Process including glycolysis and subsequent purification for recycling polyester materials
AssigneeEastman Chemical Company
InventorsMichael P. Ekart, Thomas M. Pell, Jr.
Life of this patent
Estimating the term…
Abstract
A new process is described for recycling polyesters. In accordance with the described process, postconsumer or scrap polyester is reacted with glycol to produce a monomer or low molecular weight oligomer by depolymerization of the polyester. The monomer or oligomer, as the case may be, is then purified using one or more of a number of steps including filtration, crystallization, and optionally adsorbent treatment or evaporation. The monomer or oligomer thus produced is particularly suitable as a raw material for acid or ester based polyester production of packaging grade polyester material. Because the process includes purification steps, specifications for the previously used polyester material need not be strict.
Claims8
A process comprising:
- (A) contacting at a temperature in the range of 150.degree. to 300.degree. C. for a period of time in the range of 10 minutes to 4 hours previously used polyester with from 1.1 to 10 moles of dihydric alcohol per mole of dicarboxylic acid in the polyester to depolymerize the polyester and produce a reaction mixture containing monomeric, oligomeric or a mixture of monomeric and oligomeric dihydroxy species,
- (B) removing excess dihydric alcohol from the reaction mixture at a temperature below 200.degree. C.,
- (C) dissolving the reaction mixture in about 0.5 to about 20 parts by weight of a hot solvent,
- (D) treating the hot solution to remove undesirable impurities larger than 50 microns,
- (E) cooling the treated solution to precipitate the species therefrom as a solid, and
- (F) preparing a polyester from the precipitated species.
A process comprising:
- (A) contacting at a temperature in the range of 180.degree. to 240.degree. C. for a period of time in the range of 10 minutes to 4 hours previously used polyethylene terephthalate with from 2 to 6 moles of ethylene glycol per mole of terephthalic acid in the polyethylene terephthalate to depolymerize the polyethylene terephthalate and produce a reaction mixture containing monomeric, oligomeric or a mixture of monomeric and oligomeric bis-(2-hydroxyethyl) terephthalate species,
- (B) removing excess ethylene glycol from the reaction mixture by stripping at a temperature below 200.degree. C.,
- (C) dissolving the reaction mixture in about 0.5 to about 20 parts by weight of a hot solvent comprising water or one or more esters of the general formula ##STR4## wherein R and R' are each selected from straight or branched chain alkyl radicals of 1 to about 6 carbon atoms.
- (D) treating the hot solution by filtration to remove undesirable impurities larger than 1 micron,
- (E) cooling the treated solution to precipitate the species therefrom as a solid, and
- (F) preparing a polyester from the precipitated species.