Fluidity control of cementitious compositions
AssigneesMBT Holding AG, Nippon Shokubai Co., Ltd.
InventorsYoshio Tanaka, Akira Ohta, Hideyuki Tahara, Tsuyoshi Hirata
Life of this patent
Estimating the term…
Abstract
An admixture for modifying the fluidity of a cementitious mixture comprises a cement-dispersing agent which is an aqueous solution of polymer, in which solution an oxyalkylene-based defoaming agent is dissolved or dispersed in particles of no greater that 20 .mu.M diameter. The polymer is preferably a polymer which comprises units derived from unsaturated carboxylic acid monomer and the polymer is preferably prepared in the presence of the defoaming agent. Particular addition copolymers give particularly good results. The admixture permits good control of the fluidity of cementitious compositions and has extended shelf life.
Claims17
A fluidity-controlling admixture for cementitious compositions comprising an aqueous solution of a polymer, said polymer formed by polymerizing a monomer mixture in the presence of at least one oxyalkylene-based defoaming agent, said monomer mixture comprising
- (a) 5-98% by weight of an (alkoxy)polyalkylene glycol mono(meth)acrylic acid ester monomer of formula (I) ##STR8## wherein R.sup.1 and R.sup.2 are independently hydrogen or methyl,
- R.sup.3 is an alkylene group of from 2-4 carbon atoms,
- R.sup.4 is hydrogen or an alkyl group of from 1 to 22 carbon atoms, and
- m represents an integer of 1 to 100,
- (b) 2 to 95% by weight of a (meth)acrylic acid based monomer of formula (II) ##STR9## wherein R.sup.1 and R.sup.2 have the meanings given above, and M.sup.1 is hydrogen, a monovalent metal, a divalent metal, an ammonium group or an organic amine group, and
- (c) 0 to 50% by weight of a monomer capable of being copolymerized with monomers (a) and (b), provided that the sum of (a), (b) and (c) shall be 100% by weight, said oxyalkylene-based defoaming agent selected from the group consisting of (poly)oxyalkylenes, (poly)oxyalkylene alkyl ethers, oxyethylene and oxypropylene adducts of high alcohols of 12 to 14 carbon atoms, polyoxyalkylene(alkyl)aryl ethers, acetylene ethers of alkylene oxide additionally polymerized with acetylene alcohols, (poly)oxyalkylene aliphatic acid esters, (poly)oxyalkylene (alkyl)aryl ether sulfuric acid esters, (poly)oxyalkylene alkyl phosphates, (poly)oxyalkylene sorbitan aliphatic acid esters and (poly)oxyalkylene alkylamines, said defoaming agent being either dissolved in the polymer solution or stably dispersed therein in particles of no more than 20 .mu.M diameter.
A fluidity-controlling admixture for cementitious compositions comprising an aqueous solution of a polymer, said polymer formed by polymerizing a monomer mixture in the presence of at least one oxyalkylene-based defoaming agent, said monomer mixture comprising
- (a) 5-98% by weight of an (alkoxy)polyalkylene glycol mono(meth)allyl ether based monomer of formula (III) ##STR10## wherein R.sup.1 and R.sup.2 are independently hydrogen or methyl,
- R.sup.3 is an alkylene group of from 2-4 carbon atoms,
- R.sup.4 is hydrogen or an alkyl group of from 1 to 22 carbon atoms,
- m represents an integer of 1 to 100, and
- n is 0 or 1;
- (b) 2 to 95% by weight of an ethylenically Unsaturated carboxylic acid based monomer of formula (IV) ##STR11## wherein X and Y are independently selected from hydrogen, methyl and --COOM.sup.3 or X and Y together with --COOM.sup.2 form an anhydride ring,
- Z is selected from --CH.sub.2 COOM.sup.3, hydrogen or methyl, and
- M.sup.2 and M.sup.3 are independently selected from hydrogen, monovalent metal, divalent metal, an ammonium group, an organic amine group, an alkyl group of 1-20 carbon atoms, an alkylene glycol of 2-4 carbon atoms and a polyalkylene glycol of from 2-100 moles of glycol adduct, provided that a least one of M.sup.2 and M.sup.3 is selected from hydrogen, monovalent metal, divalent metal, ammonium group and an organic amine group, and
- (c) 0 to 50% by weight of a monomer capable of being copolymerized with monomers (a) and (b), provided that the sum of (a), (b) and (c) shall be 100% by weight, said oxyalkylene-based defoaming agent selected from the group consisting of (poly)oxyalkylenes, (poly)oxyalkylene alkyl ethers, oxyethylene and oxypropylene adducts of high alcohols of 12 to 14 carbon atoms, polyoxyalkylene(alkyl)aryl ethers, acetylene ethers of alkylene oxide additionally polymerized with acetylene alcohols, (poly)oxyalkylene aliphatic acid esters, (poly)oxyalkylene (alkyl)aryl ether sulfuric acid esters, (poly)oxyalkylene alkyl phosphates, (poly)oxyalkylene sorbitan aliphatic acid esters and (poly)oxyalkylene alkylamines, said defoaming agent being either dissolved in the polymer solution or stably dispersed therein in particles of no more than 20 .mu.M diameter.
A process for producing a fluidity-controlling admixture for cementitious compositions which comprises polymerizing a monomer mixture in the presence of at least one oxyalkylene-based defoaming agent, said monomer mixture comprising
- (a) 5-98% by weight of an (alkoxy)polyalkylene glycol mono(meth)acrylic acid ester monomer of formula (I) ##STR12## wherein R.sup.1 and R.sup.2 are independently hydrogen or methyl,
- R.sup.3 is an alkylene group of from 2-4 carbon atoms,
- R.sup.4 is hydrogen or an alkyl group of from 1 to 22 carbon atoms, and
- m represents an integer of 1 to 100,
- (b) 2 to 95% by weight of a (meth)acrylic acid based monomer of formula (II) ##STR13## wherein R.sup.1 and R.sup.2 have the meanings given above, and M.sup.1 is hydrogen, a monovalent metal, a divalent metal, an ammonium group or an organic amine group, and
- (c) 0 to 50% by weight of a monomer capable of being copolymerized with monomers (a) and (b), provided that the sum of (a), (b) and (c) shall be 100% by weight, said defoaming agent selected from the group consisting of (poly)oxyalkylenes, (poly)oxyalkylene alkyl ethers, oxyethylene and oxypropylene adducts of high alcohols of 12 to 14 carbon atoms, polyoxyalkylene(alkyl)aryl ethers, acetylene ethers of alkylene oxide additionally polymerized with acetylene alcohols, (poly)oxyalkylene aliphatic acid esters, (poly)oxyalkylene (alkyl)aryl ether sulfuric acid esters, (poly)oxyalkylene alkyl phosphates, (poly)oxyalkylene sorbitan aliphatic acid esters and (poly)oxyalkylene alkylamines.
A process for producing a fluidity-controlling admixture for cementitious compositions comprising polymerizing a monomer mixture in the presence of at least one oxyalkylene-based defoaming agent, said monomer mixture comprising
- (a) 5-98% by weight of an (alkoxy)polyalkylene glycol mono(meth)allyl ether based monomer of formula (III) ##STR14## wherein R.sup.1 and R.sup.2 are independently hydrogen or methyl,
- R.sup.3 is an alkylene group of from 2-4 carbon atoms,
- R.sup.4 is hydrogen or an alkyl group of from 1 to 22 carbon atoms,
- m represents an integer of 1 to 100, and
- n is 0 or 1;
- (b) 2 to 95% by weight of an ethylenically unsaturated carboxylic acid based monomer of formula (IV) ##STR15## wherein X and Y are independently selected from hydrogen, methyl and --COOM.sup.3 or X and Y together with --COOM.sup.2 form an anhydride ring,
- Z is selected from --CH.sub.2 COOM.sup.3, hydrogen or methyl, and
- M.sup.2 and M.sup.3 are independently selected from hydrogen, monovalent metal, divalent metal, an ammonium group, an organic amine group, an alkyl group of 1-20 carbon atoms, an alkylene glycol of 2-4 carbon atoms and a polyalkylene glycol of from 2-100 moles of glycol adduct, provided that a least one of M.sup.2 and M.sup.3 is selected from hydrogen, monovalent metal, divalent metal, ammonium group and an organic amine group, and
- (c) 0 to 50% by weight of a monomer capable of being copolymerized with monomers (a) and (b), provided that the sum of (a), (b) and (c) shall be 100% by weight, said defoaming agent selected from the group consisting of (poly)oxyalkylenes, (poly)oxyalkylene alkyl ethers, oxyethylene and oxypropylene adducts of high alcohols of 12 to 14 carbon atoms, polyoxyalkylene(alkyl)aryl ethers, acetylene ethers of alkylene oxide additionally polymerized with acetylene alcohols, (poly)oxyalkylene aliphatic acid esters, (poly)oxyalkylene (alkyl)aryl ether sulfuric acid esters, (poly)oxyalkylene alkyl phosphates, (poly)oxyalkylene sorbitan aliphatic acid esters and (poly)oxyalkylene alkylamines.
A fluidity-controlling admixture for cementitious compositions comprising
- an aqueous solution of a polymer, said polymer formed by polymerizing a monomer mixture in the presence of at least one oxyalkylene-based defoaming agent, said monomer mixture comprising
- (a) 5-98% by weight of an .alpha.-olefinic monomer having 2-12 carbon atoms,
- (b) 2 to 95% by weight of an ethylenically unsaturated dicarboxylic acid anhydride based monomer, and
- (c) 0 to 50% by weight of a monomer capable of being copolymerized with monomers (a) and (b), provided that the sum of (a), (b) and (c) shall be 100% by weight,
- said oxyalkylene-based defoaming agent selected from the group consisting of (poly)oxyalkylenes, (poly)oxyalkylene alkyl ethers, oxyethylene and oxypropylene adducts of high alcohols of 12 to 14 carbon atoms, polyoxyalkylene(alkyl)aryl ethers, acetylene ethers of alkylene oxide additionally polymerized with acetylene alcohols, (poly)oxyalkylene aliphatic acid esters, (poly)oxyalkylene (alkyl)aryl ether sulfuric acid esters, (poly)oxyalkylene alkyl phosphates, (poly)oxyalkylene sorbitan aliphatic acid esters and (poly)oxyalkylene alkylamines, said defoaming agent being either dissolved in the polymer solution or stably dispersed therein in particles of no more than 20 .mu.M diameter.
A process for producing a fluidity-controlling admixture for cementitious compositions comprising polymerizing a monomer mixture in the presence of at least one oxyalkylene-based defoaming agent, said monomer mixture comprising
- (a) 5-98% by weight of an .alpha.-olefinic monomer having 2-12 carbon atoms,
- (b) 2 to 95% by weight of an ethylenically unsaturated dicarboxylic acid anhydride based monomer, and
- (c) 0 to 50% by weight of a monomer capable of being copolymerized with monomers (a) and (b), provided that the sum of (a), (b) and (c) shall be 100% by weight,
- said defoaming agent selected from the group consisting of (poly)oxyalkylenes, (poly)oxyalkylene alkyl ethers, oxyethylene and oxypropylene adducts of high alcohols of 12 to 14 carbon atoms, polyoxyalkylene(alkyl)aryl ethers, acetylene ethers of alkylene oxide additionally polymerized with acetylene alcohols, (poly)oxyalkylene aliphatic acid esters, (poly)oxyalkylene (alkyl)aryl ether sulfuric acid esters, (poly)oxyalkylene alkyl phosphates, (poly)oxyalkylene sorbitan aliphatic acid esters and (poly)oxyalkylene alkylamines.
A process for producing a fluidity-controlling admixture for cementitious compositions comprising polymerizing a monomer mixture in the presence of an oxyalkylene-based defoaming agent, said monomer mixture comprising at least one unsaturated carboxylic acid based monomer.
Dependencies are inferred from the claim text.