US 5,635,110 A · Specialized phosphors prepared by a multi-stage grinding and firing sequence

Abstract

A multi-stage process for preparing a phosphor product includes the stages of selecting precursors of a dopant and a host lattice as the phosphor starting materials, grinding the starting materials in an initial grinding stage for an initial grinding time period to produce an initial ground material having a smaller particle size distribution than the starting materials, firing the initial ground material in an initial firing stage at an initial firing temperature for an initial firing time period to produce an initial fired material, grinding the initial fired material in an intermediate grinding stage for an intermediate grinding time period to produce an intermediate ground material having a smaller particle size than the initial fired material, wherein the intermediate grinding time period is substantially less than the initial grinding time period, firing the intermediate ground material in an intermediate firing stage at an intermediate firing temperature for an intermediate firing time to produce an intermediate fired material, wherein the intermediate firing temperature is substantially greater than the initial firing temperature, grinding the intermediate fired material in a final grinding stage for a final grinding time period to produce a final ground material having a smaller particle size than the intermediate fired material, and firing the final ground material in a final firing stage at a final firing temperature for a final firing time to produce a phosphor product, wherein the final firing time is substantially less than the intermediate firing time.

Claims34

Dependent claims

A process for preparing a phosphor product comprising:

selecting phosphor starting materials comprising a precursor of a dopant and a precursor of a host lattice;
grinding said phosphor starting materials in an initial grinding stage for an initial grinding time period to produce an initial ground material having a smaller particle size distribution than said starting material;
firing said initial ground material in an initial firing stage at an initial firing temperature for an initial firing time period to produce an initial fired material;
grinding said initial fired material in an intermediate grinding stage for an intermediate grinding time period to produce an intermediate ground material having a smaller particle size than said initial fired material, wherein said intermediate grinding time period is substantially less than said initial grinding time period;
firing said intermediate ground material in an intermediate firing stage at an intermediate firing temperature for an intermediate firing time to produce an intermediate fired material, wherein said intermediate firing temperature is substantially greater than said initial firing temperature;
grinding said intermediate fired material in a final grinding stage for a final grinding time period to produce a final ground material having a smaller particle size than said intermediate fired material;
and
firing said final ground material in a final firing stage at a final firing temperature for a final firing time to produce a phosphor product, wherein said final firing time is substantially less than said intermediate firing time.

5 more elements

A phosphor product produced by a process comprising:

selecting phosphor starting materials comprising a precursor of a dopant and a precursor of a host lattice, wherein said precursor of said dopant is selected from a group consisting of Eu.sub.2 O.sub.3, EuCl.sub.3, europium acetate, europium oxalate, Eu(NO.sub.3).sub.3, Eu(CO.sub.3).sub.3, EuF.sub.3, EuBr.sub.3, Eu(SO.sub.4).sub.3, and mixtures thereof and said precursor of said host lattice is a mixture of a first component selected from the group consisting of Ga.sub.2 O.sub.3, Al.sub.2 O.sub.3, Al.sub.2 (C.sub.2 H.sub.3 O.sub.2).sub.3, Al(OC.sub.2 H.sub.5).sub.3, In.sub.2 O.sub.3, In(C.sub.2 H.sub.3 O.sub.2).sub.3, In(C.sub.5 H.sub.7 O.sub.2).sub.3, and mixtures thereof and a second component selected from the group consisting of ZnO, Zn(C.sub.2 H.sub.3 O.sub.2).sub.2, Zn(C.sub.5 H.sub.7 O.sub.2).sub.2, ZnCO.sub.3, CdO, Cd(C.sub.2 H.sub.3 O.sub.2).sub.2, CdCO.sub.3, Cd(OOCH).sub.2, MgO, Mg(C.sub.2 H.sub.3 O.sub.2).sub.2, Mg(C.sub.5 H.sub.7 O.sub.2).sub.2, MgCO.sub.3, and mixtures thereof;
grinding said phosphor starting materials in an initial grinding stage for an initial grinding time period to produce an initial ground material;
firing said initial ground material in an initial firing stage at an initial firing temperature for an initial firing time period to produce an initial fired material;
grinding said initial fired material in an intermediate grinding stage for an intermediate grinding time period to produce an intermediate ground material;
firing said intermediate ground material in an intermediate firing stage at an intermediate firing temperature for an intermediate firing time to produce an intermediate fired material, wherein said intermediate firing temperature is substantially greater than said initial firing temperature;
grinding said intermediate fired material in a final grinding stage for a final grinding time period to produce a final ground material;
and
firing said final ground material in a final firing stage at a final firing temperature for a final firing time to produce a phosphor product, wherein said final firing time is substantially less than said intermediate firing time.

5 more elements

A phosphor product produced by a process comprising:

selecting phosphor starting materials comprising a precursor of a dopant and a precursor of a host lattice, wherein said precursor of said dopant is selected from a group consisting of Eu.sub.2 O.sub.3, EuCl.sub.3, europium acetate, europium oxalate, Eu(NO.sub.3).sub.3, Eu(CO.sub.3).sub.3, EuF.sub.3, EuBr.sub.3, Eu(SO.sub.4).sub.3, and mixtures thereof and said precursor of said host lattice is a mixture of a first component selected from the group consisting of Y.sub.2 O.sub.3, Ga.sub.2 O.sub.3, Al.sub.2 O.sub.3, La.sub.2 O.sub.3, Sc.sub.2 O.sub.3, Gd.sub.2 O.sub.3, Lu.sub.2 O.sub.3, and mixtures thereof and a second component consisting of ZnO;
grinding said phosphor starting materials in an initial grinding stage for an initial grinding time period to produce an initial ground material;
firing said initial ground material in an initial firing stage at an initial firing temperature for an initial firing time period to produce an initial fired material;
grinding said initial fired material in an intermediate grinding stage for an intermediate grinding time period to produce an intermediate ground material;
firing said intermediate ground material in an intermediate firing stage at an intermediate firing temperature for an intermediate firing time to produce an intermediate fired material, wherein said intermediate firing temperature is substantially greater than said initial firing temperature;
grinding said intermediate fired material in a final grinding stage for a final grinding time period to produce a final ground material;
and
firing said final ground material in a final firing stage at a final firing temperature for a final firing time to produce a phosphor product, wherein said final firing time is substantially less than said intermediate firing time.

5 more elements

Dependencies are inferred from the claim text.

Specialized phosphors prepared by a multi-stage grinding and firing sequence

Life of this patent

Specialized phosphors prepared by a multi-stage grinding and firing sequence

Life of this patent

Abstract

Claims34