Bioceramics used in artificial bone and artificial dental implants and the process for the preparation thereof
AssigneeSamjo Industrial Co., Ltd.
InventorsChung K. Suh, Ho K. Kim
Life of this patent
Estimating the term…
Abstract
Glass ceramic for use as a biomaterial comprising CaO 34.6 to 54.6%, SiO.sub.2 24.2 to 44.8 %, P.sub.2 O.sub.5 0 to 8.0%, CaF.sub.2 0.1 to 1.0% and Mgo 1.0 to 10.0% by weight and characterized by a primary wollastonite crystalline phase (CaO, SiO.sub.2) and a secondary apatite crystalline phase, and the process for the preparation thereof are disclosed. The glass ceramic of the present invention has superior mechanical properties, good biocompatibility, bioactivity, and no toxicity making it useful as a biomaterial in artificial bone and dental implants.
Claims1
A process for preparing a biocompatible glass ceramic, comprising the steps of:
- mixing calcium phosphate, silica sand, fluorite, calcium carbonate, and magnesium oxide to produce a mixture having the following proportions:
- CaO 34.6 to 54.6%, SiO.sub.2 24.2 to 44.8%, P.sub.2 O.sub.5 0 to 8.0%, CaF.sub.2 0.1 to 1.0% and MgO 1.0 to 10% by weight;
- melting said mixture at a temperature ranging from 1440.degree. to 1550.degree. C. to produce a melt;
- quenching said melt;
- grinding the quenched melt to produce a glass powder particles having less than 325 mesh size;
- pressing said glass powder particles by cold isostatic pressing to produce a molded product;
- and
- crystallizing the molded product in a unidirectional sintering furnace having a center temperature of 1800.degree. to 1100.degree. C. while drawing the molded product at a speed of 6 to 20 mm/hr until the upper end of said product reaches the upper portion of the furnace then gradually cooling the furnace.