US 5,618,893 AGranted

Process for the preparation of cationic binders for coatings, the binders produced, and their use

AssigneeVianova Kunstharz, A.G.

InventorsRudolf Schipfer, Gerhard Schm olzer

Life of this patent

Estimating the term…

Abstract

Binders for cathodic electrodeposition coatings based on epoxy resin-amine adducts are obtained by incorporation of oxazolidone structures in combination with diamine bridges built up in a specific manner. The modified epoxy resin-amine adducts are used in electro-dipping coatings together with crosslinking components. The stoved coating films have excellent corrosion protection, especially at the edges of workpieces.

Claims9

Dependent claims

Process for the preparation of cationic binders based on modified epoxy resin-amine adducts comprising reacting;

(A) 60 to 80% by weight of an epoxy resin component consisting of
(Aa) 60 to 98% by weight of at least one aromatic and/or aliphatic diepoxy resin having an epoxide equivalent weight of between 190 and 500, and
(Ab) 2 to 40% by weight of at least one epoxide compound which is modified by N-substituted mono- and/or bis-2-oxazolidone groupings, which are obtained by reaction of glycidyl groups with isocyanate groups, and having the general formula;
##STR5## wherein R.sub.1 represents the moiety of a (cyclo)aliphatic or an aromatic diisocyanate,
R.sub.2 represents the moiety of an aliphatic monoglycidyl ether or an aliphatic monoglycidyl ester or a radical R.sub.3,
R.sub.3 represents the moiety of an (aromatic)-aliphatic or aromatic diglycidyl ether, and
R.sub.4 represents the moiety of a (cyclo)aliphatic or an aromatic monoisocyanate,
with
(B) 20 to 40% by weight of an amine component consisting of
(Ba) 0 to 20% by amine equivalence of at least one primary alkylamine and/or alkanolamine,
(Bb) 25 to 55% by amine equivalence of at least one secondary alkylamine and/or alkanolamine,
(Bc) 20 to 50% by amine equivalence of at least one primary-tertiary alkyldiamine, and
(Bd) 5 to 25% by amine equivalence of a disecondary amine compound of 2 mol of a compound resulting from the reaction product of diprimary di- or polyamines with aliphatic monoglycidyl and/or monoepoxide compounds with one mol of a diepoxide compound,
wherein the totals of the percentage figures of components A and B equals 100 to give an adduct which is free from epoxide groups and has a molecular weight of from about 2000-18,000 (weight-average), a glass transition temperature of between +20.degree. C. and +45.degree. C., and a basicity corresponding to an amine number of at least 20 mg KOH/g, with the proviso that the epoxy resin components (Aa) and (Ab) of component A are reacted with the amine components (Ba), (Bb), (Bc) and (Bd) of component B at 60.degree. C. to 80.degree. C. in a 55-75% strength partial solution in glycol ethers, and that after the end of all the additions, the reaction temperature is increased to a maximum of 120.degree. C. to bring the reaction to completion.

11 more elements

Dependencies are inferred from the claim text.

patentgrep

Loading patent…

Abstract

Process for the preparation of cationic binders based on modified epoxy resin-amine adducts comprising reacting;

(A) 60 to 80% by weight of an epoxy resin component consisting of
(Aa) 60 to 98% by weight of at least one aromatic and/or aliphatic diepoxy resin having an epoxide equivalent weight of between 190 and 500, and
(Ab) 2 to 40% by weight of at least one epoxide compound which is modified by N-substituted mono- and/or bis-2-oxazolidone groupings, which are obtained by reaction of glycidyl groups with isocyanate groups, and having the general formula;
##STR5## wherein R.sub.1 represents the moiety of a (cyclo)aliphatic or an aromatic diisocyanate,
R.sub.2 represents the moiety of an aliphatic monoglycidyl ether or an aliphatic monoglycidyl ester or a radical R.sub.3,
R.sub.3 represents the moiety of an (aromatic)-aliphatic or aromatic diglycidyl ether, and
R.sub.4 represents the moiety of a (cyclo)aliphatic or an aromatic monoisocyanate,
with
(B) 20 to 40% by weight of an amine component consisting of
(Ba) 0 to 20% by amine equivalence of at least one primary alkylamine and/or alkanolamine,
(Bb) 25 to 55% by amine equivalence of at least one secondary alkylamine and/or alkanolamine,
(Bc) 20 to 50% by amine equivalence of at least one primary-tertiary alkyldiamine, and
(Bd) 5 to 25% by amine equivalence of a disecondary amine compound of 2 mol of a compound resulting from the reaction product of diprimary di- or polyamines with aliphatic monoglycidyl and/or monoepoxide compounds with one mol of a diepoxide compound,
wherein the totals of the percentage figures of components A and B equals 100 to give an adduct which is free from epoxide groups and has a molecular weight of from about 2000-18,000 (weight-average), a glass transition temperature of between +20.degree. C. and +45.degree. C., and a basicity corresponding to an amine number of at least 20 mg KOH/g, with the proviso that the epoxy resin components (Aa) and (Ab) of component A are reacted with the amine components (Ba), (Bb), (Bc) and (Bd) of component B at 60.degree. C. to 80.degree. C. in a 55-75% strength partial solution in glycol ethers, and that after the end of all the additions, the reaction temperature is increased to a maximum of 120.degree. C. to bring the reaction to completion.

11 more elements