silicon ratio of the surface of the oxygen-containing insulating layer to that ratio found before the pretreatment of step (b);
• (d) ceasing the introduction of the etching gas in the pretreatment chamber and then evacuating said pretreatment chamber;
• (e) transferring said fabricated wafer from said pretreatment chamber to a deposition chamber;
• (f) introducing a depositing material gas into said deposition chamber and selectively depositing said material only on said exposed surfaces of the wiring in said via-holes to fill said via-holes with the deposited material;
• and,
• (g) preparing another wiring on said oxygen-containing insulating layer.

A process for forming a multilayer wiring in a fabricated wafer, said multilayer wiring comprising a plurality of wirings stacked via silicon and oxygen-containing insulating layers each provided between one and another of said wirings, one of said wirings being electrically connected to another wiring through via-holes, the surfaces of the wiring exposed at the via-holes being covered by an oxide film, which comprises the steps of:

• (a) introducing into a pretreatment chamber said fabricated wafer having the wirings, one of which is substantially covered thereon by the oxygen-containing insulating layer having said via-holes;
• (b) introducing a rare gas into said pretreatment chamber, then forming a plasma in said chamber by electric discharge to physically remove a substantial amount of said oxide film from the exposed surfaces due to the collision of plasma particles against the surfaces, and ceasing the introduction of the rare gas in the pretreatment chamber, said surface of said oxygen-containing insulating layer having a reduced oxygen/silicon ratio after the pretreatment of step (b);
• (c) introducing an etching gas into said chamber, then forming a plasma in said pretreatment chamber by electric discharge and introducing said fabricated wafer from step (b) into said plasma to increase the oxygen content of the surface of said oxygen-containing insulating layer, and restore the reduced oxygen/silicon ratio of the surface of the oxygen-containing insulating layer to that ratio found before the pretreatment of step (b);
• (d) ceasing the introduction of the etching gas in said pretreatment chamber and then evacuating said pretreatment chamber;
• (e) subjecting the exposed surfaces of the wiring to a treatment for corrosion prevention by exposing the fabricated wafer to a plasma of one or more of oxygen gas, fluorine gas, and a fluorine compound-containing gas, and transferring said fabricated wafer to an evacuated deposition chamber;
• (f) introducing a deposition material gas into said deposition chamber containing the corrosion-prevention treated wafer placed therein, and selectively depositing said material only on said exposed surfaces of the wiring in said via-holes to fill said via-holes with the deposited material;
• and,
• (g) preparing another wiring on said oxygen-containing insulating layer.

A process for forming a multilayer wiring in a fabricated wafer, said multilayer wiring comprising a plurality of wirings stacked via silicon and oxygen-containing insulating layers each provided between one and another of said wirings, one of said wirings being electrically connected to another wiring through via-holes, the surfaces of the wiring exposed at the via-holes being covered by an oxide film, which comprises the steps of:

• (a) introducing into a pretreatment chamber said fabricated wafer having the wirings, one of which is substantially covered thereon by the oxygen-containing insulating layer having said via-holes;
• (b) introducing a combination of a rare gas and an etching gas or an etching gas alone, forming a plasma of said gases or gas by electric discharge, and exposing said fabricated wafer to the plasma, to physically remove an amount of said oxide film from the exposed surfaces due to the collision of plasma particles against the surfaces and chemically removing an amount of said oxide with radicals in said plasma, said removal of the oxide film reducing the oxygen/silicon ratio of the surface of the oxygen-containing insulating layer, while simultaneously increasing the oxygen content of the surface of said oxygen-containing insulating layer to restore the oxygen/silicon ratio of the surface of the oxygen-containing insulating layer to that ratio found before the pretreatment of step (a);
• (c) ceasing the introduction of the combination of the rare gas and the etching gas or the etching gas alone in said pretreatment chamber and then evacuating said pretreatment chamber;
• (d) transferring said fabricated wafer from said pretreatment chamber to a deposition chamber;
• (e) introducing a depositing material gas into said deposition chamber and selectively depositing said material only on said exposed surfaces of the wiring in said via-holes to fill said via-holes with the deposited material;
• and,
• (f) preparing another wiring on said oxygen-containing insulating layer.

A process for forming a multilayer wiring in a fabricated wafer, said multilayer wiring comprising a plurality of wirings stacked via silicon and oxygen-containing insulating layers each provided between one and another of said wirings, one of said wirings being electrically connected to another wiring through via-holes, the surfaces of the wiring exposed at the via-holes being covered by an oxide film, which comprises the steps of:

• (a) introducing into a pretreatment chamber said fabricated wafer having the wirings, one of which is substantially covered thereon by the oxygen-containing insulating layer having said via-holes
• (b) introducing a combination of a rare gas and an etching gas or an etching gas alone, forming a plasma of said gases or gas by electric discharge, and exposing said fabricated wafer to the plasma, to physically remove an amount of said oxide film from the exposed surfaces due to the collision of plasma particles against the surfaces and chemically removing an amount of said oxide with radicals in said plasma, said removal of the oxide film reducing the oxygen/silicon ratio of the surface of the oxygen-containing insulating layer, while simultaneously increasing the oxygen content of the surface of said oxygen-containing insulating layer to restore the oxygen/silicon ratio of the surface of the oxygen-containing insulating layer to that ratio found before the pretreatment of step (a);
• (c) ceasing the introduction of the combination of the rare gas and the etching gas or the etching gas alone in said pretreatment chamber and then evacuating said pretreatment chamber;
• (d) subjecting the exposed surfaces of the wiring to a treatment for corrosion prevention by exposing the fabricated wafer to a plasma of one or more of oxygen gas, fluorine gas, and a fluorine compound-containing gas, and transferring said fabricated wafer to an evacuated deposition chamber;
• and,
• (e) introducing a deposition material gas into said deposition chamber containing the corrosion-prevention treated wafer placed therein, and selectively depositing said material only on said exposed surfaces of the wiring in said via-holes to fill said via-holes with the deposited material;
• and,
• (f) preparing another wiring on said oxygen-containing insulating layer.