Plastics
AssigneeBiocompatibles Limited
InventorGregorio P. Valencia
Life of this patent
Estimating the term…
Abstract
Plastics materials may be plasticized using lipids as the sole plasticizer or in combination with conventional plasticizers. When appropriate lipids are used thermosetting plastics and elastomers may be rendered biocompatible or therapeutic articles and substained release medicaments may be formed.
Claims7
A process for preparing a hemocompatible and thrombo-resistant plastic material consisting only of a polymer and a lipid selected from the group consisting of egg lecithin and .alpha.-phosphatidylcholine, comprising the steps of:
- (1) admixing by melt blending said lipid with a preformed polymer to produce an admixture wherein said lipid is a simple external plasticizer, the preformed polymer being a thermoplastic material selected from the group consisting of acetals, acrylics, acrylonitrile-butadiene-styrene, cellulose esters, nylon, polycarbonate, polychlorotrifluoroethylene, polyethylene, polypropylene, polystyrene, polyterephthalate and vinyl acetals;
- and
- (2) shaping the resulting admixture and forming said plastic material, whereby the hemocompatibility and thrombo-resistance of said plastic material is greater than the hemocompatibility and thrombo-resistance of said polymer, and said plastic material contains said lipid in an amount of at least 0.1% by weight based upon the weight of said polymer.
A process for preparing a hemocompatible and thrombo-resistant plastics material comprising a polymer and a lipid, said lipid being selected from the group consisting of egg lecithin and alpha-phosphatidyl choline and being present in the plastics material in an amount of at least 0.1% by weight based on the weight of said polymer, comprising the steps of:
- (1) forming a solution or dispersion of said lipid in a solvent;
- (2) forming a solution or dispersion in a solvent of said polymer which has been preformed;
- (3) mixing said solution or dispersion formed in step (1) with said solution or dispersion formed in step (2) in relative quantities such that the amount of lipid present in the resulting mixture is at least 0.1% by weight based on the weight of said polymer;
- (4) blending said mixture formed in step (3);
- and
- (5) shaping and forming said plastics material by evaporating said solvent, whereby the hemocompatibility and thrombo-resistance of said plastics material is greater than the hemocompatibility and thrombo-resistance of said polymer.
Dependencies are inferred from the claim text.