Ferrimagnetic core materials for megahertz frequency high flux density transformers and inductors
AssigneeAmerican Research Corporation of Virginia
InventorUsha Varshney
Life of this patent
Estimating the term…
Abstract
An improved NiZnCo ferrimagnetic core material which may further contain elements from the group Cr, Mn or Li. The invention permits enhancement of magnetic properties and results in core materials capable of efficient operation at high frequencies on the order of 1-100 MHz over a wide range of magnetic flux densities, on the order of 1-2500 Gauss. The composition of base NiZnCo ferrites are adjusted through ionic substitution. The magnetic properties of the ferrite are further enhanced through Bi.sub.2 O.sub.3 and SiO.sub.2 additions and controlled sintering. Methods of manufacturing the core material are also disclosed.
Claims14
An improved transformer or inductor ferrimagnetic core material for megahertz frequency high flux density applications, said ferrimagnetic core material consisting essentially of a compound of the formula RFe.sub.2 O.sub.4 where R is Ni.sub.1-x-y-z Zn.sub.x Co.sub.y Cr.sub.z, said core material being further characterized in that x is in the range of from about 0.01 to about 0.7, y is in the range of from about 0.001 to about 0.25 and z is in the range of from about 0.01 to about 0.4.
The ferrimagnetic core material of 1, where x is in the range of from about 0.01 to about 0.3, y is in the range of from about 0.001 to about 0.25 and z is in the range of from about 0.01 to about 0.4.
An improved transformer or inductor ferrimagnetic core material defined by the formula RFe.sub.2 O.sub.4 where R is Ni.sub.1-x-y-z Zn.sub.x Co.sub.y Cr.sub.z, said core material being further characterized in that x is in the range of from about 0.01 to about 0.7, y is in the range of from about 0.001 to about 0.25 and z is in the range of from about 0.01 to about 0.4, said core material being made by a method comprising the following steps:
- A. preparing a powdered mixture containing Ni, Zn, Co, Cr and Fe in sufficient amounts to produce said core material;
- B. preforming said powdered mixture into a usable shape;
- C. sintering the preformed mixture in an atmosphere of O.sub.2 at a temperature between about 1050.degree. C. and about 1350.degree. C. for between about 0.5 and about 24 hours;
- and
- D. cooling said sintered material at a rate of about 100.degree. C. per hour.
A method of making an improved ferrimagnetic core material defined by the formula RFe.sub.2 O.sub.4 where R is Ni.sub.1-x-y-z Zn.sub.x Co.sub.y Cr.sub.z where x is in the range of from about 0.01 to about 0.7, y is in the range of from about 0.001 to about 0.25 and z is in the range of from about 0.01 to about 0.40, comprising the following steps:
- A. preparing a powdered mixture containing Ni, Zn, Co, Cr and Fe in sufficient amounts to produce said core material;
- B. preforming said powdered mixture into a usable shape;
- C. sintering the preformed mixture in an O.sub.2 atmosphere at a temperature between about 1050.degree. to about 1350.degree. C. for between about 0.5 and about 24 hours;
- and
- D. cooling said sintered material at about 100.degree. C. per hour.
Dependencies are inferred from the claim text.