Back to results
US 5,628,817 AGranted
Method for leaching nickel-copper matte employing substantially neutral leaching solutions
AssigneeOutokumpu Engineering Contractors Oy
InventorsSigmund Fugleberg, Stig-Erik Hultholm, Terry Holohan
Life of this patent
Estimating the term…
Abstract
The invention relates to a process for leaching nickel and copper from nickel-copper matte formed in pyrometallurgical nickel production by means of a multi-stage process. It is essential of the invention that the leaching of nickel takes place in at least two stages in conditions where free sulfuric acid is essentially absent, and that in these stages, the leaching of the nickel content of the matte is mainly carried out with copper as the oxidizer.
Claims17
A method for recovering metals by leaching from finely ground nickel-copper matte containing primary nickel and copper sulfides, said method comprising:
- (a) leaching the nickel-copper matte at atmospheric pressure in the presence of oxygen using a substantially neutral leaching solution containing copper sulfate, wherein said substantially neutral leaching solution is essentially lacking in free sulfuric acid, whereby step (a) produces a nickel sulfate solution and a precipitate of primary nickel and copper sulfides,
- (b) nickel electrowinning the nickel sulfate solution from step (a) and producing an anolyte that contains free sulfuric acid,
- (c) leaching the precipitate from step (a) at atmospheric pressure in the presence of oxygen using the anolyte from step (b) as leaching solution, whereby step (c) produces a solution of nickel and copper sulfates and a precipitate of secondary nickel and copper sulfides, and
- (d) pressure leaching the precipitate from step (c) using substantially neutral copper sulfate as leaching solution, whereby step (d) produces a solution of nickel sulfate and a copper-rich precipitate.
1 more element
A method for recovering metals by leaching from finely ground nickel-copper matte containing primary nickel and copper sulfides, said method comprising:
- (a) leaching the nickel-copper matte at atmospheric pressure in oxidizing conditions at a temperature in the range from about 80.degree.-100.degree. C. using a substantially neutral leaching solution containing nickel sulfate and copper sulfate, whereby step (a) produces a nickel sulfate solution and a precipitate containing primary nickel and copper sulfides,
- (b) purifying the nickel sulfate solution from step (a),
- (c) nickel electrowinning the purified nickel sulfate solution from step (b) and producing an anolyte that contains sulfuric acid and nickel sulfate,
- (d) selecting a first portion of the anolyte from step (c) and neutralizing free acid present in said first portion, and supplying the neutralized first portion to step (a) for use as at least a portion of the leaching solution,
- (e) selecting a second portion of the anolyte from step (c),
- (f) leaching the precipitate from step (a) at atmospheric pressure in oxidizing conditions at a temperature in the range from about 80.degree.-100.degree. C. using the second portion of the anolyte from step (c) as leaching solution, whereby step (f) produces a solution of nickel and copper sulfates and a precipitate of secondary nickel and copper sulfides,
- (g) supplying the solution produced in step (f) to step (a) for use as at least a portion of the leaching solution,
- (h) pressure leaching the precipitate from step (f) in non-oxidizing or mildly oxidizing conditions at a temperature of at least 110.degree. C. using substantially neutral copper sulfate as leaching solution, whereby step (h) produces a solution of nickel sulfate and a copper-rich precipitate, step (h) being continued for sufficiently long to ensure that any selenium or precious metals present in the leaching solution are precipitated,
- (i) supplying the solution produced by step (h) to step (f) as leaching solution,
- (j) pressure leaching the precipitate from step (h) in oxidizing conditions at a temperature in the range from about 80.degree.-150.degree. C. using an acidic leaching solution, whereby step (j) produces a solution that contains copper sulfate,
- (k) precipitating selenium from the solution from step (j), whereby step (k) produces a solution containing copper sulfate,
- (l) supplying a first part of the solution from step (k) to step (h) as leaching solution and precipitating rhodium from a second part of the solution from step (k), whereby step (l) produces a solution containing copper sulfate,
- (m) copper electrowinning the solution from step (l) and producing an anolyte containing sulfuric acid, and
- (n) employing the anolyte from step (m) as the leaching solution employed in step (j).