Combination fire retardant, anti-soiling and biocidal agent

A process of manufacturing a combination fire retardant, soil and water resistive, and biocidal composition, comprising the steps of:

• dissolving 2.30% to 9.22% by total weight of ammonium phosphate, monobasic, 2.30% to 9.22% by total weight of ammonium phosphate, dibasic, 2.30% to 9.22% by total weight of a compound comprising 50% ammonium polyphosphate, 3% urea, and 47% water, in water comprising 57.84% to 89.475% by total weight;
• and
• adding with continuous agitation a mixture comprising 0.025% to 0.10% by total weight of coco imidazuline dicarboxylate, 2.60% to 10.4% by total weight of fluorinated acrylic polymer emulsion, and 1.00% to 4.00% by total weight of organotin.

A process of manufacturing a combination fire retardant, soil and water resistive, and biocidal composition, comprising the steps of:

• dissolving 4.61% by total weight of ammonium phosphate, monobasic, 4.61% by total weight of ammonium phosphate, dibasic, 4.61% by total weight of a compound comprising 50% ammonium polyphosphate, 3% urea, and 47% water, in water comprising 78.92% by total weight;
• and
• adding with continuous agitation a mixture comprising 0.05% by total weight of coco imidazuline dicarboxylate, 5.2% by total weight of fluorinated acrylic polymer emulsion, and 2.00% by total weight of organotin.

A process of manufacturing a fire retardant, soil and water resistive, and biocidal composition, comprising the steps of:

• providing water comprising 57.84% to 89.475% by total weight in a container having a blade mixer therein;
• commencing mixing wherein a blade tip velocity of said blade mixer is between 2500 and 3500 feet/minute, while adding 2.30% to 9.22% by total weight of ammonium phosphate, monobasic, 2.30% to 9.22% by total weight of ammonium phosphate, dibasic, and 2.30% to 9.22% by total weight of a compound comprising 50% ammonium polyphosphate, 3% urea, and 47% water, continuing said mixing until said active ingredients are dissolved;
• commencing mixing wherein said blade tip velocity is between 100 and 1000 feet per minute, while adding a mixture comprising 0.025% to 0.10% by total weight of coco imidazuline dicarboxylate, 2.60% to 10.4% by total weight of fluorinated acrylic polymer emulsion, and 1.00% to 4.00% by total weight of organotin, continuing said mixing for a desired mixing time.