Method of making a porous matrix particle
AssigneeIntegra LifeSciences Corporation
InventorFrederick Cahn
Life of this patent
Estimating the term…
Abstract
A porous particle having a generally isopycnic density with liquid growth medium, a sponge-like character and a diameter of less than 2 mm which is formed from a homogenous biologically compatible matrix is described. This particle is useful in various systems for culturing anchorage-dependent and -independent cells, and is adaptable to large scale tissue culture which permits harvesting of cell products. The method of making such a particle includes preparing a solution containing a biologically compatible material, forming droplets from the solution, freezing the droplets, drying the droplets by sublimation to form a particle, and crosslinking the biologically compatible material in the particle.
Claims11
A method of making a mass of generally spherical porous matrix particles having a generally isopycnic density with liquid growth medium, a sponge-like character and diameters of less than about 2 millimeters, each particle consisting essentially of a generally homogeneous biologically compatible matrix having a multiplicity of voids therein, the voids representing at least 10 percent of the total volume of the particle, the voids being connected to pores of less than 100 micrometers in diameter which connect the voids to the exterior of the particle, the method comprising the steps of:
- (a) dispersing a collagen in an acidic aqueous medium to form an aqueous collagen dispersion;
- (b) combining a collagen-precipitating agent with the aqueous collagen dispersion to form an aqueous suspension of a collagenous precipitate;
- (c) forming droplets from the aqueous suspension of the collagenous precipitate in a temperature-controlled droplet-formation thermal environment in thermal contact with the aqueous suspension as the droplets are formed, the temperature of the droplet-formation thermal environment being maintained at approximately 0.degree. C.;
- (d) immersing the droplets in a temperature-controlled droplet-freezer bath to freeze the droplets, the droplet-freezer bath containing a water-immiscible liquid comprising a mixture of a hydrocarbon and 1,1,2, trichlorotrifluoroethane, the liquid being maintained at a droplet-freezing temperature significantly below 0.degree. C.;
- (e) removing the frozen droplets from the droplet-freezer bath;
- (f) drying the frozen droplets by sublimation to form porous particles of a collagenous material;
- and
- (g) crosslinking the collagenous material in the particles to form porous particles of a biologically compatible crosslinked collagenous material.
Dependencies are inferred from the claim text.