Method of manufacturing CMOS device
AssigneeKabushiki Kaisha Toshiba
InventorYasuyuki Saito
Life of this patent
Estimating the term…
Abstract
An improved method of manufacturing a semiconductor device, especially suitable for a p-channel MOS transistor is disclosed. The method includes the steps of forming a gate oxide film over the surface of a semiconductor substrate in a region where a p-channel MOS transistor is to be formed, forming a polysilicon film over the gate oxide film, in order to construct a gate electrode, forming a film of an amorphous material over the polysilicon film and implanting ions of a p-type impurity, especially elemental boron atoms, into the polysilicon film, through the film of amorphous material.
Claims3
A method of manufacturing a CMOS semiconductor device, comprising the steps of:
- forming an n-type well in a part of a p-type semiconductor substrate;
- forming a gate oxide film on the surface of the semiconductor substrate and on the n-type well, said gate oxide film having holes, exposing the semiconductor substrate, corresponding to a region where a drain of an n-channel transistor in the p-type semiconductor substrate is to be formed and to a region where a drain of a p-channel transistor in the n-type well is to be formed;
- forming punch-through current suppression layers and counter-dose regions under regions where gates of the p-channel and n-channel transistors are to be formed;
- depositing a polysilicon film on said gate oxide film and on the semiconductor surface exposed through said holes;
- depositing an amorphous film on said polysilicon film;
- selectively forming a first resist film having a hole corresponding to said n-type well;
- implanting boron ions through the amorphous film into said polysilicon film over the n-type well;
- removing said first resist film;
- selectively forming a second resist film having a hole corresponding to a region where said n-channel transistor is to be formed;
- implanting n-type impurity ions into said polysilicon film within the region where said n-channel transistor is to be formed;
- and
- heat processing to diffuse boron and n-type impurity regions into said n-type well and p-type substrate, respectively, to form impurity diffusion regions at the portions where drains are to be formed.