Process for applying low-cement castable refractory material
AssigneesReno & Son, Inc., Oak Mountain Industries, Inc.
InventorEric L. Allison
Life of this patent
Estimating the term…
Abstract
A method for placing a thixotropic low-cement castable refractory material without the necessity for forms. A low-cement castable material is mixed with a measured amount of water, then is pumped hydraulically through a hose to a nozzle assembly. Compressed air and a cement setting agent are added to the mixture at the nozzle. The addition of the setting agent at the nozzle overcomes the thixotropic nature of the low-cement castable, so that it will immediately "set" in position when sprayed onto a surface, including vertical and overhead surfaces.
Claims12
A method for placing low-cement castable refractory material on a surface without the use of forms, comprising the steps of:
- (a) mixing dry low-cement castable refractory material with water until it forms a thoroughly and uniformly wet, thixotropic, low-cement castable mix of a hydraulically pumpable consistency;
- (b) hydraulically pumping said wet, thixotropic, low-cement castable mix through a hose to a nozzle;
- (c) metering an amount of a cement-setting agent to be added to said wet, thixotropic, low-cement castable mix to induce substantially instantaneous setting of said wet, thixotropic, low-cement castable mix upon contact on a surface;
- (d) introducing air and said metered amount of said cement-setting agent into said wet, thixotropic, low-cement castable mix at said nozzle, forming a low-cement castable end mix having diminished thixotropic properties;
- and
- (e) spraying said low-cement castable end mix having diminished thixotropic properties onto said surface without the use of forms until a desired thickness of said low-cement castable end mix is reached, wherein said low-cement castable end mix substantially instantaneously sets upon contact with said surface.
A method for applying a low-cement castable refractory material on a vertical or overhead surface without the use of a form, wherein a hose and nozzle are used to deliver said low-cement castable refractory material proximal said surface, comprising the steps of:
- (a) mixing a composition of low-cement refractory material with a quantity of water to ensure that said cement therein is thoroughly and uniformly wet such that a thixotropic, hydraulically pumpable, wet, low-cement refractory mixture is formed;
- (b) hydraulically pumping said thixotropic, low-cement refractory mixture through said hose to said nozzle;
- (c) forming a slurry of a cement setting agent and water;
- and
- (d) introducing air and said slurry into said thixotropic, low-cement refractory mixture at said nozzle, such that said slurry and thixotropic, low-cement refractory mixture are dispersed by said nozzle as a spray of a low-cement castable end mix having diminished thixotropic properties such that said low-cement castable end mix is deposited on said surface without the use of a form and without substantial gravity shearing from said surface due to substantially instantaneous setting of said low-cement castable end mix.
A method of applying a low-cement refractory material to a surface without the use of forms, comprising, in combination, the steps of:
- (a) in a mixer, mixing a low-cement refractory material, said refractory material including a low-cement system having a calcium aluminate based cement therein, with a quantity of water for a period of time sufficient to activate said low-cement system and to ensure that said cement therein is thoroughly and uniformly wet, such that a thixotropic, hydraulically pumpable, wet cementitious mixture is formed in said mixer;
- (b) hydraulically pumping said wet cementitious mixture through a conduit to a spray nozzle;
- (c) introducing a quantity of air to said spray nozzle concomitantly with said pumped wet cementitious mixture to create forces to spray said wet cementitious mixture from said nozzle onto said surface without the use of forms;
- and
- (d) introducing a free lime setting agent into said nozzle such that said free lime increases a calcium to alumina ratio in said wet cementitious mixture to effect immediate hydrate precipitation, thereby reversing said thixotropic nature of said wet cementitious mixture as it passes through said nozzle during said spray application to said surface.
Dependencies are inferred from the claim text.