Method of producing ceramics system superconducting wire
AssigneeSumitomo Electric Industries, Ltd.
InventorsKazuhiko Hayashi, Hisao Nonoyama
Life of this patent
Estimating the term…
Abstract
In order to obtain a ceramics system superconducting wire, a bulk type ceramics system superconductor or its precursor previously treated to have orientativity in its crystal structure is reduced in diameter in a state charged in a metallic pipe, thereby being elongated, and then heat treated. In the as-formed superconducting wire, crystal orientativity of a bulk formed of the superconductor or its precursor is maintained, whereby it is possible to obtain a superconducting wire having high critical current density. In order to further improve the critical current density, it is effective that the diameter reduction working step and the heat treatment step are alternately repeated a plurality of times.
Claims9
A method of producing a ceramics system superconducting wire, said method comprising the following steps:
- preparing a bulk type ceramics system superconductor comprising a Bi--Sr--Ca--Cu--O system oxide or a Bi--Pb--Sr--Ca--Cu--O system oxide and having the longitudinal direction of said superconductor oriented perpendicularly to the c-axes of its crystals;
- charging said superconductor into a metallic pipe;
- performing diameter reduction working by deforming said metallic pipe into a tape-shaped wire and rolling said tape-shaped wire at a reduction rate of about 6.25% to 11.1%, thereby elongating said metallic pipe while causing separation of some said crystals and also causing some of said crystals to have their c-axis become non-perpendicular with the longitudinal direction of said superconductor;
- and
- heat treating said metallic pipe and said superconductor at a temperature of about 840.degree. C., thereby combining crystals separated during the step of diameter reduction working, and
- alternately repeating the diameter reduction working and the heat treating steps so that the extent to which crystal orientation is lost is limited.
A method of producing a ceramics system superconducting wire, said method comprising the following steps:
- preparing a precursor of a bulk type ceramics system superconductor comprising a Bi--Sr--Ca--Cu--O system oxide or a Bi--Pb--Sr--Ca--Cu--O system oxide and having the longitudinal direction of said superconductor oriented perpendicularly to the c-axes of its crystals;
- charging said superconductor into a metallic pipe;
- performing diameter reduction working by deforming said metallic pipe into a tape-shaped wire and rolling said tape-shaped wire at a reduction rate of about 6.25% to 11.1%, thereby elongating said metallic pipe while causing separation of some crystals and also causing some of said crystals to have their c-axis become non-perpendicular with the longitudinal direction of said superconductor;
- and
- heat treating said metallic pipe and said superconductor at a temperature of about 840.degree. C., thereby combining crystals separated during the step of diameter reduction working, and
- alternately repeating the diameter reduction working and the heat treating steps so that the extent to which crystal orientation is lost is limited.
A method of producing a ceramics system superconducting wire, said method comprising the following steps:
- preparing a bulk type ceramics system superconductor comprising a Y--Ba--Cu--O system oxide and having the longitudinal direction of said superconductor oriented perpendicularly to the c-axes of its crystals;
- charging said superconductor into a metallic pipe;
- performing diameter reduction working by deforming said metallic pipe into a tape-shaped wire and rolling said tape-shaped wire at a reduction rate of about 12.5% to 20.0%, thereby elongating said metallic pipe while causing separation of some of said crystals and also causing some of said crystals to have their c-axis become non-perpendicular with the longitudinal direction of said superconductor;
- and
- heat treating said metallic pipe and said superconductor at temperatures of 940.degree. C. and 650.degree. C. successively, thereby combining crystals separated during the step of diameter reduction working, and
- alternately repeating the diameter reduction working and the heat treating steps so that the extent to which crystal orientation is lost is limited.
A method of producing a ceramics system superconducting wire, said method comprising the following steps:
- preparing a precursor of a bulk type ceramics system superconductor comprising a Y--Ba--Cu--O system oxide and having the longitudinal direction of said superconductor oriented perpendicularly to the c-axes of its crystals;
- charging said superconductor into a metallic pipe;
- performing diameter reduction working by deforming said metallic pipe into a tape-shaped wire and rolling said tape-shaped wire at a reduction rate of about 12.5% to 20.0%, thereby elongating said metallic pipe while causing separation of some said crystals and also causing some of said crystals to have their c-axis become non-perpendicular with the longitudinal direction of said superconductor;
- and
- heat treating said metallic pipe at temperatures of 940.degree. C. and 650.degree. C. successively thereby combining crystals separated during the step of diameter reduction working, and
- alternately repeating the diameter reduction working and the heat treating steps so that the extent to which crystal orientation is lost is limited.
Dependencies are inferred from the claim text.