Loading patent…
AssigneeGeneral Electric Company
InventorsHenry Peter Offer, Lawrence Michael Grycko
Estimating the term…
A welding process and an apparatus used therein for providing a significant improvement in the detrimental tensile residual stress condition on the root side of welds, especially on the inside wall of piping welds. The method combines an extremely thin weld joint design with a non-circular cylindrical, thin welding electrode having an elongated cross-sectional shape. During welding, the elongated dimension is aligned parallel with the length of the weld joint. This combination enables joining of piping and other residual stress-sensitive components with both the initial weld joint preparation and the completed weld having a uniquely thin width and with a high aspect ratio of depth to width. Use of this high-aspect-ratio weld joint process substantially mitigates welding-induced residual stresses, without the normally required internal water cooling. The process is considered to be effective in mitigating residual stresses and the associated welding strains (distortion) in joints having any path shape, whether welded from one or more sides of the material.
A welding electrode comprising a blade having an axis and a tip, wherein said tip is joined and electrically connected to one end of said blade, said blade is a cylinder having a generally rectangular cross section and having a thickness dimension in a thickness direction perpendicular to said axis and a width dimension in a width direction perpendicular to said thickness direction and to said axis, the ratio of said width dimension to said thickness dimension is at least 1.5:1, and said tip is a solid body comprising first, second and third faces, said first face being perpendicular to said blade axis, said second face being disposed obliquely relative to said first face, said third face being disposed obliquely relative to said first face and being non-parallel with said second face, said second and third faces being trapezoidal in shape, said first and second faces being joined at a first linear juncture, said first and third faces being joined at a second linear juncture, said blade and said second face being joined at a third linear juncture, said blade and said third face being joined at a fourth linear juncture, said first through fourth linear junctures being mutually parallel.
A method for joining first and second metal components in a depthwise direction, said first and second metal components in an unjoined state having first and second sidewalls respectively which are separated by a groove having at least a predetermined width, comprising the steps of continuously feeding weld material in the vicinity of a tip of an electrode which travels at a selected travel speed during a particular weld pass, continuously melting said weld material inside said groove by discharging electric current from a tip of said electrode in accordance with selected welding parameters while said electrode travels at said selected travel speed, and solidifying said melted weld material to form fused beads said electrode comprising a blade having an end joined and electrically connected to said tip, said blade having a non-circular cross section with a first dimension in a first direction and a second dimension in a second direction, said first and second directions being mutually perpendicular, said first dimension being less than and said second dimension being greater than said predetermined width of said groove, wherein a predetermined number of weld passes collectively produce a final residual stress state which is substantially compressive substantially across said weld joint and heat affected zones thereof, said compressive residual stress state being attained without the use of an external heat sinking medium to extract inputted heat during any of said weld passes.
A weld joint for joining first and second metal components in a depthwise direction, said first and second metal components in an unjoined state having first and second sidewalls respectively which are separated by a groove having at least a predetermined width, said weld joint being made by a process comprising the steps of continuously feeding weld material in the vicinity of a tip of an electrode traveling at a selected travel speed, continuously melting said weld material inside said groove by discharging electric current from said tip of said electrode in accordance with selected welding parameters while said electrode travels at said selected travel speed, and solidifying said melted weld material to form fused beads, wherein a predetermined number of weld passes collectively produce a final residual stress state which is substantially compressive substantially across said weld joint and heat affected zones thereof, said compressive residual stress state being attained without the use of an external heat sinking medium to extract inputted heat during any of said weld passes.
Dependencies are inferred from the claim text.