US 5,607,546 AGranted

CTMP-process

AssigneeMolnlycke AB

InventorsHans H oglund, Roland B ack, Ove Danielsson, Bo Falk

Life of this patent

Estimating the term…

Loading patent…

Abstract

An absorbent, chemithermomechanical pulp produced from lignocellulosic material with a wood yield above 88%, a low resin content <0.15%, a long fiber content above 70%, a short fiber content below 10% and a shive content below 3%. The method for producing the pulp comprises the steps of impregnating, preheating, defibering, and washing the material. The impregnation and preheating of the chips are effected in one and the same vessel over a combined time period of at most 2 minutes, particularly at most 1 minute, preferably at most 0.5 minutes; using a warm impregnating liquid having a temperature of at least 100.degree. C., suitably at least 130.degree. C. and preferably having essentially the same temperature as in the preheating process; and preheating the chips at a temperature of 150.degree.-175.degree. C., preferably 160.degree.-170.degree. C. Defibering is carried out with an energy input which is at most half of the energy input required for defibering when the preheating and defibering are carried out at 135.degree. C.

Claims15

Dependent claims

In a method for producing an absorbent chemithermomechanical pulp from lignocellulosic material consisting of wood chips at a wood yield above 88%, comprising

a) steaming the wood chips;
b) impregnating the chips with a solution selected from the group consisting of sodium sulphite, sodium dithionate and alkaline peroxide, with an addition of a complex builder;
c) preheating the chips;
d) defibering the chips to pulp at substantially the same pressure and temperature as those employed in the preheating process;
and
e) washing and dewatering the pulp;
the improvement comprising
f) carrying out steps b) and c) in one and the same vessel over a combined time period of at most 2 minutes by impregnating the chips with said impregnating solution;
g) using a warm impregnating solution having a temperature of at least 130.degree. C.;
and
h) preheating the chips at a temperature of 150.degree.-175.degree. C., wherein the pulp obtained has such a brightness that it can be bleached with peroxide to a brightness of at least 65% ISO, wherein when fractioning according to Bauer McNett, the long-fibre content is above 75% of fibres retained on a wire gauze of size 28 mesh and the short fibre content is below 8% of fibres which pass through a wire gauze of size 200 mesh;
and wherein the shive content is lower than 3% measured according to Somerville.

9 more elements